Preparation method of polyester FDY mother filament and monofilament thereof

A technology of mother silk and polyester, applied in the field of preparation of polyester FDY mother silk and its monofilament, can solve the problems that the production process cannot meet the market demand, the uneven dyeing performance of monofilament, etc. Effect

Active Publication Date: 2016-11-09
福建百宏聚纤科技实业有限公司
View PDF5 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The traditional monofilament production is completed by UDY-DT process, the spinning speed is 700-900m / min, and the monofilament dyeing performance is uneven
The production process cannot meet the market demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of polyester FDY mother filament and monofilament thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034]A preparation method of polyester FDY mother silk, the antibacterial polyester melt containing cuprous material is added into the conventional polyester melt pipeline by means of melt direct spinning pipeline, and passed through the static mixer in the melt pipeline Mixing, and then through melt spinning, cooling, drafting, heat setting and winding processes to obtain polyester FDY fiber-divided mother silk. The specific process is: spinning temperature 292°C, wind temperature 16-18°C, wind speed 0.7-0.85m / s, drawing temperature 95°C, drafting ratio 1.8-2.2 times, heat setting temperature 150°C, winding tension control It is 2.2~2.5cN, and the winding speed is 3900~4500 m / min.

[0035] The mass ratio of antibacterial polyester melt containing cuprous material to conventional polyester melt is 1:8;

[0036] The number of holes in the mother silk spinneret is 6 to 144 holes, and the denier of the mother silk is 0.3 to 20D;

[0037] The production process of monofilaments...

Embodiment 2

[0057] A preparation method of polyester FDY mother silk, the antibacterial polyester melt containing cuprous material is added into the conventional polyester melt pipeline by means of melt direct spinning pipeline, and passed through the static mixer in the melt pipeline Mixing, and then through melt spinning, cooling, drafting, heat setting and winding processes to obtain polyester FDY fiber-divided mother silk. The specific process is: spinning temperature 292°C, wind temperature 16-18°C, wind speed 0.7-0.85m / s, drawing temperature 95°C, drafting ratio 1.8-2.2 times, heat setting temperature 150°C, winding tension control It is 2.2~2.5cN, and the winding speed is 3900~4500 m / min.

[0058] The mass ratio of antibacterial polyester melt containing cuprous material to conventional polyester melt is 1:12;

[0059] The number of holes in the mother silk spinneret is 6 to 144 holes, and the denier of the mother silk is 0.3 to 20D;

[0060] The production process of monofilamen...

Embodiment 3

[0079] A preparation method of polyester FDY mother silk, the antibacterial polyester melt containing cuprous material is added into the conventional polyester melt pipeline by means of melt direct spinning pipeline, and passed through the static mixer in the melt pipeline Mixing, and then through melt spinning, cooling, drafting, heat setting and winding processes to obtain polyester FDY fiber-divided mother silk. The specific process is: spinning temperature 292°C, wind temperature 16-18°C, wind speed 0.7-0.85m / s, drawing temperature 95°C, drafting ratio 1.8-2.2 times, heat setting temperature 150°C, winding tension control It is 2.2~2.5cN, and the winding speed is 3900~4500 m / min.

[0080] The mass ratio of the antibacterial polyester melt containing cuprous material to the conventional polyester melt is 1:15;

[0081] The number of holes in the mother silk spinneret is 6 to 144 holes, and the denier of the mother silk is 0.3 to 20D;

[0082] The production process of mon...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of a polyester FDY mother filament and a monofilament thereof. The method consists of: adding an antibacterial polyester melt containing a cuprous material into a conventional polyester melt pipe by a melt direct-spinning pipe adding way, performing mixing by a static mixer in the melt pipe, then carrying out melt spinning, cooling, drafting, heat setting and winding to obtain a polyester FDY mother yarn. According to the process, specifically, the spinning temperature is 292DEG C, the wind temperature is 16-18DEG C, the wind speed is 0.7-0.85m / s, the drafting temperature is 95DEG C, the drafting ratio is 1.8-2.2 times, the heat setting temperature is 150DEG C, the winding tension is controlled at 2.2-2.5cN, and the winding speed is 3900-4500 meter / minute. While acquiring direct economic benefits, the method provided by the invention also achieves considerable indirect economic benefits, and seizes the DTY emerging market under the current situation of fierce market competition. According to the invention, the antibacterial material is added to enhance the antibacterial properties of the fiber and expand its application scope.

Description

technical field [0001] The invention relates to the technical field of textile production, in particular to a method for preparing polyester FDY mother silk and monofilament thereof. Background technique [0002] The key to the development of the textile industry lies in the development of new products. Products with multi-purpose, high performance and high added value using new technology, new equipment and new technology will become a new development trend. More and more companies have begun to join the ranks of developing new high-tech and differentiated functional chemical fiber products. [0003] Polyester filaments with a monofilament fineness of 10-30D are widely used in civil uses such as wedding dresses, evening dresses, warp-knitted fabrics, and industrial printing screens and ribbons. The traditional monofilament production is completed by UDY-DT process, the spinning speed is 700-900m / min, and the monofilament dyeing performance is uneven. This production proc...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/92D01F1/10C08G63/183C08K9/10C08K3/22D01D5/08D01D11/02
CPCC08G63/183C08K3/22C08K9/10C08K2003/2248C08K2201/011D01D5/08D01D11/02D01F1/103D01F6/92
Inventor 鲁传旺李艺龙陈文阳
Owner 福建百宏聚纤科技实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com