A kind of light bulb explosion-proof glue and preparation method thereof

An explosion-proof and glue technology for light bulbs, which can be used in adhesives, non-polymer adhesive additives, adhesive additives, etc., and can solve the problems of luminous flux attenuation, high price, and poor buffer protection effect.

Active Publication Date: 2018-10-09
宿迁市同创化工科技股份有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The cured adhesive layer of the epoxy resin coating layer is hard and brittle, and it is not resistant to yellowing, and the buffer protection effect is not good; the high price of solvent-based fluoroplastics limits its industrialization; polyurethane is prone to yellowing and luminous flux attenuation; and silicon Rubber and silicone resins are relatively viscous, making it difficult to form thinner coatings when applied

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] An anti-explosion adhesive for light bulbs, comprising the following components by mass fraction:

[0031] Hydrogenated Styrene-Butadiene Block Copolymer 25%

[0032] Butyl acetate 5%

[0033] Ethylcyclohexane 50%

[0034] Hydrocarbon solvent 19.7%

[0035] Compound stabilizer 0.1%

[0036] N-(β-aminoethyl)-γ-aminopropyltrimethoxysilane 0.2%.

[0037] Compound stabilizers are tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester, 1,3,5-tris(3,5-di-tert-butyl-4- Hydroxybenzyl)isocyanuric acid, tris(2,4-di-tert-butylphenyl)phosphite and bis(2,2,6,6-tetramethyl-4-piperidinyl)sebacate It is compounded according to the mass ratio of 1:4:2:3.

[0038] The preparation method of the bulb explosion-proof glue comprises the following steps:

[0039] Weigh butyl acetate and ethylcyclohexane according to the formula and put them into the reaction kettle, stir and mix evenly, then add hydrogenated styrene-butadiene block copolymer into the reaction ...

Embodiment 2

[0047] An anti-explosion adhesive for light bulbs, comprising the following components by mass fraction:

[0048] Hydrogenated Styrene-Butadiene Block Copolymer 15%

[0049] Butyl acetate 10%

[0050] Ethylcyclohexane 54%

[0051] Hydrocarbon solvent 20%

[0052] Compound stabilizer 0.5%

[0053] N-(β-aminoethyl)-γ-aminopropyltrimethoxysilane 0.5%.

[0054] Compound stabilizers are tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester, 1,3,5-tris(3,5-di-tert-butyl-4- Hydroxybenzyl)isocyanuric acid, tris(2,4-di-tert-butylphenyl)phosphite and bis(2,2,6,6-tetramethyl-4-piperidinyl)sebacate It is compounded according to the mass ratio of 1:4:2:3.

[0055] The preparation method of the bulb explosion-proof glue comprises the following steps:

[0056] Weigh butyl acetate and ethylcyclohexane according to the recipe and put them into the reactor, stir and mix evenly, then add hydrogenated styrene-butadiene block copolymer into the reactor, heat the m...

Embodiment 3

[0064] An anti-explosion adhesive for light bulbs, comprising the following components by mass fraction:

[0065] Hydrogenated Styrene-Butadiene Block Copolymer 20%

[0066] Butyl acetate 8%

[0067] Ethylcyclohexane 55.5%

[0068] Hydrocarbon solvent 15%

[0069] Compound stabilizer 0.5%

[0070] N-(β-aminoethyl)-γ-aminopropyltrimethoxysilane 1.0%.

[0071] Compound stabilizers are tetrakis[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionate] pentaerythritol ester, 1,3,5-tris(3,5-di-tert-butyl-4- Hydroxybenzyl)isocyanuric acid, tris(2,4-di-tert-butylphenyl)phosphite and bis(2,2,6,6-tetramethyl-4-piperidinyl)sebacate It is compounded according to the mass ratio of 1:4:2:3.

[0072] The preparation method of the bulb explosion-proof glue comprises the following steps:

[0073] Weigh butyl acetate and ethylcyclohexane according to the formula and put them into the reactor, stir and mix evenly, then add hydrogenated styrene-butadiene block copolymer into the reactor, heat the m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of glue production technology and in particular relates to anti-explosion glue for a bulb. The anti-explosion glue comprises the following components by mass fraction: 15-25% of thermoplastic elastomer, 5-10% of butyl acetate, 50-75% of ethylcyclohexane, 10-20% of carbon hydrocarbon solvent, 0.1-0.5% of compound stabilizer and 0.2-1.0% of yellowing resistant tackifier. The anti-explosion glue has the technical effects that the anti-explosion glue has good cushion protection performance, is resistant to yellowing, is easy to coat, is lower in cost and adapts to the requirements of industrialization; when the thickness is more than 3.5mu m, the coated bulb can pass the drop test of a UL1993 standard method.

Description

technical field [0001] The invention relates to the technical field of glue production, in particular to a light bulb explosion-proof glue and a preparation method thereof. Background technique [0002] In the prior art, the outer cover of lamps and lanterns is generally made of glass. Compared with resin lamp shades, the lamp shade made of glass has better heat dissipation effect and lower cost, but the lamp shade made of glass is easy to be damaged. Glass shards will fly, threatening personal safety. [0003] For this reason, many manufacturers have produced explosion-proof lamps, most of which are coated with explosion-proof layers on the surface of the bulbs. These explosion-proof layers include epoxy resins, fluoroplastics, silicones, polyurethanes, and silicone resins. [0004] The cured adhesive layer of the epoxy resin coating layer is hard and brittle, and it is not resistant to yellowing, and the buffer protection effect is not good; the high price of solvent-base...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J153/02C09J11/06
CPCC08K5/544C09J11/06C09J153/025
Inventor 陆俊南陆甫兴易先春陈振龙潘志罗栩华蒋振华
Owner 宿迁市同创化工科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com