High-strength and lightweight travertine and preparation method thereof

A travertine and high-strength technology, applied in the field of lightweight high-strength travertine and its preparation, can solve the problems of not meeting the requirements of outdoor high-altitude curtain walls, short service life, poor frost resistance, etc., and achieve light weight, low water absorption, and convenient The effect of construction

Active Publication Date: 2017-03-08
佛山市奥幕新型建材科技有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the bulk density of the above-mentioned architectural ceramics reaches 1.2-1.8 g / cm 3 and 1.96-2.33g / cm 3 , but its water absorption rate reaches 5-9% and 10-22%, which is not safe and has a short service life, especially not suitable for dry hanging on external walls
[0007] Moreover, the existing travertine has poor frost resistance and does not meet the requirements for outdoor high-altitude curtain walls.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength and lightweight travertine and preparation method thereof
  • High-strength and lightweight travertine and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0113] Correspondingly, the present invention also provides a preparation method of light-weight high-strength travertine, comprising the following steps:

[0114] (1) Fabric preparation: mix the raw materials according to the fabric formula, ball mill and spray granulate to obtain the fabric;

[0115] (2) Prepare base material: mix the raw materials according to the base material formula, and obtain the base material through ball milling and spray granulation;

[0116] (3) Cloth: Double-layer cloth is made of fabric and bottom material according to the ratio, and the ratio of fabric and bottom material is 3-8:15-22;

[0117] (4) Compression: Press and shape the powder after cloth to obtain a green body;

[0118] (5) Drying: drying the pressed body;

[0119] (6) Firing: firing the dried green body at a firing temperature of 1050-1120 degrees Celsius to obtain the primary product;

[0120] (7) Polishing: Polish the primary product to obtain a bulk density of 1.55-1.9g / cm 3 ...

Embodiment 1

[0132] Example 1 - Travertine for outdoor high-altitude curtain wall

[0133] (1) Fabric formula: 2 parts of silicon carbide, 25 parts of ceramic waste solids, 10 parts of sludge or bottom mud, 10 parts of bentonite, 0.1 part of body strengthening agent, 0.1 part of debonding agent, and 10 parts of pore forming agent.

[0134] Base material formula: 2 parts of silicon carbide, 25 parts of ceramic waste solids, 10 parts of sludge or bottom mud, 10 parts of bentonite, 0.1 part of body strengthening agent, and 0.1 part of debonding agent.

[0135] (2) Preparation method:

[0136] (1) Preparation of fabric: mix the raw materials according to the fabric formula, and obtain a slurry with a moisture content of 12% through ball milling, and then spray granulate to obtain a fabric with a moisture content range of 1%;

[0137] (2) Preparation of base material: mix the raw materials according to the base material formula, obtain a slurry with a moisture content of 12% through ball milli...

Embodiment 2

[0143] Example 2 - Travertine for outdoor high-altitude curtain wall

[0144] (1) Fabric formula: 3 parts of silicon carbide, 30 parts of ceramic waste solids, 20 parts of sludge or bottom mud, 20 parts of bentonite, 1 part of body strengthening agent, 1 part of debonding agent, and 15 parts of pore forming agent.

[0145] Base material formula: 3 parts of silicon carbide, 30 parts of ceramic waste solids, 20 parts of sludge or bottom mud, 20 parts of bentonite, 1 part of body strengthening agent, and 1 part of debonding agent.

[0146] (2) Preparation method:

[0147] (1) Preparation of fabric: mix the raw materials according to the fabric formula, and obtain a slurry with a moisture content of 15% through ball milling, and then spray granulate to obtain a fabric with a moisture content range of 2%;

[0148](2) Preparation of base material: mix the raw materials according to the base material formula, obtain a slurry with a moisture content of 15% through ball milling, and t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Densityaaaaaaaaaa
Thicknessaaaaaaaaaa
Densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses high-strength and lightweight travertine. The travertine fired at the firing temperature of 1,050-1,120 DEG C and having a stereoscopic hole inside structure has the volume weight being 1.55-1.9 g / cm<3>, the thickness being 18-30 mm, the water absorption rate being 0.1%-1% and the modulus of rupture larger than or equal to 15 MPa. The high-strength and lightweight travertine comprises a surface material and a bottom material. Correspondingly, the invention further provides a preparation method of the high-strength and lightweight travertine. The high-strength and lightweight travertine is light in weight, high in strength and low in adsorption rate, has high stone simulation degree, can be made to be larger and thicker in size and is very safe and convenient to construct when used for high-altitude outdoor curtainwalls, and the hanging cost is saved.

Description

technical field [0001] The invention relates to the field of ceramics, in particular to a lightweight high-strength travertine and a preparation method thereof. Background technique [0002] In our country, ceramic products have been widely used in the interior and exterior wall decoration of buildings. The early buildings mostly used the wet paste process for the interior and exterior wall decoration construction of ceramic tiles. However, because the tiles that adopt the wet paste construction method are on the outer surface of the building, they are prone to aging, loosening and falling off under the effects of wind and rain erosion, earthquakes and temperature changes. In severe cases, it may cause a large amount of financial losses and casualties. [0003] With the development, experimentation and maturity of the ceramic curtain wall technology, the external wall dry-hanging ceramic curtain wall system, as the latest construction form of the architectural curtain wall, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/132C04B33/13C04B38/06
CPCC04B33/132C04B33/1321C04B38/06C04B38/068C04B38/0685C04B2235/3826C04B2235/77C04B2235/95C04B2235/96C04B38/0067Y02P40/60
Inventor 江建强
Owner 佛山市奥幕新型建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com