Electric pure iron and electric pure iron part surface anti-oxidation treatment method
An electrical pure iron, anti-oxidation technology, applied in the field of surface treatment, can solve the problems of electrical pure iron being easy to rust, difficult to store, etc., and achieve the effects of reducing cost and time, being less prone to oxidation and rusting, and having good application prospects.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0029] The invention provides an anti-oxidation treatment method for the surface of electrical pure iron and its parts, including 1) machining; 2) parts inspection; 3) parts cleaning and 4) vacuum packaging.
[0030] Among them, 3) parts cleaning steps are: polishing liquid configuration - degreasing - mirror polishing - electrochemical polishing - emergency water rinsing - deionized water immersion - ultrasonic cleaning - drying.
[0031] Among them, in the steps of machining and parts inspection, the process of storage and transfer is protected by anti-rust oil.
[0032] Parts inspection step conditions: room temperature is 20 ℃, humidity is 50%;
[0033] Polishing solution configuration: put chromium trioxide into an electric fryer, pour phosphoric acid into it, heat the mixture to 70 °C, stir well until chromium trioxide is fully and evenly dissolved, wherein the mass ratio of chromium trioxide to phosphoric acid is 1:40 ;
[0034] Degreasing: add the parts into degreasi...
Embodiment 2
[0043] Similar to Example 1, the difference is:
[0044] Parts inspection step conditions: room temperature is 25 ℃, humidity is 30%;
[0045] Polishing liquid configuration: the mixture of chromium trioxide and phosphoric acid is heated to 80 ℃, and the mass ratio of chromium trioxide and phosphoric acid is 1:50;
[0046] Degreasing: add the parts into degreasing solution, heat to 90 °C for 30 min, and the degreasing solution consists of 1000 ml water and 66.66 g alkaline degreasing agent;
[0047] Electrochemical polishing: use φ1.0 stainless steel wire to fix the parts;
[0048] Emergency water flushing: the flow rate of tap water is 40 L / min, and the flushing time is 1 min;
[0049] Immersion in deionized water: Put the parts rinsed with emergency water into deionized water with a conductivity of 5 μS / cm, immerse them in deionized water for 3 minutes, and then place them in deionized water at 80 °C for 1 minute;
[0050] Ultrasonic cleaning: The time of ultrasonic clean...
Embodiment 3
[0054]Similar to Example 1, the difference is:
[0055] Parts inspection step conditions: humidity is 40%;
[0056] Polishing liquid configuration: the mixture of chromium trioxide and phosphoric acid is heated to 75 ℃, and the mass ratio of chromium trioxide and phosphoric acid is 1:45;
[0057] Degreasing: add the parts into degreasing solution, heat to 80 °C, and treat for 35 min. The degreasing solution consists of 1000 ml of water and 60 g of alkaline degreaser;
[0058] Emergency water flushing: the flow rate of tap water is 35 L / min, and the flushing time is 2 minutes;
[0059] Immersion in deionized water: Put the parts rinsed with emergency water into deionized water with a conductivity of 10 μS / cm, immerse them in deionized water for 2 minutes, and then place them in deionized water at 75 °C for 2 minutes;
[0060] Ultrasonic cleaning: The time of ultrasonic cleaning is 40 min and the frequency is 45 Hz;
[0061] Drying: the temperature is 60 °C, and the drying ti...
PUM
Property | Measurement | Unit |
---|---|---|
Conductivity | aaaaa | aaaaa |
Conductivity | aaaaa | aaaaa |
Conductivity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap