Rapid repair polymer mortar

A technology of polymer and mortar, which is applied in the field of building materials, can solve the problems that the repair effect cannot meet the engineering design repair requirements, repair failure and other problems, and achieve the effect of easy on-site maintenance, improved workability, and reduced drying shrinkage

Inactive Publication Date: 2017-05-31
河池永固混凝土有限责任公司
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The invention provides a quick-repair polymer mortar, thereby solving the problem that the actual repair effect of the existing quick-repair polymer mortar is far from meeting the repair requirements of engineering design, which leads to repair failure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rapid repair polymer mortar

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Example 1 - Quick Repair Polymer Mortar

[0029] It is made from the following raw materials:

[0030] 70kg of sand, 12kg of cement, 5kg of fly ash with 0.045mm sieve residue less than 25%, 5kg of mineral powder with specific surface area ≥ 400㎡ / kg, 28-day activity index ≥ 98%, latex powder 2kg, cellulose ether 0.1kg , 0.5kg of epoxy resin with a molecular weight of 200, 0.5kg of epoxy resin with a molecular weight of 400, 1kg of rosin glyceride and 2kg of polyurethane thickener;

[0031] Wherein, the sand refers to the sand with the following particle gradation structure:

[0032] 9.5mm sieve hole: 0%;

[0033] 4.75mm sieve hole: 10%;

[0034] 2.36mm sieve hole: 5%;

[0035] 1.18mm sieve hole: 30%;

[0036] 600μm sieve residue: 41%;

[0037] 300μm sieve: 80%;

[0038] 150μm sieve residue: 100%.

Embodiment 2

[0039] Example 2 - Quick Repair Polymer Mortar

[0040] It is made from the following raw materials:

[0041] 75kg of sand, 14kg of cement, 8kg of fly ash with 0.045mm sieve residue less than 25%, 8kg of mineral powder with specific surface area ≥ 400㎡ / kg, 28-day activity index ≥ 98%, latex powder 3kg, cellulose ether 1kg, 0.6kg of epoxy resin with a molecular weight of 250, 1kg of epoxy resin with a molecular weight of 450, 3kg of rosin glyceride and 4kg of polyurethane thickener;

[0042] Wherein, the sand refers to the sand with the following particle gradation structure:

[0043] 9.5mm sieve hole: 0%;

[0044] 4.75mm sieve hole: 5%;

[0045] 2.36mm sieve hole: 10%;

[0046] 1.18mm sieve hole: 10%;

[0047] 600μm sieve residue: 55%;

[0048] 300μm sieve residue: 71%;

[0049] 150μm sieve residue: 95%.

Embodiment 3

[0050] Example 3 - Quick Repair Polymer Mortar

[0051] It is made from the following raw materials:

[0052] 80kg of sand, 15kg of cement, 5kg to 8kg of fly ash with a sieve residue of 0.045mm less than 25%, 6kg of mineral powder with a specific surface area of ​​≥400㎡ / kg and a 28-day activity index of ≥98%, 5kg of latex powder, and cellulose ether 0.7kg, 0.7kg of epoxy resin with a molecular weight of 230, 0.8kg of epoxy resin with a molecular weight of 420, 5kg of rosin glyceride and 3kg of polyurethane thickener;

[0053] Wherein, the sand refers to the sand with the following particle gradation structure:

[0054] 9.5mm sieve hole: 0%;

[0055] 4.75mm sieve hole: 0%;

[0056] 2.36mm sieve hole: 25%;

[0057] 1.18mm sieve hole: 50%;

[0058] 600μm sieve residue: 70%;

[0059] 300μm sieve residue: 92%;

[0060] 150μm sieve residue: 82%.

[0061] The preparation method of the rapid repair polymer mortar described in the above-mentioned embodiments is as follows: take...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
activation indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses rapid repair polymer mortar which is prepared from the following raw materials in parts by weight: 70-80 parts of sand, 12-15 parts of cement, 5-8 parts of coal ash, 5-8 parts of mineral powder, 2-5 parts of emulsion powder, 0.1-1 part of cellulose ether, 0.5-1 part of low molecular weight epoxy resin, 0.5-1 part of medium molecular weight epoxy resin, 1-5 parts of glycerol ester of rosin and 2-4 parts of a polyurethane thickener. Besides excellent performances of water-retention rate, shrinking percentage, compressive strength, layering degree and the like, the rapid repair polymer mortar disclosed by the invention also has a performance of rapid agglomeration, so that when the rapid repair polymer mortar is used for engineering repair, the rapid repair polymer mortar not only effectively avoids phenomena such as cracks and hollow protuberances at the repaired parts, but also can be effectively and widely applied to pavement pulverization and suncrack repair of high and cold and high-temperature regions with large temperature difference and complicated climate.

Description

technical field [0001] The invention relates to the field of building materials, in particular to a polymer mortar. Background technique [0002] At present, the polymer mortar products on the market generally have the defect of long gel time. Therefore, when it is applied to pavement flourization and dry crack repair in areas with large temperature difference and complex weather such as high cold and high temperature, it is often due to polymer Mortar gel time is long and lead to repair failure. For this reason, the need for a polymer with short gel time and rapid repair is an urgent problem for those skilled in the art. Contents of the invention [0003] The invention provides a quick-repair polymer mortar, thereby solving the problem that the actual repair effect of the existing quick-repair polymer mortar is far from meeting the repair requirements of engineering design, thus resulting in repair failure. [0004] In order to solve the problems of the technologies des...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00
CPCC04B28/00C04B2201/10C04B2201/50C04B14/06C04B18/08C04B14/02C04B24/24C04B24/383C04B24/281C04B24/34C04B24/282
Inventor 韦正刚寇丹生梁冠忠潘战雄杨宝翠王冠球覃宝能覃岳猛韦标
Owner 河池永固混凝土有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com