Semi-worsted blended antibacterial, skin-care, skin-moistening, health-care, cool and refreshing wrapped yarn and preparation method thereof

A semi-worsted and yarn technology, which is applied in the field of semi-worsted blended antibacterial skin care, moisturizing health care and cool wrapping yarn and preparation, can solve the problem of fine denier polyester fiber mass specific resistance, web formation, yarn hairiness There are many problems such as no health care function, etc., to achieve the effects of good hygroscopicity, good antibacterial properties, and good adsorption performance.

Inactive Publication Date: 2017-04-26
ZHONGYUAN ENGINEERING COLLEGE
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the mass specific resistance of fine-denier polyester fiber is large, and the electrostatic phenomenon is prominent, which makes it difficult to form a net and yarn hairiness during the spinning process of pure fine-denier polyester fiber. Fabrics made of pure fine-denier polyester fiber Poor hygroscopicity, not soft, poor comfort, not suitable for making clothing, underwear, casual clothes, fitness clothes, home textile products, etc.
[0006] Cashmere fiber is fine in fineness, good in elasticity, delicate and smooth to the touch, soft and warm, good in bulk, good in hygroscopicity, good in comfort, but has no health care function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Taking the 40-count blended yarn as an example, the blending weight percentage of natural mint fiber, fine denier polyester fiber and cashmere fiber is 20:45:35.

[0034] Preparation according to raw materials and wool oiling, sliver making, drawing frame, roving and spinning:

[0035] (1) Oiling process of raw materials and crude oil: make oil agent from 0.8% of the total weight of raw materials and crude oil, 1.5% of antistatic agent from the total weight of raw materials, and 6% of the total weight of raw materials. On the raw material, the reconciled raw material is stuffed for 24 hours;

[0036] (2) Carding and sliver making process: Feed the stuffed raw materials into the carding machine, the sliver weight is 17.4g / 5m, the sliver speed is 45.0m / min, the feeding amount is 40.0g / time, and the licker-in speed is reduced to 620r / min, cylinder speed 328r / min, cover plate speed 72mm / min, doffer speed 20.5r / min, cylinder-doffer interval is 0.15mm, cylinder-cover interv...

Embodiment 2

[0045] Taking the 38-count blended yarn as an example, the blending weight percentage of natural mint fiber, fine denier polyester fiber and cashmere fiber is 55:15:30.

[0046] Preparation according to raw materials and wool oiling, sliver making, drawing frame, roving and spinning:

[0047] (1) Raw material and crude oil oiling process: make oil agent by making crude oil accounting for 0.8% of the total weight of raw materials, antistatic agent accounting for 1.7% of the total weight of raw materials, and water accounting for 10% of the total weight of raw materials, spraying evenly on the mixture On the raw material, the reconciled raw material is stuffed for 24 hours;

[0048] (2) Carding and sliver making process: feed the stuffed raw materials into the carding machine, the weight of the sliver is 17.4g / 5m, the speed of the sliver is 48m / min, the feeding amount is 45g / time, and the speed of the licker-in roller is reduced to 680r / min , the cylinder speed is 350r / min, the...

Embodiment 3

[0057] Taking the 36-count blended yarn as an example, the blending weight percentage of natural mint fiber, fine denier polyester fiber and cashmere fiber is 35:50:15.

[0058] Preparation according to raw material and wool oiling, sliver making, drawing frame, roving and spinning:

[0059] (1) Oiling process of raw materials and crude oil: make oil agent from crude oil accounting for 0.8% of the total weight of raw materials, antistatic agent accounting for 1.9% of the total weight of raw materials, and water accounting for 13% of the total weight of raw materials, and spray evenly on the mixture On the raw material, the reconciled raw material is stuffed for 24 hours;

[0060] (2) Carding and sliver making process: Feed the stuffed raw materials into the carding machine, the sliver weight is 17.4g / 5m, the sliver speed is 49.0m / min, the feeding amount is 47.0g / time, and the licker-in speed is reduced to 735r / min, cylinder speed 369r / min, cover plate speed 84mm / min, doffer ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical resistanceaaaaaaaaaa
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to yarns, and especially relates to a preparation method and applications of semi-worsted antibacterial, skin-care, skin-moistening, health-care, cool and refreshing wrapped yarns formed by blending of tourmaline fiber long filaments, natural mint fibers, fine denier polyester fibers and cashmere fibers. The yarns are prepared by the following raw materials by weight proportion: 20-55% of natural mint fibers, 15-50% of fine denier polyester fibers, and 15-35% of cashmere fibers. Performance indexes of the blended yarns are that the single thread breaking tenacity is 14.8-23.2 cN / tex, the single thread breaking tenacity coefficient of variation Cv is 7.9-17.0%, and the yarn evenness coefficient of variation Cv is 16.2-20.6%. Fabrics prepared by the blended yarns have cool, refreshing, comfortable, antibacterial, deodorizing, itch-relieving, skin-care, body-shaping, skin-moistening, smell-removing functions and other health-care functions.

Description

technical field [0001] The invention belongs to the field of yarns containing nanometer natural mint stock solution, in particular to a semi-worsted blended antibacterial skin care, moisturizing and health care wrapping yarn of strange ice stone fiber filament, natural mint fiber, fine denier polyester fiber and cashmere fiber And its preparation method and application. Background technique [0002] Natural mint fiber is a new type of plant antibacterial fiber. It adopts high-tech extraction technology to extract limited components such as menthol from high-quality mint. Various specifications of aloe viscose fiber, without adding any chemical substances, have permanent antibacterial and health care effects, suitable for blending with various fibers to meet the needs of various green textiles. The fiber not only concentrates many excellent properties of cellulose fiber such as moisture absorption, breathability, comfort, and easy dyeing, but also fully possesses many functi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/36D02G3/04D02G3/44
CPCD02G3/36D02G3/04D02G3/44D02G3/449D10B2101/02D10B2201/01D10B2211/02D10B2331/04D10B2501/00D10B2501/02