Slate soft tile and production method thereof

A process method and ceramic tile technology, applied in the field of slate soft ceramic tile and its process, can solve the problems of potential safety hazards, falling off, etc., and achieve the effect of simple and convenient manufacturing process and easy popularization and use

Inactive Publication Date: 2017-09-08
广东福莱特建筑材料有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the tiles attached to the wall may fall off after a long time, especially on the high-rise build

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] For slate soft tiles, the following components are proposed according to the following weight fractions:

[0037] Water -------------------------- 10 parts;

[0038] Cellulose---------------------0.3 parts;

[0039] Industrial emulsion -------------------- 7 parts;

[0040] Mineral powder --------------------- 27.7 parts;

[0041] Quartz sand --------------------- 55 parts.

[0042] The processing method is as follows: mix the above components together, and then add an appropriate amount of coloring material as required, and the content of the coloring material in this component is negligible, and then use a mixer to stir evenly to obtain a slurry.

[0043] Then use a slurry pump to spray a layer of slurry on the mold, then spread a glass fiber net on the surface of the slurry, and then use a slurry pump to sprinkle another layer of slurry on the glass fiber net to make the slurry bury the glass fiber net. The mold in this case includes a mold cavity, some patterns ...

Embodiment 2

[0045] Soft slate tiles, including the following components in the following weight fractions:

[0046] Water -------------------------- 14 parts;

[0047] Cellulose ---------------------0.7 parts;

[0048] Industrial emulsion ----------------- 9 parts;

[0049] Mineral powder --------------------- 31.3 parts;

[0050] Quartz sand --------------------- 45 parts.

[0051] The processing method is as follows: mix the above components together, and then add an appropriate amount of coloring material as required, and the content of the coloring material in this component is negligible, and then use a mixer to stir evenly to obtain a slurry.

[0052] Then use a slurry pump to spray a layer of slurry on the mold, then spread a glass fiber net on the surface of the slurry, and then use a slurry pump to sprinkle another layer of slurry on the glass fiber net to make the slurry bury the glass fiber net. The mold in this case includes a mold cavity, some patterns can be designed on ...

Embodiment 3

[0054] Soft slate tiles, including the following components in the following weight fractions:

[0055] Water -------------------------- 12 parts;

[0056] Cellulose ---------------------0.5 parts;

[0057] Industrial emulsion ----------------- 8 parts;

[0058] Mineral powder --------------------- 30 copies;

[0059] Quartz sand --------------------- 49.5 parts.

[0060] The processing method is as follows: mix the above components together, and then add an appropriate amount of coloring material as required. The content of the coloring material in this component is negligible, and then use a mixer to stir evenly to obtain a slurry.

[0061] Then use a slurry pump to spray a layer of slurry on the mold, then spread a glass fiber net on the surface of the slurry, and then use a slurry pump to sprinkle another layer of slurry on the glass fiber net to make the slurry bury the glass fiber net. The mold in this case includes a mold cavity, some patterns can be designed on the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a slate soft tile. The slate soft tile contains the following components in percentage by weight: 10%-14% of water, 0.3%-0.7% of cellulose, 7%-9% of an industrial emulsion, 27.7%-31.3% of mineral powder and 45%-55% of quartz sand. The invention further provides a process method of the slate soft tile. The process method comprises the following steps: mixing: mixing the raw materials together to obtain a mixture, adding a proper amount of coloring matters into the mixture, and uniformly stirring by virtue of a stirring machine, so as to form a slurry; mold filling: spraying a layer of slurry to the mold by virtue of a slurry pump, paving a glass fiber net on the surface of the slurry, spraying another layer of slurry to the glass fiber net by virtue of the slurry pump until the glass fiber net is submerged in the slurry; heating, putting the mold filled with the slurry into a baking oven, setting the temperature at 75-85 DEG C, and heating for 2.5-3.5 hours; and demolding: manually or mechanically taking out the soft tile put in the mold.

Description

technical field [0001] The invention relates to a soft slate tile and a process method thereof. Background technique [0002] Traditional tiles are fired, and then the tiles are used to stick to the surface of the wall. Ceramic tiles have a wide range of applications. However, the tiles attached to the wall may fall off after a long time, especially on the tall buildings attached to the outer wall. Once the tiles on the outer wall fall, it will cause a considerable safety hazard. Contents of the invention [0003] In order to solve the above technical problems, the present invention provides a soft slate tile and a process for providing the soft tile. [0004] The technical scheme adopted is as follows: [0005] A soft slate tile is characterized in that it comprises the following components by weight fraction: [0006] Water ----------------------- 10-14%; [0007] Cellulose---------------------0.3-0.7%; [0008] Industrial emulsion -----------------7-9%; [0009] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B26/02C04B14/42C04B24/38
CPCC04B14/42C04B24/383C04B26/02C04B22/002C04B14/02C04B14/06C04B2103/54
Inventor 覃雪霞
Owner 广东福莱特建筑材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap