A nanometer antibacterial tile and a preparing method thereof

A ceramic tile and nano technology, applied in the field of nano antibacterial tiles and its preparation, can solve problems such as clusters and poor antibacterial effect, and achieve the effect of reducing cluster phenomenon and excellent bactericidal effect

Inactive Publication Date: 2016-12-21
佛山市寰田陶瓷有限公司
View PDF4 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional antibacterial ceramics use nano-silver as an antibacterial agent. However, since it is easily clustered after being added to ceramic raw materials, the antibacterial effect is not good. Therefore, it is necessary to propose an antibacterial ceramic with good antibacterial effect and its preparation method.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] The embodiment of the present invention also provides a preparation method of nano antibacterial tiles, including:

[0026] (1) Preparation of ceramic raw material powder: wash the ceramic raw material, pre-sinter, dry, pulverize, and pass through a 100-200 mesh sieve to obtain the ceramic raw material powder;

[0027] (2) Preparation of antibacterial agent: take silane coupling agent and add to nano silica sol, wherein, nano silica is 40-50% of the total weight of nano silica sol, stir for 30-50min, then add nano silver and neodymium oxide, stirred for 30-50 minutes, then added nano-titanium dioxide and cerium oxide, and stirred for another 30-50 minutes to obtain an antibacterial agent;

[0028] (3) Preparation of antibacterial ceramics: Add the antibacterial agent prepared in step (2) to the ceramic raw material powder prepared in step (1), wherein the antibacterial agent is 1-5% of the total weight of the ceramic raw material, ball mill after heating in a water bath...

Embodiment 1

[0034] An embodiment of the present invention provides a nano antibacterial ceramic tile, comprising ceramic raw materials and an antibacterial agent, wherein the antibacterial agent is 1% of the total weight of the ceramic raw material, and the antibacterial agent is made of the following raw material formula in parts by weight: nanometer two Silica sol 20, nano silver 2, nano titanium dioxide 1, silane coupling agent 17, neodymium oxide 2, cerium oxide 1;

[0035] The ceramic raw material is made of the following raw material proportions by weight: 30 parts by weight of albite, 35 parts of potassium feldspar, 20 parts of quartz, 16 parts of kaolin, 2 parts of burnt talc and 5 parts of feldspar.

Embodiment 2

[0037] An embodiment of the present invention provides a nano antibacterial ceramic tile, comprising ceramic raw materials and an antibacterial agent, wherein the antibacterial agent is 5% of the total weight of the ceramic raw material, and the antibacterial agent is made of the following raw material formula by weight: nanometer two Silica sol 30, nano silver 3, nano titanium dioxide 2, silane coupling agent 22, neodymium oxide 3, cerium oxide 2;

[0038] The ceramic raw material is made of the following raw material proportions by weight: 35 parts by weight of albite feldspar, 45 parts potassium feldspar, 28 parts quartz, 24 parts kaolin, 4 calcined talc, and 10 parts feldspar.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A nanometer antibacterial tile is disclosed and comprises ceramic raw materials and an antibacterial agent. The weight of the antibacterial agent is 1-5% of the total weight of the ceramic raw materials. The antibacterial agent is prepared from, by weight, 20-30 parts of nanometer silica sol, 2-3 parts of nano-silver, 1-2 parts of nanometer titanium oxide, 17-22 parts of a silane coupling agent, 2-3 parts of neodymium oxide and 1-2 parts of cerium oxide. The antibacterial agent comprising the nanometer silica sol, the nano-silver, the nanometer titanium oxide, the silane coupling agent, the neodymium oxide and the cerium oxide is added, wherein a cluster phenomenon between the nano-silver and the nanometer titanium oxide is effectively reduced through adopting the hydrosol of the nanometer silica as a carrier and adopting the silane coupling agent as a medium, the neodymium oxide and the cerium oxide which are rare earth oxides are introduced to activate antibacterial functions of the nano-silver and the nanometer titanium oxide, and the antibacterial functions of the nano-silver and the nanometer titanium oxide are effectively combined to achieve an excellent sterilization effect.

Description

technical field [0001] The invention relates to the technical field of tile preparation, in particular to a nano antibacterial tile and a preparation method thereof. Background technique [0002] Antibacterial ceramics is a new type of functional material that protects the environment. It is the product of the combination of antibacterial technology and ceramic technology. It maintains the original function and decorative effect of ceramic products while increasing the functions of disinfection, sterilization and chemical explanation. Therefore, it is widely used Used in all walks of life. [0003] Traditional antibacterial ceramics use nano-silver as an antibacterial agent. However, since it is easily clustered after being added to ceramic raw materials, the antibacterial effect is not good. Therefore, it is necessary to propose an antibacterial ceramic with good antibacterial effect and its preparation method. . [0004] The invention provides a nano antibacterial tile a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/16C04B33/13C04B33/28C04B41/86
CPCC04B33/16C04B33/1305C04B33/131C04B33/28C04B41/009C04B41/5022C04B41/86C04B2235/3224C04B2235/3229C04B2235/3232C04B2235/3418C04B2235/3445C04B2235/3463C04B2235/3472C04B2235/408C04B2235/483C04B2235/5454C04B2235/96C04B41/4535
Inventor 魏华锦
Owner 佛山市寰田陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap