Lead-zinc accumulator plate

A battery and plate technology, applied in lead-acid batteries, battery electrodes, electrode carriers/current collectors, etc., can solve the problems of large water loss and self-discharge, decreased battery capacity, short battery life, etc., to achieve utilization and conversion The rate is fully saturated, the grid resistance is reduced, and the battery life is prolonged.

Inactive Publication Date: 2017-02-22
刘冠茂
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Existing lead-acid batteries have problems of large water loss and self-discharging during use, resulting in short battery life, especially sensitive to temperature, and the drop in battery capacity also leads to accidents

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The present invention will be described in further detail below in conjunction with specific embodiments.

[0017] The specific embodiment of the present invention is a lead-zinc storage battery plate, including a positive plate and a negative plate, the positive plate and the negative plate are connected through a conductive skeleton, and the positive plate is covered with a positive coating. The negative electrode plate is covered with a negative electrode coating, and the positive electrode plate and the negative electrode plate are both grid plate structures;

[0018] The positive plate includes 0.2-0.6% silver, 0.02-0.15% calcium, 0.1-0.4% tin, 0.01-0.05% aluminum, 98.5-99.6% lead, 0.03% zinc, 0.001% bismuth, 0.001% antimony;

[0019] The negative electrode includes 0.1-0.4% silver, 0.02-0.15% calcium, 0.05-0.8% tin, 0.01-0.05% aluminum, 98.4-99.7% lead, 0.03% zinc, 0.001% bismuth, 0.001% antimony;

[0020] Both the positive electrode coating and the negative elec...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a lead-zinc accumulator plate. The lead-zinc accumulator plate comprises a positive plate and a negative plate, wherein the positive plate and the negative plate are connected by a conducting skeleton; the positive plate is covered by a positive coating; the negative plate is covered by a negative coating; the positive plate and the negative plate are in a grid structure. The lead-zinc accumulator plate has the beneficial effects that the lead-zinc accumulator has good high current discharge stability, strong low temperature start ability, excellent corrosion resistance and long cyclic charge and discharge lives; the plate potential can be stabilized and the influences of other impurities can be reduced during floating charge because zinc is added, thus improving the charge efficiency, increasing the capacity and prolonging the accumulator life; the proportion of calcium is stabilized due to addition of aluminium, so that the grid resistance is reduced, the conductivity is enhanced and the water loss is reduced; the active substance mass is effectively increased and the conductivity and corrosion resistance of the accumulator are enhanced as the noble metal silver is added to the positive and negative plates, so that the use ratio and conversion ratio of the accumulator are fuller, discharge is more thorough, the endurance mileage is more permanent and the service life is longer.

Description

technical field [0001] The invention relates to a battery device, in particular to a pole plate of a lead-zinc storage battery. Background technique [0002] A battery made of lead and acid as a chemical reaction substance is called a lead-acid battery. It is a DC power supply that converts electrical energy into chemical energy when charging, and converts stored chemical energy into electrical energy when discharging. [0003] Lead-acid batteries have a maximum voltage of 2.0V in common system batteries. The second is its low cost, and the third is good high-rate discharge performance, good high and low temperature performance, and can work under the condition of -40-60°C. Easy to use with float charge No "memory" effect etc. Of course, lead-acid batteries also have some insurmountable disadvantages. First, their lifespan is relatively short, and long-term storage in a discharged state will lead to irreversible sulfation of the electrodes. There is a risk of explosion d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M4/66H01M10/06
CPCH01M4/661H01M4/666H01M10/06Y02E60/10
Inventor 刘冠茂
Owner 刘冠茂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products