Modified polyethylene corrugated pipe and preparing method thereof

A technology of polyethylene and bellows, which is applied in the direction of hoses, pipes, mechanical equipment, etc., can solve the problems of poor low-temperature impact resistance, low thermal deformation temperature, and poor heat resistance, and achieve good low-temperature impact resistance, Effect of high heat distortion temperature, excellent flame retardancy and electrical insulation

Inactive Publication Date: 2017-01-11
JIANGSU CHANGFENG BELLOWS CO LTD
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the polyethylene corrugated pipe commonly used in the industry has a low heat d

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0012] [Example 1]

[0013] First, take 300 parts of polyethylene, 40 parts of polypropylene, 15 parts of polytetrafluoroethylene, 10 parts of calcium stearate, 16 parts of carbon black, 30 parts of EVA resin, 24 parts of sodium silicate powder, and Malay 36 parts of acid anhydride.

[0014] Then, pour the raw materials into a mixer and mix them at a speed of 40 rpm for 20 minutes. After the mixture is evenly mixed, add the mixture to a twin-screw extruder for blending and extrusion, and then granulate to obtain pelletized modified polyethylene Then pour the obtained granular modified polyethylene material into a potassium permanganate solution with a concentration of 5%, soak it for 5 hours, and dry it naturally before use.

[0015] Then, the pelletized modified polyethylene material is added to the extrusion molding machine, and the modified polyethylene corrugated pipe is manufactured by the extrusion molding method.

[0016] Finally, put the obtained modified polyethylene bellows...

Example Embodiment

[0017] [Example 2]

[0018] First, take 320 parts of polyethylene, 50 parts of polypropylene, 25 parts of polytetrafluoroethylene, 12 parts of calcium stearate, 22 parts of carbon black, 40 parts of EVA resin, 28 parts of sodium silicate powder, and Malay 42 parts of acid anhydride.

[0019] Then, pour the raw materials into the mixer and mix them at a speed of 60rpm for 15 minutes. After evenly mixing, add the mixture to the twin-screw extruder for blending and extrusion, and then granulate to obtain pelletized modified polyethylene Then pour the obtained granular modified polyethylene material into a potassium permanganate solution with a concentration of 8%, soak it for 3 hours, and dry it naturally before use.

[0020] Then, the pelletized modified polyethylene material is added to the extrusion molding machine, and the modified polyethylene corrugated pipe is manufactured by the extrusion molding method.

[0021] Finally, put the modified polyethylene bellows into an oven at 45°...

Example Embodiment

[0022] [Example 3]

[0023] First, take 310 parts of polyethylene, 45 parts of polypropylene, 20 parts of polytetrafluoroethylene, 11 parts of calcium stearate, 19 parts of carbon black, 35 parts of EVA resin, 26 parts of sodium silicate powder, and Malay 39 parts of acid anhydride.

[0024] Then, pour the raw materials into the mixer and mix them at a speed of 50 rpm for 18 minutes. After the mixture is evenly mixed, the mixture is added to the twin-screw extruder for blending and extrusion, and then pelletized to obtain pelletized modified polyethylene Then pour the obtained granular modified polyethylene material into a potassium permanganate solution with a concentration of 6.5%, soak it for 4 hours, and dry it naturally before use.

[0025] Then, the pelletized modified polyethylene material is added to the extrusion molding machine, and the modified polyethylene corrugated pipe is manufactured by the extrusion molding method.

[0026] Finally, put the obtained modified polyethy...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a modified polyethylene corrugated pipe and preparing method thereof. The modified polyethylene corrugated pipe is made of modified polyethylene material which comprises, by weight, the following raw material: 300-320 parts of polyethylene, 40-50 parts of polypropylene, 15-25 parts of polytetrafluoroethylene, 10-12 parts of calcium stearate, 16-22 parts of carbon black, 30-40 parts of EVA resin, 24-28 parts of sodium silicate powder, 36-42 parts of maleic anhydride. The modified polyethylene corrugated pipe has relatively high heat distortion temperature, comparatively good low-temperature impact resistance performance, and can be used in the environment of -20-80oC for a long time. The modified polyethylene corrugated pipe also has excellent flame retardance and electrical insulation.

Description

technical field [0001] The invention relates to the field of corrugated pipe manufacturing, more precisely, it relates to a modified polyethylene corrugated pipe and a preparation method thereof. Background technique [0002] Polyethylene corrugated pipe is a relatively common corrugated pipe with a wide range of applications. However, the polyethylene corrugated pipe commonly used in the industry has a low heat distortion temperature, poor heat resistance, and poor low temperature impact resistance. Contents of the invention [0003] The invention mainly solves the technical problems existing in the prior art, thereby providing a modified polyethylene corrugated pipe and a preparation method thereof. [0004] Above-mentioned technical problem of the present invention is mainly solved by following technical scheme: [0005] A modified polyethylene bellows, made of modified polyethylene material, the modified polyethylene material is composed of the following raw mate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/06C08L23/12C08L27/18C08L23/08C08K13/02C08K5/098C08K3/04C08K3/34C08K5/1539F16L11/11
CPCC08L23/06C08L2201/02C08L2203/18C08L2205/02C08L2205/035F16L11/11C08L23/12C08L27/18C08L23/0853C08K13/02C08K5/098C08K3/04C08K3/34C08K5/1539
Inventor 姜爱荣
Owner JIANGSU CHANGFENG BELLOWS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap