Flame-retarding, acid-alkali-resisting wear-resisting fire hose material

A fire hose, acid and alkali resistance technology, applied in the field of fire protection, can solve the problems of heat damage to the fire hose, and achieve the effect of superior flame retardant and improved product performance.

Inactive Publication Date: 2017-01-25
袁华
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the unpredictable high heat generated by different environments during a fire, so...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Flame-retarding, acid-alkali-resisting wear-resisting fire hose material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The flame-retardant acid and alkali-resistant wear-resistant fire-fighting hose material in this embodiment is composed of the following parts by mass: 22 parts of rosin resin, 20 parts of p-tert-octylphenol formaldehyde resin, 20 parts of amino resin, and polyethylene Wax emulsion 18 parts, tall oil fatty acid 20 parts, butyl acetate 20 parts, amyl propionate 18 parts, diethylene glycol ethyl ether 20 parts, dimethyl fumarate 20 parts, sodium perborate 18 parts, imidazoline 18 parts, 18 parts of ammonium fluorosilicate, 20 parts of guanidine phosphate powder, 18 parts of phenyltriethoxysilane, 16 parts of sodium pyrophosphate, 20 parts of chrome green, 18 parts of chromium chloride, 16 parts of menthol, chromic acid 18 parts of barium powder, 16 parts of iron orthophosphate, 16 parts of triethylene glycol diisocaprylate, 16 parts of tricresol phosphate, 14 parts of decabromodiphenyl ether, 10 parts of nano magnesium hydroxide, 8 parts of lignin, 8 parts of morpholine, 8...

Embodiment 2

[0022] The flame-retardant acid and alkali resistant wear-resistant fire hose material in this embodiment is composed of the following parts by mass: 24 parts of rosin resin, 22 parts of p-tert-octylphenol formaldehyde resin, 22 parts of amino resin, polyethylene 20 parts of wax emulsion, 22 parts of tall oil fatty acid, 22 parts of butyl acetate, 20 parts of amyl propionate, 22 parts of diethylene glycol ether, 22 parts of dimethyl fumarate, 20 parts of sodium perborate, imidazoline 20 parts, 20 parts of ammonium fluorosilicate, 22 parts of guanidine phosphate powder, 20 parts of phenyltriethoxysilane, 18 parts of sodium pyrophosphate, 22 parts of chrome green, 20 parts of chromium chloride, 18 parts of menthol, chromic acid 20 parts of barium powder, 18 parts of iron orthophosphate, 18 parts of triethylene glycol diisocaprylate, 18 parts of tricresol phosphate, 16 parts of decabromodiphenyl ether, 12 parts of nano magnesium hydroxide, 10 parts of lignin, 10 parts of morpholin...

Embodiment 3

[0028] The flame-retardant acid and alkali resistant wear-resistant fire hose material in this embodiment is composed of the following parts by mass: 26 parts of rosin resin, 24 parts of p-tert-octylphenol formaldehyde resin, 24 parts of amino resin, and polyethylene 22 parts of wax emulsion, 24 parts of tall oil fatty acid, 24 parts of butyl acetate, 22 parts of pentyl propionate, 24 parts of diethylene glycol ethyl ether, 24 parts of dimethyl fumarate, 22 parts of sodium perborate, imidazoline 22 parts, 22 parts of ammonium fluorosilicate, 24 parts of guanidine phosphate powder, 22 parts of phenyltriethoxysilane, 20 parts of sodium pyrophosphate, 24 parts of chrome green, 22 parts of chromium chloride, 20 parts of menthol, chromic acid 22 parts of barium powder, 20 parts of iron orthophosphate, 20 parts of triethylene glycol diisocaprylate, 20 parts of tricresol phosphate, 18 parts of decabromodiphenyl ether, 14 parts of nano-magnesium hydroxide, 12 parts of lignin, 12 parts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a flame-retarding, acid-alkali-resisting wear-resisting fire hose material. The flame-retarding, acid-alkali-resisting wear-resisting fire hose material is prepared from rosin resin, p-tert-octyl phenolformaldehyde resin, amino resin, polyethylene wax emulsion, tall oil fatty acid, butyl acetate, isoamyl propionate, diethylene glycol dimethyl ether, dimethyl fumarate, sodium perborate, imidazoline, ammonium fluosilicate, guanidine phosphate powder, phenyl triethoxy silane, sodium pyrophosphate, chromium oxide, chromium chloride, menthol, barium chromate powder, ferrous orthophosphate, ethylenedioxydiethyl bis, tricresol phosphate ester, decabromodiphenyl ether, nanometer magnesium hydroxide, lignin, morpholine, polyoxyethylene polyoxy propyl alcohol amine ether, alkyl polyglucoside, propylamine, sodium ricinoleic acid. The product has excellent flame retardance, acid-base resistance, anti-mildew and anti-microbial performances, and the product performance is improved.

Description

Technical field [0001] The invention relates to a flame-retardant acid and alkali resistant wear-resistant fire hose material, which belongs to the technical field of fire protection. Background technique [0002] Fire hose is a hose used to transport high-pressure water or foam and other flame-retardant liquids. It is easy to lay when used and has become one of the most important fire-fighting tools in daily life. Due to the unpredictable high heat generated in different environments during a fire, some burning materials will generate high radiant heat, which will cause the fire hose to be heated and damaged. Improve the existing fire hose to make the hose resistant to high pressure, abrasion, high temperature, durable, not easy to leak, low resistance, can be bent and folded at will, easy to use, and can perform better in fire fighting operations effect. Summary of the invention [0003] The purpose of the present invention is to provide a flame-retardant, acid- and alkali-res...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L93/04C08L61/06C08L61/20C08L23/06C08L97/00C08K13/02C08K3/38C08K3/16C08K3/24C08K3/22C08K5/17C08K5/103
CPCC08L93/04C08K2201/011C08L2201/02C08L2205/02C08L2205/035C08L61/06C08L61/20C08L23/06C08L97/005C08K13/02C08K3/38C08K3/16C08K3/24C08K2003/2224C08K5/17C08K5/103
Inventor 袁华
Owner 袁华
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap