A kind of light-weight high-strength ceramic plate and preparation method thereof

A ceramic plate and high-strength technology, applied in the field of ceramics, can solve the problems of not conforming to outdoor high-altitude curtain walls, short service life, poor frost resistance, etc., to achieve convenient construction, save installation costs, and reduce building loads.

Active Publication Date: 2017-12-19
佛山市奥幕新型建材科技有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Although the bulk density of the above-mentioned architectural ceramics reaches 1.2-1.8 g / cm 3 and 1.96-2.33 g / cm 3 , but its water absorption rate reaches 5-9% and 10-22%, which is not safe and has a short service life, especially not suitable for dry hanging on external walls
[0008] In addition, the existing travertine and sandstone have poor frost resistance and do not meet the requirements for outdoor high-altitude curtain walls

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of light-weight high-strength ceramic plate and preparation method thereof
  • A kind of light-weight high-strength ceramic plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0124] Correspondingly, the present invention also provides a method for preparing a lightweight high-strength ceramic plate, comprising the following steps:

[0125] 1. Mix the raw materials according to the formula to obtain the mixture;

[0126] 2. Put the mixture into a ball mill for ball milling to obtain mud;

[0127] 3. Spray and granulate the ball-milled slurry to obtain powder;

[0128] 4. Press and form the powder to obtain a green body;

[0129] 5. Drying the compacted green body;

[0130] 6. Surface treatment is carried out on the dried green body to obtain the primary product;

[0131] 7. Sinter the primary product at a temperature of 1050-1120 degrees Celsius to obtain a bulk density of 1.55-2.1g / cm 3 , a finished product with a thickness of 18-30mm and a water absorption rate of 0.1-0.5%.

[0132] Preferably, the preparation method of the lightweight high-strength ceramic plate is as follows:

[0133] 1. Mix the raw materials according to the formula to ob...

Embodiment 1

[0142] Example 1 - artificial granite hanging boards for outdoor high-altitude curtain walls

[0143] (1) Formula: 1.5 parts of silicon carbide, 25 parts of ceramic waste solids, 10 parts of sludge or bottom sludge, 10 parts of bentonite, 0.1 part of body strengthening agent, and 0.1 part of debonding agent.

[0144] (2) Preparation method:

[0145] 1. Mix the raw materials according to the formula to obtain the mixture;

[0146] 2. Put the mixture into a ball mill for ball milling to obtain a slurry with a moisture content of 12%;

[0147] 3. Spray and granulate the ball-milled slurry to obtain a powder with a moisture content of 1%;

[0148] 4. Press and form the powder to obtain a green body;

[0149] 5. Drying the compacted green body to obtain a green body with a moisture content in the range of 0.1%;

[0150] 6. The dried green body is distributed by a special material truck for granite, and then 3D inkjet printing is carried out, so that the green body can restore t...

Embodiment 2

[0152] Example 2 - artificial marble hanging boards for outdoor high-altitude curtain walls

[0153] (1) Formula: 1.6 parts of silicon carbide, 28 parts of ceramic waste solids, 15 parts of sludge or bottom sludge, 15 parts of bentonite, 0.5 parts of body strengthening agent, and 0.2 parts of debonding agent.

[0154] (2) Preparation method:

[0155] 1. Mix the raw materials according to the formula to obtain the mixture;

[0156] 2. Put the mixture into a ball mill for ball milling to obtain a slurry with a moisture content of 13%;

[0157] 3. Spray and granulate the ball-milled slurry to obtain a powder with a moisture content of 1.5%;

[0158] 4. Press and form the powder to obtain a green body;

[0159] 5. Drying the compacted green body to obtain a green body with a moisture content in the range of 0.2%;

[0160] 6. The dried green body is clothed by a special marble material truck, and then 3D inkjet printing is carried out to restore the natural marble temperament o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
thicknessaaaaaaaaaa
modulusaaaaaaaaaa
Login to View More

Abstract

The invention discloses a light-weight high-strength ceramic plate. The light-weight high-strength ceramic plate is a light-weight ceramic plate which is fired at a firing temperature of 1050-1120 DEG C and has a honeycomb-like sealed pore internal structure, the volume weight is 1.55-2.1g / cm<3>, the thickness is 18-30mm, the water absorptivity is 0.1-0.5%, and the rupture modulus is no less than 20MPa.The light-weight high-strength ceramic plate is mainly prepared from the following raw materials: 1-3 parts of silicon carbide, 15-50 parts of ceramic waste solid, 10-35 parts of sludge or sediment, 10-35 parts of bentonite, 0.1-2 parts of green body enhancer and 0.1-3 parts of dispergator. Correspondingly, the invention also provides a preparation method of the light-weight high-strength ceramic plate. The light-weight high-strength ceramic plate has the advantages of light weight, high strength, low water absorptivity and high stone simulation degree, and can be dimensionally enlarged and thickened. When being used as an outdoor high-altitude curtain wall, the light-weight high-strength ceramic plate is very safe and convenient to construct, and the hanging cost is saved.

Description

technical field [0001] The invention relates to the field of ceramics, in particular to a lightweight high-strength ceramic plate and a preparation method thereof. Background technique [0002] In our country, ceramic products have been widely used in the interior and exterior wall decoration of buildings. The early buildings mostly used the wet paste process for the interior and exterior wall decoration construction of ceramic tiles. However, because the tiles that adopt the wet paste construction method are on the outer surface of the building, they are prone to aging, loosening and falling off under the effects of wind and rain erosion, earthquakes and temperature changes. In severe cases, it may cause a large amount of financial losses and casualties. [0003] With the development, experimentation and maturity of the ceramic panel curtain wall technology, the external wall dry-hanging ceramic panel curtain wall system, as the latest construction form of the building curt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/02C04B33/132C04B33/13
CPCC04B33/131C04B33/1321C04B33/1324C04B38/02C04B2235/3826C04B2235/77C04B2235/95C04B2235/96C04B38/0006Y02P40/60
Inventor 江建强
Owner 佛山市奥幕新型建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com