Preparation process of warm-keeping and antibacterial fiber

An antibacterial fiber and preparation technology, which is applied in fiber treatment, biochemical fiber treatment, textiles and papermaking, etc., can solve the problems of not having antibacterial ability and threatening human health, and achieve the effect of reducing potential harm

Inactive Publication Date: 2017-10-10
NANTONG BOAO TEXTILE CO LTD
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the fibers used to prepare textiles do not have antibacterial ability. Under certain conditions, they will provide an environment for bacteria to survive and reproduce, threatening human health.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A preparation process for warm-keeping and antibacterial fibers, including two dipping steps, the specific steps are as follows:

[0017] The first impregnation: impregnate the hollow fiber in the alginic acid solution with the opposite charge to the fiber, the bath ratio is 1:15, the concentration of sodium alginate is 5g / L, the neutral electrolyte NaCl is added, the pH is 3, and the impregnation The liquid temperature is 25°C, the soaking time is 1h, and the sodium alginate is adsorbed on the surface of the fiber by electrostatic attraction;

[0018] The second impregnation: the fiber after sodium alginate adsorption is immersed in the antibacterial finishing solution with the opposite charge, the bath ratio is 1:15, the concentration of antibacterial solution is 5g / L, and neutral electrolyte NaCl, oxidation Zinc, pH value 3, dipping solution temperature 20°C, dipping time 1h, the antibacterial agent is adsorbed on the fiber surface after sodium alginate adsorption by...

Embodiment 2

[0020] A preparation process for warm-keeping and antibacterial fibers, including two dipping steps, the specific steps are as follows:

[0021] The first impregnation: the hollow fiber is impregnated in the alginic acid solution with the opposite charge to the fiber, the bath ratio is 1:30, the concentration of sodium alginate is 20g / L, and the neutral electrolyte NaHSO is added 4 , the pH is 11, the temperature of the impregnating solution is 50°C, and the impregnating time is 4 hours. Sodium alginate is adsorbed on the surface of the fiber by electrostatic attraction;

[0022] The second impregnation: soak the fibers adsorbed by sodium alginate in the antibacterial finishing solution with the opposite charge, the bath ratio of the antibacterial solution is 1:30, the concentration of the antibacterial solution is 15g / L, and a neutral electrolyte is added to it NaHSO 4 , Silver ion antibacterial agent, pH value is 11, soaking liquid temperature is 60°C, soaking time is 3h, t...

Embodiment 3

[0024] A preparation process for warm-keeping and antibacterial fibers, including two dipping steps, the specific steps are as follows:

[0025] The first impregnation: the hollow fiber is immersed in the alginic acid solution with the opposite charge to the fiber, the bath ratio is 1:20, the concentration of sodium alginate is 17g / L, and the neutral electrolyte Na 2 SO 4 , the pH is 7, the temperature of the impregnating solution is 35°C, and the impregnating time is 2 hours. Sodium alginate is adsorbed on the surface of the fiber by electrostatic attraction;

[0026] The second impregnation: the fiber after sodium alginate adsorption is immersed in the antibacterial finishing solution with the opposite charge, the bath ratio is 1:20, the concentration of antibacterial solution is 10g / L, and the neutral electrolyte Na is added. 2 SO 4 , copper oxide, the pH value is 7, the temperature of the impregnation solution is 40°C, and the impregnation time is 2 hours. The antibacter...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation process of warm-keeping and antibacterial fiber. The preparation process comprises two impregnation steps. The preparation process has the advantages that the antibacterial fiber is prepared with an electrostatic self-assembly technology by impregnation of a fabric in an antibacterial finishing solution with an opposite charge, so that the internal structure of the fiber is not damaged, and an antibacterial effect can be achieved; a hollow fiber is used as a fiber body, and warm keeping and cold resisting functions are realized; besides, an inorganic antibacterial agent is used, and potential harm to human bodies by organics is reduced.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a preparation process of a warm-keeping and antibacterial fiber. Background technique [0002] With the advancement of science and technology, people's living standards have improved, and consumers have higher and higher requirements for textiles. They are no longer simply beautiful and durable, but need additional multi-functional and beneficial elements, especially for antibacterial and antibacterial. and sterilization of textiles demand is increasing. At present, the fibers used to prepare textiles do not have antibacterial ability, and under certain conditions, they will provide an environment for bacteria to survive and reproduce, threatening human health. [0003] At present, the main method to realize the antibacterial function of fibers is through surface modification technology and blending modification technology. The former is to attach the antibacterial...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/13D06M11/00D06M11/44D06M11/42
CPCD06M15/13D06M11/00D06M11/42D06M11/44D06M16/00
Inventor 王建
Owner NANTONG BOAO TEXTILE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap