Deodorant composition and preparation method thereof

A composition and deodorant technology, applied in the field of deodorants, can solve the problems of poor dispersibility and compatibility, complex preparation process, short duration of effect, etc., and achieve good high temperature resistance, simple preparation process and long-lasting effect. long time effect

Active Publication Date: 2017-10-10
郑州久源化工有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the existing rubber deodorants are all prepared by mixing activated carbon or other organic materials. The preparation process is complicated, and strong acid or alkali is needed in the preparation process, which is easy to cause environmental pollution, poor compatibility, and short duration. After use, the selectivity is poor, the adsorption capacity is small, the efficiency is low, and the dispersion and compatibility in rubber products are poor.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A deodorant composition, characterized in that the composition is composed of the following components by weight: 72% opal, 7% silane coupling agent, 7% stearic acid, 11% titanium dioxide, and 3% zinc oxide. The particle size of the opal is 3 μm. The particle size of zinc oxide is 40nm, and the titanium dioxide is nano-active titanium dioxide.

[0027] The present embodiment also discloses the preparation method of the above-mentioned deodorant composition, which is characterized in that the preparation method comprises the following steps:

[0028] (1) Opal treatment: The opal ore is crushed into small pieces with a particle size of 0.3 cm by a crusher, and then dried in a rotary kiln dryer to a moisture content of ≤ 0.3%; then the dried opal particles are crushed to 300 Then, calcined in a ceramic jar for 2.5 hours, and the calcination temperature was 900 ° C, to obtain opal powder; finally, the opal powder was crushed to 3 μm to obtain opal micropowder;

[0029] (2...

Embodiment 2

[0032] A deodorant composition, characterized in that the composition is composed of the following components by weight: 92% opal, 2% silane coupling agent, 2% stearic acid, 3% titanium dioxide, and 1% zinc oxide. The particle size of the opal is 6 μm. The particle size of zinc oxide is 30nm, and the titanium dioxide is nano-active titanium dioxide.

[0033] The present embodiment also discloses the preparation method of the above-mentioned deodorant composition, which is characterized in that the preparation method comprises the following steps:

[0034] (1) Opal treatment: The opal ore is crushed into small pieces with a particle size of 0.5 cm by a crusher, and then dried in a rotary kiln dryer to a moisture content of ≤0.3%; then the dried opal particles are crushed to 350 Then, calcined in a ceramic pot for 3 hours, and the calcination temperature was 1000 ° C, to obtain opal powder; finally, the opal powder was pulverized to 6 μm to obtain opal micropowder;

[0035] (2...

Embodiment 3

[0038] A deodorant composition, characterized in that the composition is composed of the following components by weight: 82% opal, 4% silane coupling agent, 4% stearic acid, 8% titanium dioxide, and 2% zinc oxide. The particle size of the opal is 5 μm. The particle size of zinc oxide is 50nm, and the titanium dioxide is nano-active titanium dioxide.

[0039] The present embodiment also discloses the preparation method of the above-mentioned deodorant composition, which is characterized in that the preparation method comprises the following steps:

[0040] (1) Opal treatment: The opal ore is crushed into small pieces with a particle size of 0.5 cm by a crusher, and then dried in a rotary kiln dryer to a moisture content of ≤ 0.3%; then the dried opal particles are crushed to 325 Then, calcined in a ceramic pot for 3 hours, and the calcination temperature was 950 ° C, to obtain opal powder; finally, the opal powder was pulverized to 5 μm to obtain opal micropowder;

[0041] (2...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a deodorant composition. The deodorant composition is characterized by being prepared from, by weight, 72%-92% of opal, 2%-8% of a silane coupling agent, 2%-8% of stearic acid, 1%-12% of titanium dioxide and 1%-4% of zinc oxide. A preparation method of the deodorant composition includes opal treatment, primary mixer preparation and finished product preparation. A prepared product is great in rubber product deodorizing effect and obtained by addition of other components on the basis of opal, and simplicity in preparation process, low cost, less proneness to environment pollution, high compatibility and long efficacy time are realized.

Description

technical field [0001] The patent of the present invention relates to a deodorant, especially a deodorant prepared for rubber and plastic. Background technique [0002] Rubber deodorant is a chemical additive used to eliminate, weaken or cover odor. It can be divided into many types according to different uses. It can effectively reduce or eliminate the odor or odor caused by rubber additives and residual monomers in the rubber itself. It is especially suitable for some rubber products that are reprocessed using secondary recycled materials. Rubber formulation is a rather complicated process. The number of materials added to a formula varies from a dozen to dozens, because most of them are petroleum and chemically purified organic materials, with a variety of raw materials and additives. , under the action of heat and shear force, the small molecular materials in the composite materials in the raw materials or additives will be gradually released, accompanied by an unpleasa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08K9/06C08K9/04C08K3/36C08K3/22C08L21/00
CPCC08K3/22C08K3/36C08K9/04C08K9/06C08K2003/2241C08K2003/2296C08K2201/003C08K2201/011C08L21/00
Inventor 白富超
Owner 郑州久源化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products