Antibacterial deodorizing ceramic tile and preparation method thereof

A ceramic tile and deodorant technology, applied in the field of quartz stone, can solve the problems of single, not having multiple functions, limiting the scope of application, etc.

Inactive Publication Date: 2016-12-21
FOSHAN GAOMING DISTRICT MINGCHENG TOWN NEW ENERGYNEW MATERIAL IND TECH INNOVATION CENT
View PDF12 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, there are few reports about ceramic tiles with good uniformity and stable antibacterial function.
Moreover, the existing ceramic tiles are generally single-function products, such as antibacterial, anti-static, etc., that is, one product does not have multiple functions, which greatly limits its application range and needs to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial deodorizing ceramic tile and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] An antibacterial and deodorizing ceramic tile and a preparation method thereof, the preparation method comprising the following steps:

[0036] Step A, prepare the bottom glaze: according to the mass percentage, mix 30% frit, 9% functional agent, 24% lithium china stone, 5% zirconium silicate, 20% kaolin and 12% quartz, wet ball mill, pass 300~350 mesh sieve to get slurry bottom glaze;

[0037] Step B, preparing the surface glaze: by mass percentage, 72% frit, 1% deodorant, 20% kaolin, 5% alumina, 1% zinc oxide and 1% zirconium silicate are evenly mixed, wet ball milled, Pass through a 300-350 mesh sieve to obtain a paste-like top glaze;

[0038] In step C, the bottom glaze and top glaze prepared in steps A and B are glazed successively on the clay of the ceramic tile by means of glazing; then fired in a kiln at a firing temperature of 800-900°C and a firing cycle of 45 minutes to obtain ceramics brick;

[0039] Wherein, the frit is prepared by the following method: ...

Embodiment 2

[0051] An antibacterial and deodorizing ceramic tile and a preparation method thereof, the preparation method comprising the following steps:

[0052] Step A, preparing the bottom glaze: by mass percentage, 32% frit, 6% functional agent, 24% lithium china stone, 5% zirconium silicate, 22% kaolin and 11% quartz are mixed evenly, wet ball milled, passed 300~350 mesh sieve to get slurry bottom glaze;

[0053] Step B, prepare the surface glaze: mix 70% frit, 4% deodorant, 14% kaolin, 7% alumina, 1% zinc oxide and 3% zirconium silicate evenly by mass percentage, wet ball milling, Pass through a 300-350 mesh sieve to obtain a paste-like top glaze;

[0054] In step C, the bottom glaze and top glaze prepared in steps A and B are glazed successively on the clay of the ceramic tile by means of glazing; then fired in a kiln at a firing temperature of 800-900°C and a firing cycle of 45 minutes to obtain ceramics brick;

[0055] Wherein, the frit is prepared by the following method: by ...

Embodiment 3

[0067] An antibacterial and deodorizing ceramic tile and a preparation method thereof, the preparation method comprising the following steps:

[0068] Step A, preparing the bottom glaze: by mass percentage, 37% frit, 3% functional agent, 15% lithium china stone, 10% zirconium silicate, 25% kaolin and 10% quartz are mixed evenly, wet ball milled, passed 300~350 mesh sieve to get slurry bottom glaze;

[0069] Step B, prepare the surface glaze: mix 62% frit, 6% deodorant, 20% kaolin, 8% alumina, 1% zinc oxide and 3% zirconium silicate evenly by mass percentage, wet ball milling, Pass through a 300-350 mesh sieve to obtain a paste-like top glaze;

[0070] In step C, the bottom glaze and top glaze prepared in steps A and B are glazed successively on the clay of the ceramic tile by means of glazing; then fired in a kiln at a firing temperature of 800-900°C and a firing cycle of 45 minutes to obtain ceramics brick;

[0071] Wherein, the frit is prepared by the following method: by...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an antibacterial deodorizing ceramic tile and a preparation method thereof. The preparation method comprises the following steps: step A, preparing a ground coat: evenly mixing a frit, a functional agent, a lithium chinastone, zirconium silicate, kaolin and quartz according to mass percent, ball-milling through a wet method, and screening to obtain the pulpous ground coat; step B, preparing a surface glaze: evenly mixing a frit, a deodorant, the kaolin, aluminum oxide, zinc oxide and zirconium silicate, ball-milling through a wet method, and screening to obtain the pulpous surface glaze; step C, sequentially applying the ground coat and the surface glaze prepared in the step A and the step B on a tile clay, and firing to obtain the ceramic tile. Compared with an existing ceramic pile, the ceramic pile prepared through the preparation method is scientific in material collocation, reasonable in preparation and stable in performances; with reasonably allocated photochromic compound, deodorant and antibacterial powder, the ceramic tile has excellent antibacterial performance, air purification performance and photochromic performance, so that the application scope of the ceramic tile is further expanded.

Description

technical field [0001] The invention relates to the technical field of quartz stone, in particular to an antibacterial and deodorizing ceramic brick and a preparation method thereof. Background technique [0002] Bacteria and mold, as pathogenic bacteria, are very harmful to humans, animals and plants, affecting people's health and even life-threatening, and bringing significant economic losses. Therefore, the research on antibacterial materials and their products has attracted people's attention day by day, and the demand for antibacterial products will constitute a huge market. [0003] Ceramic bricks are plate or block ceramic products produced from clay and other inorganic non-metallic raw materials through molding and sintering processes, and are used to decorate and protect the walls and floors of buildings and structures. [0004] However, there are few reports about ceramic tiles with good uniformity and stable antibacterial function. Moreover, the existing ceramic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/20C03C8/06C04B41/89B01D53/76
CPCC03C8/20B01D53/76C03C8/06C04B41/52C04B41/89C04B41/504C04B41/5022
Inventor 麦浩
Owner FOSHAN GAOMING DISTRICT MINGCHENG TOWN NEW ENERGYNEW MATERIAL IND TECH INNOVATION CENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com