Method for preparing waterproof material by modifying surfaces of sisal fibers with water-based organosilicone

A technology of sisal fiber and waterproof material, which is applied in the direction of liquid repellent fiber, fiber treatment, plant fiber, etc., can solve the problems of complicated technical process and high cost, and achieve the effect of broadening research and application

Inactive Publication Date: 2017-02-15
GUILIN UNIVERSITY OF TECHNOLOGY
View PDF4 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the effective treatment of the surface of sisal fiber to improve its performance mainly includes: steam exp

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing waterproof material by modifying surfaces of sisal fibers with water-based organosilicone

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] 200 μL of silane coupling agent methyltrimethoxysilane was added dropwise to 105 g of PDMS emulsion (10% solid content), stirred and mixed evenly to obtain silicone emulsion immersion solution; sisal fibers were soaked in water after washing and drying In the immersion solution, ultrasonically disperse for 5 minutes, after soaking evenly, take out the sisal fiber and remove the excess immersion solution, and then place it at room temperature for curing to obtain the modified sisal fiber.

Embodiment 2

[0017] Add 500 μL of silane coupling agent methyltrimethoxysilane dropwise to 200 g of PDMS emulsion (solid content 10%), stir and mix evenly to obtain silicone emulsion immersion solution; wash and dry sisal fiber soaked in In the immersion solution, ultrasonically disperse for 5 minutes, after soaking evenly, take out the sisal fiber and remove the excess immersion solution, and then place it at room temperature for curing to obtain the modified sisal fiber.

Embodiment 3

[0019] Add 200 μL of silane coupling agent KH-550 dropwise to 105 g of PDMS emulsion (solid content 10%), stir and mix evenly to obtain a silicone emulsion immersion solution; soak the sisal fiber after washing and drying in the immersion solution , ultrasonically dispersed for 5 min, soaked evenly, took out the sisal fiber and removed the excess immersion liquid, and then placed it at room temperature to solidify, that is, the modified sisal fiber was obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for preparing a waterproof material by modifying surfaces of sisal fibers with water-based organosilicone. The method utilizes sisal fibers as raw materials, and through the simple immersion curing process, surfaces of the sisal fibers form organosilicone hydrophobic layers. The method which produces sisal fibers with high hydrophobicity through hydrophilicity change is a simple and effective sisal fiber surface modification method. The method has the advantages of use of cheap and easy raw materials with wide raw material sources and simple and fast preparation process. The method realizes the synergistic effects of organosilicone and sisal fibers and overcomes the defects of use of the single material. The organosilicone hydrophobic layer coats the sisal fiber surface so that the sisal fibers have hydrophobicity, fiber interface adhesion is improved and sisal fiber application development is broadened.

Description

technical field [0001] The invention belongs to the technical field of sisal fiber modification, and in particular relates to a method for preparing a waterproof material by modifying the surface of sisal fiber with water-based organic silicon. The surface modification method is simple and efficient, which makes the sisal fiber hydrophobic, improves its interfacial adhesion, and can broaden the research and application of the sisal fiber. Background technique [0002] As the most abundant green and environmentally friendly renewable resource on the earth, natural plant fiber has attracted extensive attention in its application and development. Sisal is a perennial natural hard fiber plant with leaves of the genus Agave. As an important natural tropical economic crop, it is widely planted in parts of southern my country. Sisal bundle fiber has hard texture, high strength, low density, high cellulose content, easy surface modification, low price, and is a renewable resource. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M15/643D06M13/513D06M101/06
CPCD06M15/643D06M13/513D06M2101/06D06M2200/12
Inventor 邓卫星彭锦雯权翼腾邓俊杰王敏徐旭刘远立
Owner GUILIN UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap