Annealing method of exterior aluminum wire of composite-core soft aluminum stranded wire

A technology of aluminum stranded wire and composite core, which is applied in the field of annealing the outer layer of the aluminum wire of the composite core flexible aluminum stranded wire, can solve the problems of a single annealing process of the aluminum wire, the inability to meet the range of the stranded wire, and the complicated operation. Avoid appearance damage, improve economic and social benefits, and avoid the effect of blackening of aluminum wires

Inactive Publication Date: 2017-01-11
JIANGSU PROVINCE WEINENGDA WIRE & CABLE
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the deficiencies of the prior art, the present invention provides a method for annealing the outer layer aluminum wire of the composite core soft aluminum stranded wire, which solves the problem that the aluminum wire annealing process is very single, and the operation is complicated, which cannot meet the tolerance range of the stranded wire The problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] S1. Material selection: According to the specific specifications required for the production of fiber-reinforced resin-based composite core soft aluminum stranded wire, select the aluminum wire that meets the requirements for wire drawing and stranding;

[0028] S2. Heating: heat the aluminum wire and the heating furnace for heating, and heat the temperature to 400°C, place the selected aluminum wire inside the heating furnace, and start the heating treatment;

[0029] S3. Heat preservation treatment: place the required aluminum wires in the heating furnace, and maintain the temperature at 400°C for 3 hours, and keep the aluminum wires standing still, and start high-temperature storage;

[0030] S4: Cooling treatment: Change the power of the heating furnace to reduce the temperature inside the heating furnace. The temperature sensor can detect the temperature in the heating furnace at any time, and the staff can understand it more clearly. The temperature is more conven...

Embodiment 2

[0035] S1. Material selection: According to the specific specifications required for the production of fiber-reinforced resin-based composite core soft aluminum stranded wire, select the aluminum wire that meets the requirements for wire drawing and stranding;

[0036] S2. Heating: heat the aluminum wire and the heating furnace for heating, and heat the temperature to 450°C, place the selected aluminum wire inside the heating furnace, and start the heating treatment;

[0037] S3. Heat preservation treatment: place the required aluminum wires in the heating furnace, and maintain the temperature at 450°C for 3 hours, and keep the aluminum wires standing still, and start high-temperature storage;

[0038] S4: Cooling treatment: change the power of the heating furnace, lower the temperature inside the heating furnace, and lower the temperature in the heating furnace at a rate of 20°C / h, and the cooling time is 8 hours;

[0039] S5 Cooling: Prepare a cold water tank, the temperatur...

Embodiment 3

[0043] S1. Material selection: According to the specific specifications required for the production of fiber-reinforced resin-based composite core soft aluminum stranded wire, select the aluminum wire that meets the requirements for wire drawing and stranding;

[0044] S2. Heating: heat the aluminum wire and the heating furnace for heating, and heat the temperature to 500°C, place the selected aluminum wire inside the heating furnace, and start the heating treatment;

[0045] S3. Heat preservation treatment: place the required aluminum wires in the heating furnace, and maintain the temperature at 500°C for 3 hours, and keep the aluminum wires standing still, and start high-temperature storage;

[0046] S4: Cooling treatment: change the power of the heating furnace, lower the temperature inside the heating furnace, and lower the temperature in the heating furnace at a rate of 20°C / h, and the cooling time is 8 hours;

[0047] S5 Cooling: Prepare a cold water tank, the temperatur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an annealing method of an exterior aluminum wire of a composite-core soft aluminum stranded wire, comprising the following steps of S1, material selection: selecting an aluminum wire meeting specifications; S2, heating: heating the demanded aluminum wire and a heating furnace; S3, insulation treatment: standing the demanded aluminum wire in the heating furnace; S4, decreasing temperature treatment: decreasing the internal temperature of the heating furnace; S5, cooling: quickly placing the aluminum wire in a cold water basin; S6, drying: placing the cooled aluminum wire on a blow drying machine; S7, oil coating: coating the aluminum wire surface with oxidation-resistant oil. By the annealing method, the aluminum wire is relatively strong in plasticity to facilitate cutting and cold deformation and the aluminum wire stranding process can be completed, and thus the annealing method can be widely used and popularized, and economic and social benefits are increased.

Description

technical field [0001] The technical field of aluminum stranded wire processing technology of the present invention is specifically a method for annealing the outer layer aluminum-shaped wire of a composite core soft aluminum stranded wire. Background technique [0002] With the sustained and stable growth of my country's national economy, energy construction will become the key to sustainable development, and electricity is the main body of clean secondary energy capacity. Most of the energy must be converted into electricity before it can be effectively used. The origin of our country's energy Concentrated in the southwest and northwest regions, while a large amount of energy consumption is concentrated in the industrially developed southeast coastal regions. [0003] Annealing heat treatment is divided into complete annealing, incomplete annealing and stress relief annealing, diffusion annealing, spheroidizing annealing, recrystallization annealing, the mechanical properti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01B13/00H01B13/02
CPCH01B13/0016H01B13/02
Inventor 刘万龙
Owner JIANGSU PROVINCE WEINENGDA WIRE & CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap