Cement tea ware preparation process based on reverse mold technology

A preparation process and tea utensil technology, which is applied in the field of cement handicraft preparation, can solve the problems of destroying the tea appreciation situation, etc., and achieve the effect of simple curing conditions, low energy consumption and smooth surface

Active Publication Date: 2017-03-29
WUHAN UNIV OF TECH
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] But at present, some cement handicrafts (mainly used for flower vessels) often contain rubber powder, latex, ammonium chloride, quick-setting agent and other ingredients that are prone to volatile odors. If they are used in tea vessels, it will destroy the tea appreciation situation. It must be composed of high-temperature calcined cement clinker and gypsum and admixtures without volatile odor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cement tea ware preparation process based on reverse mold technology
  • Cement tea ware preparation process based on reverse mold technology

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A process for preparing a cement tea utensil (cement tea tray) based on an inverted mold technology, comprising the following steps:

[0035] 1) Mold frame preparation: Select the black gold stone tea tray prepared for pouring as the template, and its specific size is 580mm×270mm×80mm, and use 12 10mm long pins to support the tea tray in the center on a cardboard mold frame with a size of 60cm×30cm×12cm ;

[0036] 2) Preparation of mold casting materials: select 903 translucent silica gel as the mold casting material, weigh about 18L of silica gel according to the volume of the mold frame, add a curing agent and mix (ethyl orthosilicate, the additive accounts for 2% of the silica gel mass), and then add cement ( 1% of the mass of silica gel), stir evenly as a mold casting material;

[0037] 3) Mold preparation: pour the mold casting material into the mold frame until it exceeds 10mm from the top of the tea tray, carefully remove the bubbles in the silica gel, and let i...

Embodiment 2

[0041] A process for preparing a cement tea utensil (cement tea pet) based on an inverted mold technology, comprising the following steps:

[0042] 1) Mold frame preparation: Select the tea pet prepared for pouring as the template, and its specific size is 50mm×30mm×30mm, and four 10mm long pins are used to centrally support the tea tray on a cardboard mold frame with a size of 60mm×50mm×50mm middle;

[0043] 2) Preparation of mold casting material: select 903 translucent silica gel as the mold casting material, weigh about 150ml of silica gel according to the volume of the mold frame, add a curing agent and mix (ethyl orthosilicate, the additive accounts for 1% of the mass of the silica gel), stir evenly as a mold pouring material;

[0044] 3) Mold preparation: pour the mold casting material into the mold frame until it exceeds 10mm from the top of the tea pet, carefully remove the bubbles in the silica gel, and leave the mold for about 40 minutes after the silica gel is com...

Embodiment 3

[0048] A process for preparing a cement tea utensil (cement tea cup) based on an inverted mold technology, comprising the following steps:

[0049] 1) Mold frame preparation: select the tea cup prepared to be poured as the template, and its specific size is 40mm (cup mouth diameter) × 30mm (height) × 10mm (cup bottom diameter), and four 10mm long support pins are used to connect the tea tray. Centered and supported in a cardboard mold box with a size of 50mm×50mm×40mm;

[0050] 2) Preparation of mold casting material: select 903 translucent silica gel as the mold casting material, weigh about 105ml of silica gel according to the volume of the mold frame, add a curing agent and mix (ethyl orthosilicate, the additive accounts for 1% of the mass of the silica gel), stir evenly as a mold pouring material;

[0051] 3) Mold preparation: pour the mold casting material into the mold box until it exceeds 10mm from the top of the tea cup, carefully remove the bubbles in the silica gel,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a method for preparing a concrete process tea ware through the reverse mold technology. The method comprises the following steps that (1) a mold frame capable of accommodating a tea ware original model is manufactured according to the tea ware original model such as a tea tray, a saucer, a tea hold, a tea pet and a tea holder; (2) a mold pouring material is blended; (3) the pre-blended mold pouring material is poured till overflows the top end of the mold frame by 1-5 cm, bubbles are removed, mold opening is conducted after the pouring material is hardened, the mold frame is taken out, and a tea ware mold is obtained; (4) a cement-based mixture is prepared, prepared cement concrete is poured into the tea ware mold, vibration is conducted so that all spaces can be sufficiently filled with the concrete, plastering and finishing are conducted, and a top mold body is covered; and (5) a cement tea ware is maintained in the mold, and a finished cement tea ware is obtained. According to the method, the cement concrete is applied to prepare the tea ware for the first time, the prepared cement tea ware is good in fragrance gathering effect, and the plain texture of the cement material is sufficiently achieved.

Description

technical field [0001] The invention belongs to the field of preparation of cement handicrafts, and in particular relates to a preparation process of a cement tea vessel based on a mold-inversion technique. Background technique [0002] Although the texture of cement is rough and has a heavy industrial flavor, the handicrafts made of cement can reflect the chic lightness and magic by virtue of their bare nature. The simple image of cement can be interpreted in the rendering of high-grade gray. Stylish beauty. And this kind of low-key and unassuming minimalist temperament just reflects the aesthetic taste of "the person who is conscientious and frugal" in Lu Yu's "The Book of Tea". In recent years, with the rapid development of concrete technology, especially the development of self-compacting concrete technology, concrete has better fluidity and filling properties, and it is possible to use concrete to prepare exquisite handicrafts. [0003] However, at present, the ingred...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B28B1/08B28B11/24B28B7/34C04B28/00
CPCB28B1/08B28B7/346B28B7/348B28B11/245C04B28/00C04B22/002C04B18/08C04B14/06C04B14/02C04B24/24
Inventor 沈卫国章长应蒋娜张燕玲黄嘉祺王帆何鹏涛周聪聪刘安琪黄海巍陶子豪周振贵陈祖毅
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap