Aluminum alloy hub hot-spinning technology for improving overall strength of wheel

A technology of aluminum alloy wheels and overall strength, applied in the direction of metal processing equipment, etc., can solve the problems of many production processes and high production costs

Inactive Publication Date: 2017-09-12
ANHUI HENGXING WHEEL
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The biggest disadvantage of forged aluminum wheels is that there are many pro

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Example 1: Aluminum alloy wheel hot spinning process to improve the overall strength of the wheel. The main process of the process is melting-casting preforming-homogenization treatment-heating spinning-preheating treatment-shot peening-spinning-heat treatment- Shot peening-machining-coating; specifically:

[0041] Melting: Prepare aluminum alloy according to requirements and use electric melting furnace for melting;

[0042] Casting preforming: use pressure casting to make liquid metal fill the cavity at a very high speed under high pressure, and solidify under pressure to obtain castings;

[0043] Homogenization treatment: each processed hub must be polished on the deburring machine, and then carefully polished by workers to polish the casting surface of the workpiece to be smooth and flat;

[0044] Heating spinning: at high temperature, the workpiece is heated, and the wire is spun. Before spinning, the workpiece is heated. During the heating process, a layer of str...

Embodiment 2

[0068] Example 2: Aluminum alloy wheel hot spinning process to improve the overall strength of the wheel. The main process of the process is melting-casting preforming-homogenization treatment-heating spinning-preheating treatment-shot peening-spinning-heat treatment- Shot peening-machining-coating; specifically:

[0069] Melting: Prepare aluminum alloy according to requirements and use electric melting furnace for melting;

[0070] Casting preforming: use pressure casting to make liquid metal fill the cavity at a very high speed under high pressure, and solidify under pressure to obtain castings;

[0071] Homogenization treatment: each processed hub must be polished on the deburring machine, and then carefully polished by workers to polish the casting surface of the workpiece to be smooth and flat;

[0072] Heating spinning: at high temperature, the workpiece is heated, and the wire is spun. Before spinning, the workpiece is heated. During the heating process, a layer of str...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Aluminum alloy wheel hot spinning process to improve the overall strength of the wheel. The main process of the process is melting-casting pre-forming-homogenization treatment-heating spinning-preheating treatment-shot peening-spinning-heat treatment-shot peening-machine Plus‑coating. The plastic deformation of hot spinning can bridge the fine loose defects, thereby improving the mechanical properties of the wheel hub. The new casting and spinning process greatly improves the overall strength and corrosion resistance of the wheel, while the machining allowance is greatly reduced, and the service life and safety of the wheel are improved. Significantly improved, which is conducive to vehicle weight reduction and fuel saving, and the production cost of wheels is reduced.

Description

Technical field: [0001] The invention relates to a common aluminum alloy wheel hub, in particular to a hot spinning process for the aluminum alloy wheel hub to improve the overall strength of the wheel. Background technique: [0002] With the rapid development of the automobile industry, the requirements for energy saving and consumption reduction of modern automobiles are constantly increasing, safety and environmental protection regulations are becoming stricter, and the requirements for automobile lightweight are more urgent. Due to the wide use of aluminum alloy wheels, its beautiful, atmospheric and changeable shape design also adds a lot to the car. At present, in the Chinese auto market, the utilization rate of aluminum alloy wheels for cars has reached at least 70 shares of the total car market. According to relevant statistics, in 2003 this proportion was about 50 copies. Aluminum alloy is light in weight, high in strength, good in formability, moderate in price, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B23P15/00B21D22/14B21D53/26
CPCB23P15/00B21D22/14B21D53/26
Inventor 年君
Owner ANHUI HENGXING WHEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap