High-temperature-resisting and corrosion-resisting dye stirring device
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A stirring device and high-temperature-resistant technology, which is applied in the field of high-temperature and corrosion-resistant dyestuff stirring devices, can solve the problems of not reflecting the real situation of dissolution and the like
Inactive Publication Date: 2017-04-26
苏州富艾姆工业设备有限公司
View PDF5 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0002] In the production process of printing and dyeing auxiliaries, the main raw material is starch, which needs to be fully dissolved in water. However, in the existing technology, the degree of starch dissolution can only be judged by experience, and the corresponding stirring time can be set, which cannot reflect the reality of dissolution at all. Happening
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0024] This implementation provides a kind of high-temperature-resistant and anti-corrosion dye stirring device, including a cylinder body, a blade and a motor for driving the blade are arranged in the cylinder body, and the mass percentage of the chemical composition of the blade is: C: 0.27%, Si: 0.95%, Mn: 1.95%, P: 0.043%, Ni: 11%, Cr: 16.8%, Nb: 0.18%, Cu: 0.85-0.95%, N: 0.095%, Mo: 2.7%, Al: 0.25%, S: 0.027%, Ti: 0.035%, V: 0.027%, B: 0.003%, lanthanide rare earth: 4%, the balance is Fe;
[0025] The mass percentages of lanthanide rare earth components are: lanthanum: 20%, cerium: 25%, samarium: 15%, neodymium: 15%, gadolinium: 2%, praseodymium: 18%, dysprosium: 5%, and other lanthanide elements: 1-3%, the sum of the above components is 100;
[0026] The specific preparation process is:
[0027] Billet blanking: After the billet is heated to 700°C in the electric furnace, it is controlled to be heated rapidly to the initial forging temperature within 3 minutes, and the...
Embodiment 2
[0035] This implementation provides a kind of high-temperature-resistant and anti-corrosion dye stirring device, including a cylinder body, a blade and a motor for driving the blade are arranged in the cylinder body, and the mass percentage of the chemical composition of the blade is: C: 0.25%, Si: 1.15%, Mn: 2.7%, P: 0.045%, Ni: 12%, Cr: 17.2%, Nb: 0.18%, Cu: 0.90%, N: 0.10%, Mo: 2.65%, Al: 0.27%, S: 0.031%, Ti: 0.038%, V: 0.024%, B: 0.003%, lanthanide rare earth: 4%, the balance is Fe;
[0038] Billet blanking: After the billet is heated to 700°C in the electric furnace, it is controlled to be heated rapidly to the initial forging temperature within 3 minutes, and the initial ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses a high-temperature-resisting and corrosion-resisting dye stirring device which comprises a cylinder, and a blade and a motor driving the blade are arranged in the cylinder. The blade comprises chemical components including, by mass percent, 0.25%-0.35% of C, 0.85%-1.25% of Si, 1.85%-2.95% of Mn, 0.04%-0.05% of P, 11%-13% of Ni, 16.5%-17.5% of Cr, 0.15%-0.20% of Nb, 0.85%-0.95% of Cu, 0.08%-0.11% of N, 2.15%-2.95% of Mo, 0.2%-0.3% of Al, 0.025%-0.035% of S, 0.03%-0.04% of Ti, 0.02%-0.03% of V, 0.002%-0.004% of B, 3%-5% of lanthanide series rare earth and the balance Fe. The lanthanide series rare earth includes, by mass percent, 20%-24% of lanthanum, 20%-25% of cerium, 14%-16% of samarium, 14%-16% of neodymium, 2%-4% of gadolinium, 16%-18% of praseodymium, 5%-6% of dysprosium and 1%-3% of other lanthanide series elements, and the sum of the above components is 100%.
Description
technical field [0001] The invention belongs to the technical field of textile equipment, in particular to a high-temperature-resistant and anti-corrosion dye stirring device. Background technique [0002] In the production process of printing and dyeing auxiliaries, the main raw material is starch, which needs to be fully dissolved in water. However, in the existing technology, the degree of starchdissolution can only be judged by experience, and the corresponding stirring time can be set, which cannot reflect the reality of dissolution at all. Condition. Contents of the invention [0003] The invention provides a high-temperature-resistant and anti-corrosion dye stirring device to solve the technical problems existing in the known technology. [0004] The technical solution adopted by the present invention to solve the technical problems existing in the known technology is: a high-temperature-resistant and anti-corrosion dyestuff mixing device, including a cylinder bod...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More