Calcium silicate board manufacturing process

A preparation process and technology of calcium silicate board, applied in the direction of manufacturing tools, fiberboard, ceramic molding machines, etc., can solve the problems of complex process flow and high input cost, and achieve the effect of good comprehensive benefit, reasonable process arrangement and simple preparation process

Inactive Publication Date: 2017-10-17
安徽联塑科技实业有限公司
View PDF5 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Nowadays, in the preparation process of calcium silicate board, the process is complicated and the input cost is high, which is not the best solution for preparing calcium silicate board

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The preparation technology of the calcium silicate board that the present invention proposes, the process is as follows:

[0038] The treatment process of step (1) is as follows: First, put the pulp board paper into the pulper, add quantitative water to fully relax, and the relaxation time is 40 minutes; the pulp after relaxation is pumped into the pulp tank, and then diluted with water to a lower concentration Enter the double-disc refiner for coarse grinding.

[0039] The treatment process in step (2) is as follows: First, add the fibers into the pulper, add quantitative water to fully relax; pump the loose fiber mixed pulp into the countercurrent mixer, add an appropriate amount of pulp after fine grinding, and then sequentially Add an appropriate amount of lime powder, quartz powder, and cement, and stir well in a countercurrent mixer to make a slurry.

[0040] The process in step (3) is as follows: First, the slurry is quantitatively and uniformly supplied to the ...

Embodiment 2

[0045] The preparation technology of the calcium silicate board that the present invention proposes, the process is as follows:

[0046] The process of step (1) is as follows: firstly, put the pulpboard paper into the pulper, add quantitative water to fully relax, and the relaxation time is 60 minutes; the pulp after relaxation is pumped into the pulp tank, and then diluted with water to a lower concentration Enter the double-disc refiner for coarse grinding.

[0047] The treatment process in step (2) is as follows: First, add the fibers into the pulper, add quantitative water to fully relax; pump the loose fiber mixed pulp into the countercurrent mixer, add an appropriate amount of pulp after fine grinding, and then sequentially Add an appropriate amount of lime powder, quartz powder, and cement, and stir well in a countercurrent mixer to make a slurry.

[0048] The process in step (3) is as follows: First, the slurry is quantitatively and uniformly supplied to the single-di...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation process of a calcium silicate board, comprising the following steps: (1), pulp treatment; (2), preparation of slurry; (3), pretreatment of slurry; (4), board making and Blank receiving, stacking, pressurization; (5), pre-curing and demoulding; (6), steam curing; (7), drying treatment; (8), sanding and edging and chamfering; (9), Finished product inventory, the invention has reasonable process arrangement, simple and scientific preparation process, reduced cost and good comprehensive benefits.

Description

technical field [0001] The invention relates to the technical field of calcium silicate boards, in particular to a preparation process of calcium silicate boards. Background technique [0002] Calcium silicate board, as a new type of green and environmentally friendly building material, not only has the functions of traditional gypsum board, but also has the advantages of superior fire resistance, moisture resistance and long service life. It is widely used in suspended ceilings and partition walls of industrial and commercial engineering buildings, home decoration, Lining boards for furniture, billboards, ship partitions, warehouse sheds, network floors, and wall panels for tunnels and other indoor projects. [0003] Calcium silicate board is made of loose short fibers such as inorganic mineral fibers or cellulose fibers as reinforcing materials, and siliceous-calcic materials as the main cementing material. Plates made of calcium silicate gel. It is a new type of buildin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D21J1/16D21F11/00D21J1/10D21J1/06B28B1/52B28B11/24
CPCD21J1/16B28B1/525B28B11/24D21F11/00D21J1/06D21J1/10
Inventor 袁丹军
Owner 安徽联塑科技实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com