Ultralight sole material

A sole material and ultra-light technology, applied in the field of shoe materials, can solve problems such as poor anti-slip performance, water resistance, and poor elongation, and achieve the effects of improving rebound comfort, improving portability, and ensuring wear resistance

Inactive Publication Date: 2017-01-04
佛山市南海宏展鞋材有限公司
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It has defects such as heavy weight, poor slip resistance, easy breakage, poor elongation, and water resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] An ultra-light shoe sole material, prepared from the following raw materials in parts by weight: 35 parts of isoprene rubber, 35 parts of butadiene rubber, 20 parts of EVA foam material powder, 7 parts of fumed white carbon black, and 1.5 parts of nano zinc oxide , 2.5 parts of microporous physical foaming agent, 1.5 parts of anti-aging agent, and 1.5 parts of active agent.

[0011] It is formed by high temperature, high pressure, internal mixing and mixing vulcanizing machine.

Embodiment 2

[0013] An ultra-light shoe sole material, prepared from the following raw materials in parts by weight: 30 parts of isoprene rubber, 30 parts of butadiene rubber, 20 parts of EVA foam material powder, 5 parts of fumed white carbon black, and 1 part of nano-zinc oxide , 2 parts of microporous physical foaming agent, 1 part of anti-aging agent, and 1 part of active agent. It is formed by high temperature, high pressure, internal mixing and mixing vulcanizing machine.

Embodiment 3

[0015] An ultra-light shoe sole material, prepared from the following raw materials in parts by weight: 40 parts of isoprene rubber, 40 parts of butadiene rubber, 20 parts of EVA foam material powder, 8 parts of fumed white carbon black, and 2 parts of nano-zinc oxide , 3 parts of microporous physical foaming agent, 2 parts of anti-aging agent, 2 parts of active agent. It is formed by high temperature, high pressure, internal mixing and mixing vulcanizing machine.

[0016] The comparison of the main physical properties of this ultra-light sole material with that of conventional common rubber soles is as follows:

[0017] serial number compare names Common ordinary rubber sole materials Super light foam (Brown.RUBBER) material 1 Tensile force (kg / cm 2 ) 100 100 2 extend(%) 450 600 3 Density (g / cm 3 1.12-1.2 Below 0.95 (floating on the water surface) 4 Hardness (A) 60A 60A 5 (DIN) wear resistance (mm 3 ) 200 Below 150 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an ultralight sole material. The ultralight sole material is prepared from raw materials in parts by weight as follows: 30-40 parts of isoprene rubber, 30-40 parts of polybutadiene, 20 parts of an EVA (ethylene vinyl acetate copolymer) foaming material, 5-8 parts of fumed silica, 1-2 parts of nano-zinc oxide, 2-3 parts of a microporous physical foaming agent, 1-2 parts of an anti-aging agent and 1-2 parts of an active agent. By means of the characteristics that the volume density / ratio of the ultralight sole material is 0.95 or lower, the ultralight sole material floats on the water surface completely, the portability of the sole material is improved, the original wear resistance and non-slip performance of rubber can be guaranteed, and the resilience comfort is improved.

Description

technical field [0001] The invention relates to the technical field of shoe materials, in particular to an ultralight shoe sole material. Background technique [0002] Existing materials for making shoe soles are mainly ordinary rubber, TPR thermoplastic rubber, PU polymer polyurethane synthetic materials and the like. It has defects such as heavy weight, poor anti-slip performance, easy to break, poor elongation, and water resistance. Contents of the invention [0003] The object of the present invention is to provide an ultra-light shoe sole material to solve the above technical problems. [0004] To achieve the above object, the present invention adopts the following technical solutions: [0005] An ultra-light shoe sole material, prepared from the following raw materials in parts by weight: 30-40 parts of isoprene rubber, 30-40 parts of butadiene rubber, 20 parts of EVA foam material powder, and 5-8 parts of fumed white carbon black , 1-2 parts of nano-zinc oxide, 2...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/00C08L23/08C08K13/02C08K3/36C08K3/22C08J9/12A43B13/04
CPCC08L9/00A43B13/04C08J9/12C08J2205/044C08J2309/00C08J2423/08C08K2201/011C08L2203/14C08L2205/025C08L2205/03C08L23/0853C08K13/02C08K3/36C08K2003/2296
Inventor 滕孟林
Owner 佛山市南海宏展鞋材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com