Thermal insulation coating for barrier fabric

A technology for thermal insulation coatings and fabrics, used in textiles, papermaking, fiber processing, etc., can solve problems such as poor corrosion resistance of coatings, and achieve the effects of preventing corrosion, reducing absorption efficiency, and excellent stability.

Inactive Publication Date: 2017-10-20
常州五荣化工有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention: Aiming at the defect that the coating formed after the use of the existing thermal insulation coating for fabrics is poor in corrosion resistance and unable to meet the existing use requirements, a thermal insulation coating for thermal insulation fabrics is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Thermal insulation coating for barrier fabric

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0018] According to the mass ratio of 1:25, mix barium carbonate and 10% acetic acid solution by mass fraction, heat in a water bath at 45°C for 1 hour, filter the filtrate to prepare solution A, and then mix tetrabutyl titanate with a mass ratio of 1:15 Mix the ester with absolute ethanol, stir and mix with magnetic force at 450r / min for 25min to prepare solution B, then slowly add solution A dropwise to solution B under the condition of heating in a water bath at 45°C at a volume ratio of 1:5, and control The dropping rate was 15min. After the dropping was completed, the mixed gel solution was left to defoam; the mixed gel solution was placed in a spray gun, and evenly sprayed onto the surface of a clean glass plate under 3MPa, and the spray thickness was controlled to be 0.3mm, stand and solidify at room temperature for 3 hours, then dry at 120°C for 25 minutes, stand and cool to room temperature to prepare a sprayed film, crush the sprayed film and pass through a 100-mesh s...

example 2

[0020] According to the mass ratio of 1:25, barium carbonate and 10% acetic acid solution were mixed, heated in a water bath at 50°C for 2 hours, and the filtrate was filtered to prepare solution A. Then, according to the mass ratio of 1:15, tetrabutyl titanate Mix the ester with absolute ethanol, stir and mix for 30 minutes at 450-500r / min with magnetic force to prepare solution B, then slowly add solution A dropwise to solution B at a volume ratio of 1:5 under the condition of heating in a water bath at 50°C , control the dropping rate for 20min, after the addition is completed, let stand to defoam to obtain the mixed gel solution; put the mixed gel solution in the spray gun, spray evenly to the surface of the clean glass plate under 5MPa, and control the spraying The thickness is 0.5mm, after standing and solidifying at room temperature for 5 hours, then drying at 125°C for 30 minutes, standing and cooling to room temperature to prepare a sprayed film, crushing the sprayed f...

example 3

[0022]According to the mass ratio of 1:25, mix barium carbonate and 10% acetic acid solution by mass fraction, heat in a water bath at 47°C for 2 hours, filter the filtrate to prepare solution A, and then prepare solution A according to the mass ratio of 1:15, tetrabutyl titanate Mix the ester with absolute ethanol, stir and mix for 27min under magnetic force at 475r / min to prepare solution B, and then slowly add solution A to solution B under the condition of heating in a water bath at 47°C at a volume ratio of 1:5, and control The dropping speed rate is 17min. After the dropping is completed, the mixed gel solution is obtained by standing for defoaming; the mixed gel solution is placed in the spray gun and evenly sprayed on the surface of the clean glass plate under 4MPa, and the thickness of the sprayed coating is controlled to be 0.4mm, stand and solidify at room temperature for 4 hours, then dry at 122°C for 27 minutes, stand and cool to room temperature to prepare a spray...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a thermal insulation coating for a barrier fabric and belongs to the technical field of preparation of coatings. The thermal insulation coating is characterized in that a flaky material is used as a substrate and is loaded with a deposited tantalum oxide material; the deposited tantalum oxide material uniformly coats a flaky substrate-shaped lens to form filler particles with high reflection strength; the filler particles have excellent reflecting properties for visible light and near-infrared light, so that the heat absorption property of textiles is effectively reduced, and a heat insulating protection effect is realized; and moreover, tantalum oxide formed by surface deposition and calcination compactly coats modified filler doped in the coating prepared by the invention and has excellent stable performance, so that the corrosion is effectively prevented in the daily use process of the coating, and the thermal insulation coating has high stability and using persistence.

Description

technical field [0001] The invention relates to a heat-insulating paint for heat-insulating fabrics, belonging to the technical field of paint preparation. Background technique [0002] Heat-insulating coated fabric is to coat a layer of heat-insulating coating on the fabric, which can reduce the internal temperature of the fabric covering by blocking, reflecting or radiating solar energy, and can reduce energy consumption. It has a good application prospect in the textile industry. Textile thermal insulation coatings were originally used in fabrics worn by military personnel to eliminate or reduce the difference in infrared reflection characteristics between the fabric and the background by reflecting, blocking, and radiating infrared radiation to achieve infrared camouflage for military personnel. Then it was applied in the civilian field. According to the way of inhibiting infrared heat radiation, the thermal insulation coating for fabrics can be divided into barrier the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D06M11/46D06M11/47
CPCD06M11/46D06M11/47
Inventor 王金华季美
Owner 常州五荣化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com