Fireproof heat-isolating building material and preparation method thereof

A technology of building materials and building boards, which is applied in the field of building materials, can solve the problems of poor fireproof and heat insulation effects and high cost, and achieve the effects of good fireproof and heat insulation effects, low cost and good refrigeration effect

Inactive Publication Date: 2017-10-24
肥西县碧涛建材有限公司
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In order to solve the problems of poor fireproof and heat insulation effect and high cost in existing fireproof and heat insulation building materials, the purpose of the present invention is to provide a kind of fireproof and heat insulation building material and its preparation method, which have good fireproof and heat insulation effect and low cost. low advantage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fireproof heat-isolating building material and preparation method thereof
  • Fireproof heat-isolating building material and preparation method thereof
  • Fireproof heat-isolating building material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A fire-proof and heat-insulating building material, which is made of the following raw materials in parts by weight:

[0041]

[0042] It has the advantages of the best fire and heat insulation effect and the lowest cost.

[0043] A method for preparing a fire-proof and heat-insulating building material, comprising the following steps:

[0044] (1) sepiolite powder, attapulgite powder, bamboo charcoal powder and calcium carbonate powder are pulverized into 400 mesh powder respectively;

[0045] (2) Take by weight 25 parts of stearyl alcohol, 14 parts of sepiolite powder, 8 parts of attapulgite powder, 24 parts of vitrified microbeads, 8 parts of bamboo charcoal powder, 24 parts of gypsum board, and 65 parts of calcium carbonate powder , 8 parts of foamed ceramic plates, 18 parts of glass wool, heated to 200°C for stirring and mixing;

[0046] (3) Add 6 parts of silk fibroin fiber and 18 parts of 1,4-butenediol to the mixture in step (2), and then heat to 200°C for ...

Embodiment 2

[0053] A fire-proof and heat-insulating building material, which is made of the following raw materials in parts by weight:

[0054]

[0055] It has the advantages of good fireproof and heat insulation effect and low cost.

[0056] A method for preparing a fire-proof and heat-insulating building material, comprising the following steps:

[0057] (1) Sepiolite powder, attapulgite powder, bamboo charcoal powder and calcium carbonate powder are pulverized into 400 mesh powders respectively with a pulverizer;

[0058](2) Take by weight 20 parts of stearyl alcohol, 10 parts of sepiolite powder, 6 parts of attapulgite powder, 22 parts of vitrified microbeads, 6 parts of bamboo charcoal powder, 22 parts of gypsum board, and 60 parts of calcium carbonate powder , 6 parts of foamed ceramic plates, 16 parts of glass wool, heated to 200°C for stirring and mixing;

[0059] (3) Add 5 parts of silk fibroin fiber and 16 parts of 1,4-butenediol to the mixture in step (2), and then heat t...

Embodiment 3

[0065] A fire-proof and heat-insulating building material, which is made of the following raw materials in parts by weight:

[0066]

[0067] It has the advantages of good fireproof and heat insulation effect and low cost.

[0068] A method for preparing a fire-proof and heat-insulating building material, comprising the following steps:

[0069] (1) Sepiolite powder, attapulgite powder, bamboo charcoal powder and calcium carbonate powder are pulverized into 400 mesh powders respectively with a pulverizer;

[0070] (2) Take by weight 15 parts of stearyl alcohol, 8 parts of sepiolite powder, 5 parts of attapulgite powder, 20 parts of vitrified microbeads, 5 parts of bamboo charcoal powder, 20 parts of gypsum board, and 50 parts of calcium carbonate powder , 5 parts of foamed ceramic plates, 15 parts of glass wool, heated to 200°C for stirring and mixing;

[0071] (3) Add 4 parts of silk fibroin fiber and 15 parts of 1,4-butenediol to the mixture in step (2), and then heat t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a fireproof heat-isolating building material and a preparation method thereof and relates to the field of building materials. The building material is prepared from the following raw materials in parts by weight: 15-30 parts of stearyl alcohol, 8-15 parts of sepiolite powder, 5-10 parts of attapulgite powder, 20-25 parts of glass beads, 5-10 parts of bamboo carbon powder, 20-25 parts of gypsum boards, 50-70 parts of calcium carbonate powder, 5-10 parts of foamed ceramic plates, 15-20 parts of glass wool, 4-6 parts of fibroin fibers and 15-20 parts of 1,4-butenediol. The preparation method of the building material comprises the following steps of: crushing; stirring; pouring; and cooling. The building material provided by the invention solves the problem that an existing fireproof heat-isolating building material is poor in fireproof heat-isolating effect and high in cost.

Description

technical field [0001] The invention belongs to the field of building materials, and in particular relates to a fire-proof and heat-insulating building material and a preparation method thereof. Background technique [0002] With the continuous development of social economy and science and technology, people's living standards are rapidly improving, and the requirements for building materials are more prominent. There are many types of new building materials in different forms, leading the development and improvement of modern building technology innovation trends. [0003] New building materials are economical, practical, fashionable and environmentally friendly, and fully meet the aesthetic requirements of the general public for architectural decoration. With the continuous development of the times, new building materials have emerged as the times require and are constantly innovating in technology. The main new building materials include: new wall materials, fireproof and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14C04B111/28
CPCC04B28/14C04B2111/28C04B2201/32C04B24/085C04B14/042C04B14/102C04B18/027C04B14/022C04B14/28C04B14/42C04B16/06C04B24/02
Inventor 俞克波
Owner 肥西县碧涛建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com