Reinforced heat-resistant electrostatic-spinning/electret composite fiber membrane filtering material and preparing method thereof

A composite fiber membrane and filter material technology, which is applied in electrospinning, spinning solution preparation, fiber treatment, etc., can solve the problems of charge stability easily affected by the environment, fast charge decay rate, and decrease in filtration efficiency, and achieve excellent Stable charge storage performance, improved filtration efficiency, and low air resistance effects

Inactive Publication Date: 2017-02-22
安徽名杰净化科技有限公司
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The traditional melt-blown nonwoven electret material is treated with electret, and the surface is charged to make it have a high filtration efficiency, but its charge stability is easily affected by the environment, and the charge decay rate is fast, and the filtration efficiency is greatly reduced.
In addition, the electret process, as a necessary post-treatment process, also increases the production cost to a certain extent

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0030] An enhanced heat-resistant electrospinning / electret composite fiber membrane filter material consists of the following raw material components in parts by weight: polyetherimide 80, silicon monoxide 10, powdered activated carbon 15, 3-aminopropyl triethyl Oxysilane coupling agent 2, glacial acetic acid 2, appropriate amount of deionized water, metatitanic acid 6, 0.6mol / L AgNO 3 Appropriate amount of solution, appropriate amount of N-methylpyrrolidone, graphene oxide 2, zinc nitrate hexahydrate 3, dimethylimidazole 6, methanol 36.

[0031] Specific steps are as follows:

[0032] (1) Preparation of silver-loaded nano-titanium dioxide:

[0033] Add metatitanic acid into deionized water, control the solution concentration at 0.6mol / L, heat to 115°C to keep it boiling, hydrolysis reaction occurs to form white metatitanic acid precipitate, centrifugal filtration, washing until no SO is detected in the precipitate 4 2- ions, impregnated in 0.6mol / L AgNO 3 solution, after ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a reinforced heat-resistant electrostatic-spinning / electret composite fiber membrane filtering material. The reinforced heat-resistant electrostatic-spinning / electret composite fiber membrane filtering material is prepared from, by weight, 75-85 parts of polyetherimide, 7-13 parts of silicon monoxide, 10-16 parts of powdered activated carbon, 1-2 parts of a 3-aminopropyltriethoxysilane coupling agent, 0.8-2 parts of glacial acetic acid, a proper amount of deionized water, 2-6 parts of metatitanic acid, a proper quantity of a AgNO3 solution of 0.6 mol / L, a proper amount of N-methyl-pyrrolidone, 1-2 parts of oxidized graphene, 1-3 parts of zinc nitrate hexahydrate, 3-9 parts of dimethyl imidazole and 25-40 parts of methyl alcohol. According to the reinforced heat-resistant electrostatic-spinning / electret composite fiber membrane filtering material, silicon nanowires containing alpha-quartz are prepared, the electrostatic-spinning / electret composite fiber filtering material is prepared with the electrospinning technique, the excellent charge storage stability is achieved, and the filtering efficiency of the filtering material is greatly improved; in addition, nano-silver is added to load nanometer titania, the antibacterial durability of the filtering material is improved, and the long-time efficient filtering effect is achieved.

Description

technical field [0001] The invention belongs to the field of air filtration, and in particular relates to a heat-resistant electrostatic spinning / electret composite fiber membrane filter material and a preparation method thereof. [0002] technical background [0003] With the deepening and rapid development of the industrialization process, the dust particles discharged into the atmosphere have increased sharply, among which PM2.5 (particulate pollutants with a particle size of less than 2.5µm) will cause serious harm to human health. It will directly enter the bronchi and cause diseases such as asthma, bronchitis, pneumoconiosis and cardiovascular disease. This is one of the main reasons for the sharp increase in lung cancer patients in my country. Therefore, air filter equipment has become a research hotspot, and the research and development of its core filter materials has become a top priority. [0004] The traditional melt-blown nonwoven electret material is treated wit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01D1/02D01D5/00D01F6/94D01F1/10
CPCD01D1/02D01D5/003D01D5/0069D01D5/0092D01F1/10D01F1/103D01F6/94
Inventor 殷友生
Owner 安徽名杰净化科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products