Cement-based water permeable brick with wear resistance enhanced by EVA resin and steel slag micropowder

A steel slag micro-powder, cement-based technology, applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problems of affecting water permeability, unfavorable brick strength development, slurry sinking, etc., to achieve pore enlargement, Inhibits the occurrence and development of cracks, and has good hydrophilicity

Inactive Publication Date: 2017-06-09
闻承岳
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the article "Research on Optimizing the Production of Permeable Bricks Using Waste Concrete", waste concrete was used to replace natural aggregates, and the orthogonal design test method was used to analyze aggregate particle size, bone-to-cement ratio, water-cement ratio, and water reducing agent, silica fume and waste concrete. The influence of different dosages on the strength and water permeability coefficient of permeable bricks was obtained, and the optimal mix ratio was obtained. The strength of permeable bricks made with the strengthening of recycled aggregates and the improvement of curing methods was improved, which met the laying requirements and realized the waste Utilization, energy saving and emission reduction, but due to the limited increase in strength and the fluidity of concrete, slurry sinking is prone to occur when the brick body is formed, blocking the seepage channel affects water permeability, and the cement layer is due to slurry, the joints at the joints The cement layer will become thinner, which is not conducive to the development of brick strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A cement-based water-permeable brick reinforced with EVA resin and steel slag powder for abrasion resistance. It is made of the following parts by weight (kg) of raw materials: granite corner waste 40, waste concrete 30, 42.5 grade ordinary Portland cement 20, polyester cotton fabric Leftover material 2, polyepichlorohydrin dimethylamine 0.1, early-strength polycarboxylic acid water reducer 0.3, appropriate amount of water, EVA resin emulsion 3, steel slag powder 6, micro silicon powder 3, silica sol 2.

[0015] The cement-based water-permeable brick reinforced with EVA resin and steel slag powder for abrasion resistance is made by the following specific steps:

[0016] (1) Put the granite corner waste into the crusher and crush into 7mm small particles, put the waste concrete into the crusher and crush into 5mm particles, and then mix the two kinds of particles to obtain mixed coarse aggregate;

[0017] (2) Cut and tear off the polyester-cotton fabric scraps to form 3mm×3mm f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a cement-based water permeable brick with wear resistance enhanced by EVA resin and steel slag micropowder. The cement-based water permeable brick is prepared form the following raw materials in parts by weight: 40-43 parts of granite scrap, 30-32 parts of waste concrete, 20-22 parts of 42.5-level ordinary Portland cement, 2-2.5 parts of polyester-cotton fabric scrap, 0.1-0.12 part of polyepichlorohydrin dimethylamine, 0.3-0.4 part of early strength polycarboxylate water reducer, an appropriate amount of water, 3-4 parts of EVA resin emulsion, 6-7 parts of steel slag micropowder, 3-4 parts of silica fume and 2-3 parts of silica sol. The cement-based water permeable brick disclosed by the invention has excellent water permeability; with a large number of ventilation pores in the brick body, the surface water can quickly permeate to underground, and the adjustment of surface humidity is promoted; the cement-based water permeable brick is firm and wear-resistant and has high compressive strength and is suitable for park roads, stadiums and the like; and moreover, the raw materials are conveniently available, and the technology facilitates batch production.

Description

Technical field [0001] The invention relates to the technical field of water-permeable bricks, in particular to a cement-based water-permeable brick enhanced by EVA resin and steel slag powder for abrasion resistance. Background technique [0002] In recent years, during the rainy season, the phenomenon of "watching the sea" frequently occurs in major cities. Permeable ground has attracted more and more researchers' attention due to its advantages such as alleviating the pressure of urban drainage system, replenishing groundwater resources, improving the living conditions of urban surface plants and soil microorganisms, making underground water easy to evaporate and eliminating the urban heat island effect. Water-permeable pavement helps to circulate air and moisture, eliminate the heat island effect, absorb sound and reduce noise. Water-permeable pavement bricks are the main components of urban water-permeable pavements. There are mainly three types of cement-based permeable co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B18/20C04B20/10C04B111/34
CPCC04B18/20C04B20/1037C04B28/04C04B2111/00284C04B2111/343C04B2201/50C04B18/12C04B18/16C04B24/288C04B24/24C04B22/002C04B24/2611C04B18/142C04B18/146C04B24/42Y02W30/91
Inventor 闻承岳
Owner 闻承岳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products