Road coating capable of adsorbing tail gas as well as preparation method and application thereof

A road and coating technology, which is applied in the field of road coating for absorbing exhaust gas and its preparation, can solve the problems of road surface skid resistance, water stability damage, slow down the service life of asphalt pavement, affect the performance of asphalt pavement, etc., and achieve high Mechanochemical stability, high utilization potential, non-toxic and harmless raw materials

Inactive Publication Date: 2017-05-31
ZHENGZHOU CHENGHE INFORMATION TECH CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For the purification of automobile exhaust, in the field of roads, the technology of coating a layer of air-purifying materials on the surface of asphalt concrete roads is currently the main technology. The coating is mainly added to the carrier with TiO 2 Although the main exhaust gas decomposition catalyst can achieve certain effects, there are still many problems: the quantum yield of the catalyst itself is low, the rate of photocatalytic degradation is slow, and many harmful intermediate products will be produced, and the purification effect is not obvious ; Poor use durability, affecting the performance of asphalt pavement, slowing down the service life of asphalt pavement; affecting the road performance of the pavement, easy to damage the performance of the road surface such as skid resistance and water stability; increasing the construction cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Road coating capable of adsorbing tail gas as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] In the embodiment of the present invention, a road coating for absorbing exhaust gas is composed of the following raw materials in parts by weight: 42 parts of seaweed mud, 17 parts of vermiculite, 5 parts of cocamidopropyl betaine, 11 parts of triethanolamine, lemon acid 3 parts.

[0019] Triethanolamine is mixed with deionized water whose mass is 5.5 times to prepare triethanolamine solution; cocamidopropyl betaine is mixed with deionized water whose mass is 3.2 times to prepare cocamidopropyl betaine solution. Mix and grind seaweed mud and citric acid, pass through a 150-mesh sieve, mix with triethanolamine solution, put it into a polytetrafluoroethylene reactor, heat and stir at 126°C for 82 minutes, then lower it to 75°C to prepare mixture A . The vermiculite was pulverized and passed through a 150-mesh sieve, then mixed with cocamidopropyl betaine solution, and stirred at 92°C for 52 minutes to obtain mixture B. Mix mixture A and mixture B, stir at 75°C for 45 m...

Embodiment 2

[0021] In the embodiment of the present invention, a road coating for absorbing exhaust gas is composed of the following raw materials in parts by weight: 50 parts of seaweed mud, 25 parts of vermiculite, 13 parts of cocamidopropyl betaine, 19 parts of triethanolamine, lemon Sour 7 parts.

[0022] Triethanolamine is mixed with deionized water whose mass is 5.5 times to prepare triethanolamine solution; cocamidopropyl betaine is mixed with deionized water whose mass is 3.2 times to prepare cocamidopropyl betaine solution. Mix and grind seaweed mud and citric acid, pass through a 150-mesh sieve, mix with triethanolamine solution, put it into a polytetrafluoroethylene reactor, heat and stir it at 126°C for 85 minutes, then lower it to 75°C to prepare mixture A . The vermiculite was pulverized and passed through a 150-mesh sieve, then mixed with cocamidopropyl betaine solution, and stirred at 92°C for 52 minutes to obtain mixture B. Mix mixture A and mixture B, stir at 75°C for ...

Embodiment 3

[0024] In the embodiment of the present invention, a road coating for absorbing exhaust gas is composed of the following raw materials in parts by weight: 44 parts of seaweed mud, 19 parts of vermiculite, 7 parts of cocamidopropyl betaine, 13 parts of triethanolamine, lemon acid 4 parts.

[0025] Triethanolamine is mixed with deionized water whose mass is 5.5 times to prepare triethanolamine solution; cocamidopropyl betaine is mixed with deionized water whose mass is 3.2 times to prepare cocamidopropyl betaine solution. Mix and grind seaweed mud and citric acid, pass through a 150-mesh sieve, mix with triethanolamine solution, put it into a polytetrafluoroethylene reactor, heat and stir at 126°C for 83 minutes, then lower it to 75°C to prepare mixture A . The vermiculite was pulverized and passed through a 150-mesh sieve, then mixed with cocamidopropyl betaine solution, and stirred at 92°C for 52 minutes to obtain mixture B. Mix mixture A and mixture B, stir at 75°C for 45 m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a road coating capable of adsorbing tail gas as well as a preparation method and an application thereof. The road coating material is prepared from raw materials in parts by weight as follows: 42-50 parts of seaweed clay, 17-25 parts of vermiculite, 5-13 parts of cocamidopropyl betaine, 11-19 parts of triethanolamine and 3-7 parts of citric acid. The road coating material takes the seaweed clay and the vermiculite as main raw materials, after treatment with other substances, excellent characteristics of all raw materials are reasonably utilized, and the road coating can purify NOX, HC compounds, CO and other harmful gas in the air, has a certain effect on absorbing greenhouse gas, namely, CO2 and significantly improves the road environment. The road coating is pollution-free and high in mechanical and chemical stability and durability. The road coating is simple and convenient to construct and has excellent pavement performance, the construction process is simple, raw materials are non-toxic and harmless, and the road coating has great social benefit in improving road use quality and protecting the environment.

Description

technical field [0001] The invention relates to the technical field of road materials, in particular to a road coating for absorbing tail gas, a preparation method and application thereof. Background technique [0002] With the rapid increase of the number of automobiles, the environmental pollution caused by automobile exhaust is becoming more and more serious, and the environment around the road is constantly deteriorating. The main harmful components of automobile exhaust are NO X , HC compounds, CO, particulate matter, etc. More than 40% NO in air pollutants X , More than 80% of CO and more than 70% of HC compounds are caused by automobile exhaust. Therefore, controlling the environmental pollution caused by automobile exhaust is of great significance to improving the quality of road use and protecting the environment. For the purification of automobile exhaust, in the field of roads, the technology of coating a layer of air-purifying materials on the surface of aspha...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B30/00B01J20/22B01J20/30B01D53/02
CPCB01D2257/40B01D2257/502B01D2257/702B01J20/10B01J20/22B01J20/24C04B30/00C04B14/04C04B14/202C04B24/123C04B24/122C04B24/06C04B2111/00482C04B2111/0075Y02C20/40
Inventor 不公告发明人
Owner ZHENGZHOU CHENGHE INFORMATION TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com