A deoxygenation type drying agent and a preparing method thereof
The technology of a desiccant and diatomite is applied in the field of deoxygenation desiccant and its preparation, which can solve the problems of poor drying effect and heavy taste, and achieve the effects of simple preparation method, prolonged storage time and good deoxidation effect.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0015] The desiccant components include 20 parts of diatomite, 10 parts of iron powder, 10 parts of carboxymethyl cellulose, 5 parts of bentonite, 3 parts of rosin, 2 parts of linseed oil, 10 parts of zeolite powder, and 8 parts of chitosan in parts by weight. 10 parts, 10 parts of bamboo charcoal powder, 2 parts of hollow microspheres and 1 part of glass fiber.
[0016] The preparation method of the present embodiment comprises the following steps:
[0017] A. Mix diatomaceous earth, iron powder, bentonite, zeolite powder, bamboo charcoal powder, and hollow microbeads and add them to a grinder for grinding for 40 minutes to obtain mixture A;
[0018] B. Add rosin and linseed oil to the mixture A, mix it and add it to the stirring tank to stir at a low speed, the stirring speed is 300 rpm, and the stirring time is 30min to obtain the mixture B;
[0019] C. Add carboxymethyl cellulose, zeolite powder, chitosan, bamboo charcoal powder and glass fiber to the mixture B, stir thor...
Embodiment 2
[0021] The desiccant components include 40 parts by weight of diatomite, 20 parts of iron powder, 20 parts of carboxymethyl cellulose, 10 parts of bentonite, 8 parts of rosin, 8 parts of linseed oil, 20 parts of zeolite powder, and 17 parts of chitosan 30 parts, 30 parts of bamboo charcoal powder, 8 parts of hollow microspheres and 5 parts of glass fibers.
[0022] The preparation method of the present embodiment comprises the following steps:
[0023] A. Mix diatomaceous earth, iron powder, bentonite, zeolite powder, bamboo charcoal powder, and hollow microbeads and add them to a grinder for grinding for 40 minutes to obtain mixture A;
[0024] B. Add rosin and linseed oil to the mixture A, mix it and add it to the stirring tank to stir at a low speed, the stirring speed is 300 rpm, and the stirring time is 30min to obtain the mixture B;
[0025] C. Add carboxymethyl cellulose, zeolite powder, chitosan, bamboo charcoal powder and glass fiber to the mixture B, stir thoroughly...
Embodiment 3
[0027] The desiccant components include 25 parts by weight of diatomite, 12 parts of iron powder, 12 parts of carboxymethyl cellulose, 7 parts of bentonite, 4 parts of rosin, 3 parts of linseed oil, 12 parts of zeolite powder, and 9 parts of chitosan 15 parts, 15 parts of bamboo charcoal powder, 3 parts of hollow microspheres and 2 parts of glass fiber.
[0028] The preparation method of the present embodiment comprises the following steps:
[0029] A. Mix diatomaceous earth, iron powder, bentonite, zeolite powder, bamboo charcoal powder, and hollow microbeads and add them to a grinder for grinding for 40 minutes to obtain mixture A;
[0030] B. Add rosin and linseed oil to the mixture A, mix it and add it to the stirring tank to stir at a low speed, the stirring speed is 300 rpm, and the stirring time is 30min to obtain the mixture B;
[0031] C. Add carboxymethyl cellulose, zeolite powder, chitosan, bamboo charcoal powder and glass fiber to the mixture B, stir thoroughly af...
PUM
Login to View More Abstract