Pavement water permeable brick with compound packing reinforced antibacterial performance

Abstract

The invention discloses a pavement water permeable brick with compound packing reinforced antibacterial performance. The water permeable brick is prepared from the following raw materials in parts by weight: 40-43 parts of granite scrap, 32-32 parts of waste concrete, 20-22 parts of 42.5# conventional silicate cement, 2-2.5 parts of polyester-cotton fabric scraps, 0.1-0.12 part of dimethylamine-epichlorohydrin polymer, 0.3-0.4 part of early-strength polycarboxylate superplasticizer, 0.7-0.9 part of sodium polyacrylate, 4-5 parts of nano-zinc oxide, 2-3 parts of bromopropyl triphenylphosphonium bromide, 0.3-0.4 part of ammonia water having a concentration of 25 weight percent, 0.3-0.4 part of methane sulfonic acid and a proper amount of deionized water. The water permeable brick has excellent tensile strength, abrasion resistance and good antibacterial anticorrosive effect, is clean, does not have foreign odor, has a long service life, and can keep a tidy pavement environment for a long time.

Description

technical field [0001] The invention relates to the technical field of permeable bricks, in particular to a pavement permeable brick with compound filler to enhance antibacterial performance. Background technique [0002] In recent years, during the rainy season, the phenomenon of "watching the sea" has occurred frequently in major cities. Permeable ground has attracted more and more attention from researchers because of its advantages of alleviating the flood discharge pressure of urban drainage systems, replenishing groundwater resources, improving the living conditions of urban surface plants and soil microorganisms, making groundwater easy to evaporate and eliminating the urban heat island effect. Permeable pavement facilitates air and moisture circulation, eliminates the heat island effect, and absorbs and reduces noise. Permeable pavement bricks are the main components of urban permeable pavement, mainly including cement-based permeable concrete bricks, polymer permea...

AI Technical Summary

Problems solved by technology

[0003] In the article "Research on Optimizing the Production of Permeable Bricks Using Waste Concrete", waste concrete was used to replace natural aggregates, and the orthogonal design test method was used to analyze aggregate particle size, bone-to-cement ratio, water-cement ratio, and water reducing agent, silica fume and waste concrete. The influence of different dosages on the strength and water permeability coefficient of permeable bricks was obtained, and the optimal mix ratio was obtained. The strength of permeable bricks made with the strengthening of recycled aggregates and the improvement of curing methods was improved, which met the laying requirements and realized the waste Utilization, energy saving and emission reduction, but due to the limited increase in strength and the fluidity of concrete, slurry sinking is prone to occur when the brick body is formed, blocking the seepage channel affects water permeability, and the cement layer is due to slurry, the joints at the joints The cement layer will become thinner, which is not conducive to the development of brick strength