Cast steel part for nuclear power unit and production technology thereof

A production process and technology for nuclear power units, which are applied in the field of zero-defect and high-quality cast steel parts for nuclear use and their production processes, can solve the problems of poor mechanical properties of cast steel parts, low product quality, and difficult production, etc. Achieve the effect of improving solid solubility, preventing grain coarsening, good working performance and service life

Active Publication Date: 2017-02-08
SANMING CITY YIJUN MACHINERY FOUNDRY
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The invention provides a nuclear cast steel part and its production process, and its purpose is to s...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cast steel part for nuclear power unit and production technology thereof
  • Cast steel part for nuclear power unit and production technology thereof
  • Cast steel part for nuclear power unit and production technology thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A cast steel component used for nuclear power units, the steps of its production process are as follows:

[0034] (1) Steel shavings and low-carbon punched briquettes without rust are heated and melted in an electric furnace to form molten steel in a molten state.

[0035] (2) Send the molten steel into the oxygen top-blown converter, and oxidize and remove Si, Mn, P, S, C, Ni and Cr from the molten steel to obtain low-impurity molten steel.

[0036] (3) Refining and purifying low-impurity molten steel in an AOD refining furnace.

[0037] (4) Add ferrosilicon, electrolytic manganese, low-carbon ferrochrome and metal zirconium to the refined molten steel for smelting.

[0038] (5) Add the cleaned and returned material of the same grade for smelting. After the molten steel is melted, take a sample of the molten steel for chemical composition analysis, that is, use a portable spectrometer to quickly analyze the chemical composition of the molten steel sample in front of t...

Embodiment 2

[0062] A cast steel component used for nuclear power units, the steps of its production process are as follows:

[0063] (1) Steel shavings and low-carbon punched briquettes without rust are heated and melted in an electric furnace to form molten steel in a molten state.

[0064] (2) Send the molten steel into the oxygen top-blown converter, and oxidize and remove Si, Mn, P, S, C, Ni and Cr from the molten steel to obtain low-impurity molten steel.

[0065] (3) Refining and purifying low-impurity molten steel in an AOD refining furnace.

[0066] (4) Add ferrosilicon, electrolytic manganese, low-carbon ferrochrome and metal zirconium to the refined molten steel for smelting.

[0067] (5) Add the cleaned and returned material of the same grade for smelting. After the molten steel is melted, take a sample of the molten steel for chemical composition analysis, that is, use a portable spectrometer to quickly analyze the chemical composition of the molten steel sample in front of t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Yield strengthaaaaaaaaaa
Yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a zero-defect high-quality cast steel part for nuclear power. The cast steel part is characterized in that the cast steel part is chemically composed of, by weight, 0.18% to 0.20% of C, less than or equal to 0.60% of Si, 0.60% to 0.80% of Mn, less than or equal to 0.02% of P, less than or equal to 0.015% of S, 1.35% to 1.50% of Cr, less than or equal to 0.50% of Ni, 0.90% to 1.10% of Mo, 0.20% to 0.30% of V, less than or equal to 0.025% of Sn, 0.08% to 0.12% of Zr, the balance Fe and unavoidable trace impurities. The invention further discloses a technology used for producing the cast steel part, and according to the technology, the cast steel part has no defects, is high in quality, and is good in abrasion resistance and corrosion resistance, and high in toughness when in the high-temperature environment, and therefore, the cast steel part is suitable for a nuclear power unit.

Description

technical field [0001] The invention relates to a cast steel part and its production process, in particular to a nuclear zero-defect high-quality cast steel part and its production process. Background technique [0002] Cast steel parts for nuclear use are used in key positions of nuclear equipment. Because other processes cannot be manufactured or the production cost is too high technically, nuclear parts for nuclear use are produced by casting as needed. Nuclear equipment is high-end equipment. Due to the needs of operating environment, safety and durability, there are higher requirements for some performance and quality of cast steel parts. In addition to meeting the conventional mechanical performance requirements, since its operation often reaches a high temperature above 500°C, it is required to have good performance at high temperatures. [0003] The cast steel parts (such as cylinders, half-ring castings, etc.) are important parts of nuclear power units, and their q...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/50C22C38/46C22C38/44C22C38/28C22C38/24C22C38/22C22C38/04C22C38/02C22C33/06C21D1/18C21C7/06
CPCC21C7/0006C21C7/06C21D1/18C22C33/06C22C38/008C22C38/02C22C38/04C22C38/22C22C38/24C22C38/28C22C38/44C22C38/46C22C38/50
Inventor 刘渊毅蔡建黄高翔郑明华刘薇
Owner SANMING CITY YIJUN MACHINERY FOUNDRY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap