Improved conductive master batch production technology

A conductive masterbatch and production process technology, applied in the field of conductive masterbatch production technology, can solve the problems of conductive masterbatch injection fluidity, surface appearance quality, toughness, bending strength and other physical properties decline, and achieve good electrical conductivity, good Injection fluidity, effect of high carbon black content

Inactive Publication Date: 2017-05-31
东莞市淦宏信息科技有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Conductive masterbatch contains carbon black, the content of carbon black determines the electrical conductivity, the more carbon black content, the better the electrical conductivity, but, subsequently, the injection fluidity, surface appearance quality, toughness, bending Physical properties such as strength will be greatly reduced, so it is necessary to improve

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of production technology of improved conductive masterbatch, comprises the following steps,

[0031] Prepare the main material molten material, by weight, 100 parts of polypropylene, 30-50 parts of polyethylene, 10-20 parts of nano-sized iron oxide, 10-20 parts of nano-sized zirconia, 0.1-0.3 parts of cocamide , 0.1 to 0.3 parts of polymer flow agent and 0.1 to 0.3 parts of antioxidant are mixed uniformly and put into the first screw extruder, and the main material molten material is delivered through the die head of the first screw extruder, wherein,

[0032] Add a strong magnetic field to the material smelting reaction zone and melt conveying zone of the first screw extruder, the strength of the strong magnetic field is 5000-6000 A / m, to magnetize the molten material in the heating barrel of the first screw extruder,

[0033] The temperature of the material smelting reaction zone of the first screw extruder is controlled at 250-260° C., and the extrusion pressu...

Embodiment 2

[0042] A kind of production technology of improved conductive masterbatch, comprises the following steps,

[0043] Prepare the main material molten material, by weight, 100 parts of polypropylene, 31-35 parts of polyethylene, 11-14 parts of nano-scale iron oxide, 12-14 parts of nano-scale zirconia, 0.1-0.3 parts of cocamide , 0.1 to 0.3 parts of polymer flow agent and 0.1 to 0.3 parts of antioxidant are mixed uniformly and put into the first screw extruder, and the main material molten material is delivered through the die head of the first screw extruder, wherein,

[0044] Add a strong magnetic field to the material smelting reaction zone and melt conveying zone of the first screw extruder, the strength of the strong magnetic field is 5000-6000 A / m, to magnetize the molten material in the heating barrel of the first screw extruder,

[0045] The temperature of the material smelting reaction zone of the first screw extruder is controlled at 250-260° C., and the extrusion pressu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an improved conductive master batch production technology. The technology comprises the following steps: preparing a main material melt, preparing a carbon black melt, and granulating master batch. The technology concretely comprises: adding 100 parts by weight of main material particles, 10-20 parts of polyformaldehyde, 5-10 parts of diatomaceous earth, 1-5 parts of disodium ethylenediamine tetraacetate, 0.1-0.5 parts of silver nano-powder, 5-10 parts of nanometer zirconium oxide, 10-20 parts of crosslinked carboxymethyl cellulose, 1-5 parts of cocamide, 0.1-0.3 parts of a polymeric flowable agent and 0.1-0.3 parts of an antioxidant, uniformly mixing above materials, adding the obtained mixture to a double screw granulator, adding the carbon black melt and the main material melt to the material melting reaction zone of the double screw granulator, and carrying out extrusion granulation through the double screw granulator. Conductive master batch in the invention has the advantages of high carbon black content, good electrical conductivity, good injection fluidity, good surface appearance quality, good toughness and good bending strength.

Description

technical field [0001] The invention relates to the technical field of conductive master batches, in particular to an improved production process of conductive master batches. Background technique [0002] Conductive masterbatch contains carbon black, the content of carbon black determines the electrical conductivity, the more carbon black content, the better the electrical conductivity, but, subsequently, the injection fluidity, surface appearance quality, toughness, bending Physical properties such as strength will be greatly reduced, so it is necessary to improve. Contents of the invention [0003] Aiming at the deficiencies in the prior art, the purpose of the present invention is to provide an improved production process of conductive masterbatch, which has high carbon black content, good electrical conductivity, good injection fluidity, surface appearance quality, Physical properties such as toughness and flexural strength. [0004] In order to achieve the above ob...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/06C08L45/00C08L59/00C08L1/28C08K13/02C08K3/22C08K5/20C08K3/04C08K5/3445C08K3/34C08K3/08B29B9/06
CPCC08L23/12B29B9/06C08K2201/001C08K2201/011C08K2201/014C08L2205/025C08L2205/035C08L23/06C08L45/00C08L59/00C08L1/286C08K13/02C08K2003/2272C08K2003/2244C08K5/20C08K3/04C08K5/3445C08K3/346C08K2003/0806
Inventor 简顺年
Owner 东莞市淦宏信息科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap