Method for calcining active lime
A technology of active lime and calcination, which is applied in the direction of lime production, etc., can solve the problems of leftover scraps and stone powder occupation, land pollution and environmental pollution, achieve high-efficiency calcination, improve resource utilization rate and lime enterprise production efficiency, and realize waste utilization. Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0027] Example 1
[0028] Weigh the materials according to the following ratio:
[0029] Limestone slag 0.2 tons
[0030] Stone powder 0.7 tons
[0031] Powdered calcium oxide 0.05 tons
[0032] 0.05 tons of water
[0033] The powdery calcium oxide and water in the above raw materials are added separately, and after being stirred and mixed uniformly, they are pressed into cube-shaped bricks with hydraulic forming equipment.
[0034] Stack the obtained limestone bricks to a height of 10 stories, and send them to a drying furnace by a flat trolley for drying. The temperature of the drying furnace is controlled between 100 and 300°C. After drying for 3 hours, it is transferred to a tunnel kiln for calcination as follows. The front section of the tunnel kiln is 5m, the temperature is controlled at 300℃~800℃, and the stone brick passing time is about 5h; the middle section of the tunnel kiln is 8m, the temperature is controlled at 800℃~1000℃, and the stone brick passing time is about 7.5h; th...
Example Embodiment
[0035] Example 2
[0036] Weigh the materials according to the following ratio:
[0037] Limestone slag 0.5 tons
[0038] Stone powder 0.45 tons
[0039] 0.05 tons of water
[0040] The above-mentioned raw materials are stirred and mixed uniformly, and pressed into cylindrical bricks with hydraulic forming equipment.
[0041] Stack the obtained limestone bricks to a height of 15 floors, and send them to a drying furnace by a flat trolley for drying. The temperature of the drying furnace is controlled between 100 and 300°C. After drying for 3 hours, it is transferred to a tunnel kiln for calcination as follows. The front section of the tunnel kiln is 5m, the temperature is controlled at 300℃~800℃, and the stone brick passing time is about 5h; the middle section of the tunnel kiln is 8m, the temperature is controlled at 800℃~1000℃, and the stone brick passing time is about 7.5h; the back section of the tunnel kiln is 5m, the temperature is It is controlled at 800℃~100℃, and the stone bri...
Example Embodiment
[0042] Example 3
[0043] Weigh the materials according to the following ratio:
[0044] Limestone slag 0.5 tons
[0045] Stone powder 0.45 tons
[0046] 0.05 tons of water
[0047] The above-mentioned raw materials are stirred and mixed uniformly, and pressed into a cake-shaped brick with hydraulic forming equipment.
[0048] Stack the obtained limestone bricks to a height of 15 floors, and send them to a drying furnace by a flat trolley for drying. The temperature of the drying furnace is controlled between 100 and 300°C. After drying for 3 hours, it is transferred to a tunnel kiln for calcination as follows. The front section of the tunnel kiln is 5m, the temperature is controlled at 300℃~800℃, and the stone brick passing time is about 5h; the middle section of the tunnel kiln is 8m, the temperature is controlled at 800℃~1000℃, and the stone brick passing time is about 7.5h; the back section of the tunnel kiln is 5m, the temperature is It is controlled at 800℃~100℃, and the stone br...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap