Thermochromic TPE (thermoplastic elastomer) material

A color-forming agent and flame retardant technology, which is applied in the field of TPE materials to achieve the effect of improving the flame retardant effect, reducing losses and avoiding fire accidents

Inactive Publication Date: 2017-10-24
邓韵
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, with the increase of people's needs, ordinary materials have been difficult to meet people's needs. Therefore, it is necessary to design a TPE material that heats up and develops color.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A temperature-rising and color-developing TPE material, in parts by mass, includes the following components:

[0035] TPE 70 parts,

[0036] 25 parts polyester staple fiber,

[0037] 20 parts of epoxy resin,

[0038] 20 parts of curing agent,

[0039] 0.3 parts of hair coloring agent,

[0040] 0.2 parts of color developer,

[0041] 10 parts of flame retardant,

[0042] Adhesive 8 parts.

[0043] In terms of mass percentage, the TPE includes the following components:

[0044] SEBS 45%,

[0045] White Mineral Oil 15%,

[0046] Polyurethane 10%,

[0047] Calcium Carbonate 10%,

[0048] Polypropylene 10%,

[0049] EVA 8%,

[0050] Antioxidant 2%.

[0051] The curing agent is diaminodichlorodiphenylmethane.

[0052] The binder is one or more of carboxymethyl cellulose, styrene-butadiene latex, styrene-acrylic latex, and starch.

[0053] The chromogenic agent is one or more of crystal violet lactone (CVL), ODB (N102), thermosensitive green, and thermosensitive ...

Embodiment 2

[0059] A temperature-rising and color-developing TPE material, in parts by mass, includes the following components:

[0060] 30 parts of TPE,

[0061] 50 parts of polyester staple fiber,

[0062] 25 parts of epoxy resin,

[0063] 10 parts of curing agent,

[0064] 0.5 parts of hair coloring agent,

[0065] 0.4 parts of developer,

[0066] 25 parts of flame retardant,

[0067] Adhesive 10 parts.

[0068] In terms of mass percentage, the TPE includes the following components:

[0069] SEBS 45%,

[0070] White Mineral Oil 15%,

[0071] Polyurethane 10%,

[0072] Calcium Carbonate 10%,

[0073] Polypropylene 10%,

[0074] EVA 8%,

[0075] Antioxidant 2%.

[0076] The curing agent is diaminodichlorodiphenylmethane.

[0077] The binder is one or more of carboxymethyl cellulose, styrene-butadiene latex, styrene-acrylic latex, and starch.

[0078] The chromogenic agent is one or more of crystal violet lactone (CVL), ODB (N102), thermosensitive green, and thermosensitive...

Embodiment 3

[0084] A temperature-rising and color-developing TPE material, in parts by mass, includes the following components:

[0085] TPE 50 parts,

[0086] 5 parts polyester staple fiber,

[0087] 30 parts of epoxy resin,

[0088] 15 parts of curing agent,

[0089] 0.1 parts of hair coloring agent,

[0090] 0.6 parts of color developer,

[0091] 50 parts of flame retardant,

[0092] Adhesive 5 parts.

[0093] In terms of mass percentage, the TPE includes the following components:

[0094] SEBS 45%,

[0095] White Mineral Oil 15%,

[0096] Polyurethane 10%,

[0097] Calcium Carbonate 10%,

[0098] Polypropylene 10%,

[0099] EVA 8%,

[0100] Antioxidant 2%.

[0101] The curing agent is diaminodichlorodiphenylmethane.

[0102] The binder is one or more of carboxymethyl cellulose, styrene-butadiene latex, styrene-acrylic latex, and starch.

[0103] The chromogenic agent is one or more of crystal violet lactone (CVL), ODB (N102), thermosensitive green, and thermosensitive r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a thermochromic TPE (thermoplastic elastomer) material. The thermochromic TPE material is prepared from TPE, polyester staple fibers, epoxy resin, a curing agent, a chromogenic agent, color developing agent, flame retardants and an adhesive. The thermochromic TPE material is high in elasticity, strength and rebound resilience and has a characteristic of availability for injection molding. The thermochromic TPE material can be controlled to realize a thermochromic function at a set temperature through selection of different chromogenic agents and color developing agents, warning of the internal temperature of the material can be realized, and fire accidents can be avoided by warning when the temperature is overhigh; due to addition of the flame retardants, combustion of the material can be prevented in case of inevitable fire, so that loss caused by fire disasters is reduced; by joint use of halogen-free flame retardants and synergistic flame retardants, flame retardation effects are remarkably improved.

Description

technical field [0001] The invention relates to the field of special TPE materials, in particular to a TPE material that develops color when heated. Background technique [0002] Compared with rubber, the more focused meaning of elastomer is a concept of physics and materials science, and its scope is broader. In addition to rubber, elastomers also include many polymer materials with different elastic deformations and diverse cross-linking methods of macromolecular chains. According to whether the elastomer can be plasticized, it can be divided into two categories: thermosetting elastomer and thermoplastic elastomer. Thermosetting elastomers, which are rubber in the traditional sense, and thermoplastic elastomers (Thermoplastic elastomer), abbreviated as TPE, have gradually been used more and more commercially since the 1990s. This classification also shows that these two types of elastomers are processed in two different ways: rubber is processed by thermosetting equipmen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L53/02C08L91/06C08L75/04C08L23/12C08L23/08C08L67/00C08L63/00C08L61/14C08K13/02C08K5/13C08K3/38C08K3/22C08K3/32C08K13/06C08K9/00C08K5/523
CPCC08L67/00C08K2003/2224C08K2003/2255C08K2003/323C08K2003/387C08L53/025C08L2201/02C08L2205/035C08L2205/16C08L2207/04C08L91/06C08L75/04C08L23/12C08L23/0853C08L63/00C08L61/14C08K13/02C08K5/13C08K3/38C08K3/22C08K3/32C08K13/06C08K9/00C08K5/523C08K3/2279
Inventor 邓韵
Owner 邓韵
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com