Preparing method for easy-care fabric

A textile and air technology, applied in the field of preparation of non-iron textiles, can solve the problems of easy wrinkling, poor non-iron performance, etc., and achieve the effects of excellent antibacterial, good non-iron performance, and good moisture absorption and air permeability.

Inactive Publication Date: 2017-02-08
EASTERN LIAONING UNIV
View PDF8 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the wearable textiles made of these fibers generally have problems such as easy wrinkling and poor non-ironing performance during wearing and washing, and subsequent non-ironing finishing is required to improve their non-ironing performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A method for preparing non-iron textiles, including the following steps:

[0024] S1. Blending 3 parts by weight of high-elasticity artificial silk fiber and 1.2 parts by weight of cotton fiber treated with air low-temperature plasma as warp yarn;

[0025] S2, blending 3 parts by weight of hemp fiber and 4 parts by weight of polyacrylonitrile fiber as weft yarn;

[0026] S3. Take the warp yarn obtained in step S1 and the weft yarn obtained in step S2, and weave the grey fabric according to the set weave structure and warp and weft density;

[0027] S4. Put the grey cloth obtained in step S3 into the finishing solution for ultrasonic padding treatment, then wash with water and dry to obtain it; the drying operation includes preliminary drying and re-drying of the fabric after padding, the temperature of the initial drying is 85℃, the temperature of re-bake is 145℃

[0028] The finishing liquid contains the following components:

[0029] Core-shell acrylic elastic emulsion 7 parts,...

Embodiment 2

[0031] A method for preparing non-iron textiles, including the following steps:

[0032] S1. Blending 3.5 parts by weight of high-elasticity artificial silk fiber and 1.8 parts by weight of cotton fiber treated with air low-temperature plasma as warp yarn;

[0033] S2. Blending 3.5 parts by weight of hemp fiber and 5 parts by weight of polyacrylonitrile fiber as weft yarn;

[0034] S3. Take the warp yarn obtained in step S1 and the weft yarn obtained in step S2, and weave the grey fabric according to the set weave structure and warp and weft density;

[0035] S4. Put the grey cloth obtained in step S3 into the finishing solution for ultrasonic padding treatment, then wash with water and dry to obtain it; the drying operation includes preliminary drying and re-drying of the fabric after padding, the temperature of the initial drying is 85℃, the temperature of re-bake is 145℃

[0036] The finishing liquid contains the following components:

[0037] Core-shell acrylic elastic emulsion 15 p...

Embodiment 3

[0039] A method for preparing non-iron textiles, including the following steps:

[0040] S1. Blending 3.25 parts by weight of high-elasticity artificial silk fiber and 1.5 parts by weight of cotton fiber treated with air low temperature plasma as warp yarn;

[0041] S2. Blending 3.25 parts by weight of hemp fiber and 4.5 parts by weight of polyacrylonitrile fiber as weft yarn;

[0042] S3. Take the warp yarn obtained in step S1 and the weft yarn obtained in step S2, and weave the grey fabric according to the set weave structure and warp and weft density;

[0043] S4. Put the grey cloth obtained in step S3 into the finishing solution for ultrasonic padding treatment, then wash with water and dry to obtain it; the drying operation includes preliminary drying and re-drying of the fabric after padding, the temperature of the initial drying is 85℃, the temperature of re-bake is 145℃

[0044] The finishing liquid contains the following components:

[0045] Core-shell acrylic elastic emulsion ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparing method for an easy-care fabric. High-elastic imitated silk fibers and cotton fibers processed via air low-temperature plasma are blended to form warp yarns; hemp fibers and polyacrylonitrile fibers are blended to form weft yarns; a gray fabric is weaved according to a set tissue structure and thread counts; the acquired gray fabric is ultrasonic wave-padded in finishing liquid, and then washed and dried; and at last, the easy-care fabric can be achieved. The fabric has great easy-care performance and softness and comfortableness; excellent performance of natural fibers can be remained; great moisture-absorbing and ventilating property can be achieved; and the easy-care fabric has great wrinkle resisting, shape-keeping and wash and wear properties.

Description

Technical field [0001] The invention relates to the field of textile production, in particular to a method for preparing non-iron textiles. Background technique [0002] Natural fibers such as cotton, wool, silk and hemp are commonly used textile fibers and have many excellent properties, such as soft hand feeling, comfortable wearing, soft luster and good antistatic properties. However, clothing textiles made of these fibers generally have problems such as easy wrinkling and poor non-ironing properties during wearing and washing, and they need to be subjected to subsequent non-iron finishing to improve their non-iron performance. Summary of the invention [0003] In order to solve the above problems, the present invention provides a method for preparing non-iron textiles. The resulting textile has good non-iron performance, softness and comfort, retains the excellent properties of natural fibers, good moisture absorption and air permeability, and has good wrinkle resistance and s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D15/00D03D15/08D06B13/00D06B15/00D06M15/263D06M13/123D06M13/207D06M13/00D06M15/03D06M11/70D06M15/53D06M15/227D06M11/36D06M10/02D06M13/402D06M13/165D03D15/217D03D15/283D03D15/47D03D15/50D03D15/56
CPCD06B13/00D06B15/00D06M10/025D06M11/36D06M11/70D06M13/123D06M13/165D06M13/207D06M13/402D06M15/03D06M15/227D06M15/263D06M15/53D06M16/006D10B2201/01D10B2201/02D10B2321/10D10B2401/061D03D15/47D03D15/56
Inventor 于学成毛成栋曹继鹏
Owner EASTERN LIAONING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com