Bamboo fiber hemostatic gauze and preparation method thereof

The technology of hemostatic gauze and bamboo fiber is applied in the field of bamboo fiber gauze and its preparation, which can solve the problems of staying, there is no effective composite hemostatic gauze, etc., and achieve the effects of stable properties, good hemostatic effect, and not easy to fall off.

Inactive Publication Date: 2016-11-16
WUHAN GENERAL HOSPITAL OF GUANGZHOU MILITARY
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the hemostatic gauze used for first aid in China is still at the level of non-woven gauze, and there is no effective composite hemostatic gauze for emergency use so far.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bamboo fiber hemostatic gauze and preparation method thereof
  • Bamboo fiber hemostatic gauze and preparation method thereof
  • Bamboo fiber hemostatic gauze and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] The present embodiment provides a kind of bamboo fiber hemostatic gauze, prepared according to the following method:

[0042] The whole system is 100g, and each component is weighed according to the following formula, the specific formula: 0.1g kaolin, 2g 1% hypromellose 2910-SHE50 (Hydroxypropyl methylcellulose, HPMC), 20g polyethylene glycol 600, 77.9g water Carry out mechanical stirring to make it fully mix to make 100ml each of 4 different kaolin concentration suspensions. Bamboo fiber gauze is cut into 7cm * 70cm (corresponding to 50ml above-mentioned suspension), as base material. Using the method of spray-freeze drying, spray about 50ml of the above suspension on the substrate with a nozzle with an inner diameter of 0.4mm and 80 holes. The ambient temperature is constant at 25°C and the spraying time is 30min. Dipping, the soaking time is 60min. Take out the gauze and put it into a freeze dryer, and freeze it for 24 hours under the condition of 223K to obtain t...

Embodiment 2

[0044] The present embodiment provides a kind of bamboo fiber hemostatic gauze, prepared according to the following method:

[0045]The whole system is 100g, and each component is weighed according to the following formula, the specific formula: 0.4g kaolin, 2g 1% hypromellose 2910-SHE50 (Hydroxypropyl methylcellulose, HPMC), 20g polyethylene glycol 600, 77.6g water ; Perform mechanical stirring to make it fully mixed to make a suspension of 100ml. Bamboo fiber gauze is cut into 7cm * 70cm (corresponding to 50ml above-mentioned suspension), as base material. Using the method of spray-freeze drying, spray about 50ml of the above suspension on the substrate with a nozzle with an inner diameter of 0.4mm and 80 holes. The ambient temperature is constant at 25°C and the spraying time is 30min. Dipping, the soaking time is 60min. Take out the gauze and put it into a freeze dryer, and freeze it for 24 hours under the condition of 223K to obtain the bamboo fiber hemostatic gauze. F...

Embodiment 3

[0047] The present embodiment provides a kind of bamboo fiber hemostatic gauze, prepared according to the following method:

[0048] The whole system is 100g, and each component is weighed according to the following formula, the specific formula: 0.75g kaolin, 2g 1% hypromellose 2910-SHE50 (Hydroxypropyl methylcellulose, HPMC), 20g polyethylene glycol 600, 77.25g water ; Perform mechanical stirring to make it fully mixed to make a suspension of 100ml. Bamboo fiber gauze is cut into 7cm * 70cm (corresponding to 50ml above-mentioned suspension), as base material. Using the method of spray-freeze drying, spray about 50ml of the above suspension on the substrate with a nozzle with an inner diameter of 0.4mm and 80 holes. The ambient temperature is constant at 25°C and the spraying time is 30min. Dipping, the soaking time is 60min. Take out the gauze and put it into a freeze dryer, and freeze it for 24 hours under the condition of 223K to obtain the bamboo fiber hemostatic gauze....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the technical fields of a medical dressing and a production process thereof, in particular to bamboo fiber hemostatic gauze and a preparation method thereof. The hemostatic gauze consists of a base material made from a raw or regenerated bamboo fiber material , a kaolin or kaolinite hemostatic clay material which is bonded to the base material and a binding agent for binding the hemostatic clay material to the base material. According to the hemostatic gauze disclosed by the invention, the base material in the bamboo fiber hemostatic gauze consists of bamboo fibers, the hemostatic clay material consists of kaolin or kaolinite and the hemostatic clay material is bonded to the bamboo fibers of the base material by virtue of the bonding agent, so that a stable nature is guaranteed, the hemostatic clay material is prevented from falling off easily, and the hemostatic gauze is good in hemostatic effect.

Description

technical field [0001] The invention relates to the technical field of medical dressings and production techniques thereof, in particular to a bamboo fiber gauze and a preparation method thereof. Background technique [0002] Blood loss is the primary factor of traumatic death, and at least 30% of the wounded who died due to excessive blood loss can be saved if timely and effective hemostasis can be achieved. Blood loss is also the main cause of traumatic death such as war wounds and falling injuries. Successful hemostasis within an effective time is of great significance to saving lives. All countries in the world attach great importance to the research on post-traumatic hemostasis measures. But at present the hemostatic gauze that domestic emergency is used still stays at the level of non-woven gauze, there is still no effective, composite hemostatic gauze that can be used for first aid so far. In order to solve this problem, it is necessary to base itself on domestic res...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61L15/28A61L15/18A61L15/42A61L15/46A61L15/58
CPCA61L15/28A61L15/18A61L15/42A61L15/46A61L15/58A61L2300/102A61L2300/232A61L2300/404A61L2300/412A61L2400/04C08L1/02
Inventor 樊光辉张宜刁波喻晶黎檀石
Owner WUHAN GENERAL HOSPITAL OF GUANGZHOU MILITARY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap