Pulp for artificial sand dyeing and preparing method thereof

A kind of mortar material and artificial technology, applied in the field of architectural coatings, can solve the problems of VOC emission, good mechanical stability, low energy consumption, etc., and achieve the effect of low VOC emission and high mechanical stability

Active Publication Date: 2017-09-22
FIRST NEW MATERIAL TECH DEV
View PDF1 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The inorganic dyeing method needs to burn the dyed material and the sand source together at high temperature, which consumes a lot of energy, but has good mechanical stability; the organic dyeing method is to blend the color paste and film-forming material with the sand source and then dry at room temperature or bake at low temperature Formed, low energy consumption but poor mechanical stability
Moreover, the organic sand dyeing method is also accompanied by VOC emissions, which is not conducive to environmental protection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pulp for artificial sand dyeing and preparing method thereof
  • Pulp for artificial sand dyeing and preparing method thereof
  • Pulp for artificial sand dyeing and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] The embodiment of the present invention also provides a preparation method for artificial sand dyeing slurry, which is used to prepare the artificial sand dyeing slurry according to the present invention, comprising the following steps:

[0034] Get each raw material and sand source of water-soluble acrylic acid amino glue according to the prescription that is used for artificially dyed sand slurry according to the present invention;

[0035] Preparation of water-soluble acrylic amino glue: Add the water-soluble acrylic resin of water-soluble acrylic amino glue into the dispersion tank, disperse and mix for 10-15 minutes, then add water, continue mixing for 10 minutes, add dispersant, anti-sedimentation agent, leveling agent and defoaming agent Add the agent into the dispersion cylinder, disperse for 10-20min at the speed of 500-1000rpm, then add rutile titanium dioxide and calcined kaolin, disperse at the speed of 2200-3000rpm until the fineness is less than or equal to...

Embodiment 1

[0043] This embodiment provides a slurry material for artificial dyeing sand, which is composed of water-soluble acrylic amino glue and sand source, in percentage by weight, water-soluble acrylic amino glue: 0.9%, sand source: 99.1%;

[0044] Among them, the water-soluble acrylic amino glue is composed of the following components by mass percentage:

[0045]

[0046]

[0047] The above-mentioned preparation method for artificially dyed sand slurry comprises the following steps:

[0048] Preparation of water-soluble acrylic amino glue: first add 60% water-soluble acrylic resin into the dispersion tank, disperse and mix for 10-15 minutes, then add water, continue mixing for 10 minutes, then add dispersant, anti-sedimentation agent, leveling agent, defoamer Put into the dispersion tank, disperse at 500-1000rpm for 10-20min, then add imported titanium dioxide, disperse calcined kaolin at 2200-3000rpm to fineness≤30μm, add amino resin, disperse at low speed 100-300rpm for 10m...

Embodiment 2

[0052] This embodiment provides a slurry material for artificial sand dyeing, which is composed of water-soluble acrylic amino glue and sand source, in percentage by weight, water-soluble acrylic amino glue: 3%, sand source: 97%;

[0053] Among them, the water-soluble acrylic amino glue is composed of the following components by mass percentage:

[0054]

[0055] The above-mentioned preparation method for artificially dyed sand slurry comprises the following steps:

[0056]Preparation of water-soluble acrylic amino glue: first add 40% water-soluble acrylic acid to the dispersion tank, disperse and mix for 10-15 minutes, then add water, continue mixing for 10 minutes, then add dispersant, anti-sedimentation agent, leveling agent, defoamer to the In the dispersion cylinder, disperse at 500-1000rpm for 10-20min, then add imported titanium dioxide, disperse calcined kaolin at 2200-3000rpm until the fineness is ≤30μm, add 6% amino resin, disperse at a low speed of 100-300rpm for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a pulp for artificial sand dyeing and a preparing method thereof. The pulp is prepared from water-soluble acrylic amino adhesive and sand sources; a base material of the water-soluble acrylic acid amino adhesive is prepared from water-soluble acrylic resin, water, a dispersing agent, an anti-settling agent, a flatting agent, an antifoaming agent, a thickening agent, rutile titanium dioxide, calcined kaolin and amino resin. According to the pulp, the water-soluble acrylic resin and the amino resin are subjected to a curing crosslinking reaction under the condition of low-temperature roasting, and are matched with all the assistants, and the water-soluble acrylic acid amino adhesive is prepared. The sand sources are dyed with the water-soluble acrylic acid amino adhesive, prepared artificial color sand has the high mechanical stability, and compared with the mechanical stability of conventional artificial color sand, the mechanical stability of the prepared artificial color sand is prolonged to be 2 h, and the color is invariable; as the water-soluble resin is adopted, VOC discharging is low, and the pulp is ecological and environmentally friendly.

Description

technical field [0001] The invention relates to the field of architectural coatings, in particular to an artificial dyed sand slurry mainly used for real stone paint and a preparation method thereof. Background technique [0002] In recent years, with the development of the real estate industry, the application of architectural coatings has become more and more extensive, and the dosage is also increasing. Among them, real stone paint has the effect of imitating natural stone, marble and granite, and occupies an irreplaceable position in architectural coatings. One of the main raw materials of real stone paint is natural colored sand, which needs to be mined in some ore sources, and then crushed and screened. The mining of mines not only severely damages the local original ecological environment, but also produces dust particles that are one of the main pollution sources of smog. On the other hand, natural colored sand has the characteristics of poor batch stability, which...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B20/10C04B26/18C04B111/82
CPCC04B20/1092C04B26/18C04B2111/00017C04B2111/82C04B24/42C04B14/305C04B18/025C04B14/06C04B14/068C04B14/28C04B2103/408C04B2103/44C04B2103/0068
Inventor 李娅杨会来于丽佳
Owner FIRST NEW MATERIAL TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap