Combtype macro monomer and preparation method thereof, polymer polyol and polyurethane foam

A macromonomer and polymer technology, applied to comb macromonomers and their preparation, can solve the problems of high product viscosity, easy polymerization, and many product particles, and achieve excellent stability, high conversion rate, and simple process. Effect

Active Publication Date: 2017-03-22
WANHUA CHEM GRP CO LTD
View PDF8 Cites 25 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the prior art, the product has high viscosity, many particles, and is easy to polymerize. In particular, maleic anhydride or phthalic anhydride is often used in the preparation process of the stabilizer, which is easy to sublime and block the gas phase pipeline, which increases the maintenance of the device. Expenses, in severe cases will cause the device to stop

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Combtype macro monomer and preparation method thereof, polymer polyol and polyurethane foam
  • Combtype macro monomer and preparation method thereof, polymer polyol and polyurethane foam
  • Combtype macro monomer and preparation method thereof, polymer polyol and polyurethane foam

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0084] step 1)

[0085] Add: 79.80 g of acrylic acid, polyethylene glycol with a weight average molecular weight of about 370 in a 1 liter reactor equipped with a stirrer, a heater, a thermocouple, a condensing device with a water separator, an inlet and an outlet device, and under nitrogen protection 450.71g, toluene 200g, hydroquinone 3g, p-toluenesulfonic acid 0.6g, mix well, maintain 110°C for 4h, then cool to room temperature.

[0086] Step 2)

[0087] Add 66.50 g of butadiene and 3 g of benzoyl peroxide (BPO) initiator into the reaction solution in step 1), raise the temperature to 80° C. under stirring, react for 2 hours, and obtain 1# comb-shaped macromer solution after cooling down.

Embodiment 2

[0089] step 1)

[0090] In a 1 liter reactor equipped with a stirrer, a heater, a thermocouple, a condensing device with a water separator, an inlet and an outlet device, under nitrogen protection, add: 22.07 g of acrylic acid, 119.41 g of polypropylene glycol with a weight average molecular weight of 370, 640 g of toluene, 0.8 g of hydroquinone, and 0.2 g of tert-butyl titanate were mixed uniformly, maintained at 120° C. for 4 h, and then cooled to room temperature.

[0091] Step 2)

[0092] Add 17.56 g of isoprene and 0.96 g of benzoyl peroxide (BPO) initiator into the reaction solution in step 1), raise the temperature to 90° C. under stirring, and react for 2 hours. Obtain 2# comb type macromonomer solution after cooling.

Embodiment 3

[0094] step 1)

[0095] In a 1-liter reactor equipped with a stirrer, a heater, a thermocouple, a condensing device with a water separator, an inlet and an outlet device, and under nitrogen protection, add: 89.43 g of methacrylic acid, polyethylene glycol with a weight average molecular weight of 290 235g of alcohol, 97.11g of polypropylene glycol with a weight-average molecular weight of 350, 320g of toluene, 2.4g of hydroquinone, and 0.5g of t-butyl titanate were mixed uniformly, and kept at 110°C for 4 hours, and then cooled to room temperature.

[0096] Step 2)

[0097] Add 54.93 g of butadiene and 3.36 g of benzoyl peroxide (BPO) initiator into the reaction liquid in step 1), raise the temperature to 80° C. under stirring, and react for 2 h. Obtain 3# comb type macromonomer solution after cooling.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a combtype macro monomer and a preparation method thereof, and polymer polyol prepared according to the combtype macro monomer. The preparation method includes the steps that a compound containing double bonds is reacted with dihydric alcohol at first; and then in the existence of an optional initiator, the monomer containing conjugated double bonds is added for carrying out a polymerization reaction, and accordingly the combtype macro monomer can be obtained. The combtype macro monomer is suitable for being used as a dispersion stabilizer of the polymer polyol, the viscosity is lowered, and the stability performance is excellent. Soft polyurethane foam prepared through the polymer polyol is high in performance, the VOC and odors are low, and the elongation at break and tensile strength are excellent.

Description

technical field [0001] The invention relates to the preparation of a macromonomer used in polymer polyols and its application in polymer polyols. Specifically, it relates to a comb-shaped macromonomer and a preparation method thereof, a method for preparing a polymer polyol using the macromonomer and the prepared polymer polyol, and also relates to a soft polymer polyol prepared using the polymer polyol. Quality polyurethane foam. Background technique [0002] Various types of graft polyols known in the art include polyisocyanate addition polyols, polyurea and / or polydiurea polyols, polymer polyols, and the like. Polymer polyol (POP) is the most widely used, and is mainly used to prepare suitable isocyanate-reactive components for polyurethane materials such as foams and elastomers. The two main types of polyurethane foam include slabstock foam and molded foam. Slabstock foam is used in the carpet, furniture and bedding industries. The primary use of slabstock foam is as...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F291/08C08F220/28C08F236/06C08F236/08C08G18/66C08G18/63C08G18/48C08G18/32C08G18/22C08G18/18C08J9/08C08G101/00
CPCC08F220/28C08F265/04C08F283/06C08G18/163C08G18/1825C08G18/1833C08G18/227C08G18/3275C08G18/3281C08G18/4072C08G18/48C08G18/632C08G18/633C08G18/657C08G18/6688C08F220/286C08F220/287C08F220/288C08G2110/0083C08F236/08C08F236/06
Inventor 李付国姜乃化鞠昌迅孙双翼李晶陈杰杨洗李文滨何金同
Owner WANHUA CHEM GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com