Polyester polyamide and cotton bamboo blending process

A polyester-nylon and cotton-bamboo technology, applied in the field of polyester-nylon and cotton-bamboo blended textile technology, can solve the problems of multiple dams and unsatisfactory effects, and achieve the effect of not being easy to break and reducing the number of dams

Inactive Publication Date: 2017-10-24
RUGAO XIAYUAN SCI & TECH ESTABLISH A BUSINESS SERVICES CO LTD
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the effect of the above-mentioned traction and pretreatment process is still unsatisfactory, and there will still be more baffles in the final woven product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] In this embodiment, the blended textile process of nylon, cotton and bamboo includes the following steps:

[0030] (1) Polyester-nylon blended yarn is selected, and the polyester-nylon blended yarn is formed by blending polyester fiber and nylon fiber, and the ratio of polyester fiber to nylon fiber is 3:1;

[0031] (2) select cotton-bamboo blended silk, described cotton-bamboo blended silk is formed by blending cotton fiber and bamboo fiber, and the ratio of described cotton fiber and bamboo fiber is 2:1;

[0032] (3) Measure the stretchable maximum of cotton-bamboo blended silk, that is, the maximum pressure value that can be applied to it;

[0033] (4) Put the polyester-nylon blended yarn in a water steamer at a water temperature of 100°C and steam for 50 minutes;

[0034] (5) Place the polyester-nylon blended yarn treated in step (4) in a natural state for pre-setting for 20 hours;

[0035] (6) Use the water-jet loom to carry out mixed spinning with the maximum pr...

Embodiment 2

[0037] In this embodiment, the blended textile process of nylon, cotton and bamboo includes the following steps:

[0038] (1) Polyester-nylon blended yarn is selected, and the polyester-nylon blended yarn is formed by blending polyester fiber and nylon fiber, and the ratio of polyester fiber to nylon fiber is 3:1;

[0039] (2) select cotton-bamboo blended silk, described cotton-bamboo blended silk is formed by blending cotton fiber and bamboo fiber, and the ratio of described cotton fiber and bamboo fiber is 2:1;

[0040] (3) Measure the stretchable maximum of cotton-bamboo blended silk, that is, the maximum pressure value that can be applied to it;

[0041] (4) Put the polyester-nylon blended yarn in a water steamer at a water temperature of 90°C and steam for 60 minutes;

[0042] (5) Place the polyester-nylon blended yarn treated in step (4) in a natural state for pre-setting for 16 hours;

[0043] (6) Use the water-jet loom to carry out mixed spinning with the maximum pre...

Embodiment 3

[0045] In this embodiment, the blended textile process of nylon, cotton and bamboo includes the following steps:

[0046] (1) Polyester-nylon blended yarn is selected, and the polyester-nylon blended yarn is formed by blending polyester fiber and nylon fiber, and the ratio of polyester fiber to nylon fiber is 3:1;

[0047] (2) select cotton-bamboo blended silk, described cotton-bamboo blended silk is formed by blending cotton fiber and bamboo fiber, and the ratio of described cotton fiber and bamboo fiber is 2:1;

[0048] (3) Measure the stretchable maximum of cotton-bamboo blended silk, that is, the maximum pressure value that can be applied to it;

[0049] (4) Put the polyester-nylon blended yarn in a water steamer at a water temperature of 95°C and steam for 55 minutes;

[0050] (5) Place the polyester-nylon blended yarn treated in step (4) in a natural state for pre-setting for 18 hours;

[0051] (6) Use the water-jet loom to carry out mixed spinning with the maximum pre...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a polyester polyamide and cotton bamboo blending process. The process includes following steps: (1), selecting polyester polyamide blended yarn; (2), selecting cotton bamboo blended yarn; (3), measuring maximum stretching limit of the cotton bamboo blended yarn, namely maximum pressure value that can be applied to the cotton bamboo blended yarn; (4), putting the polyester polyamide blended yarn into a water steamer; (5), presetting the polyester polyamide blended yarn after being treated in the step (4); (6), adopting a hydraulic loom to blend the polyester polyamide blended yarn and the cotton bamboo blended yarn at the maximum pressure value in the step (3), wherein a nozzle of 75-40 in specification is adopted for traction of the polyester polyamide blended yarn, and a nozzle of 45-20 in specification is adopted for traction of the cotton bamboo blended yarn. The polyester polyamide and cotton bamboo blending process has the advantage that the defect that finally woven products are unsatisfactory in quality due to the fact that characteristics of the polyester polyamide blended yarn and the cotton bamboo blended yarn are different when the polyester polyamide blended yarn and the cotton bamboo blended yarn are adopted for blending can be overcome.

Description

technical field [0001] The invention relates to a weaving process, and relates to a method of using different raw materials for mixed spinning [0002] The weaving technology of weaving, especially relates to a kind of polyester brocade and cotton bamboo mixed weaving technology. Background technique [0003] When using different raw material yarns for mixed spinning, the tension of various raw material yarns and suitable processing temperature are important parameters that affect the quality of the final product. Therefore, it is necessary to take into account the characteristics of different raw material yarns when designing the textile process. For example, when we use polyester-nylon blended yarn and cotton-bamboo blended yarn to weave fabrics, since the characteristics of polyester-nylon blended yarn and cotton-bamboo blended yarn are quite different, we need to use a specific process for weaving. Specifically, the cotton-bamboo blended yarn is soft and comfortable, bu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D15/00D03D47/32D02G3/04D06B21/00
CPCD02G3/042D02G3/045D03D47/32D06B21/00D10B2201/02D10B2201/10D10B2331/02D10B2331/04D03D15/47
Inventor 曹建民
Owner RUGAO XIAYUAN SCI & TECH ESTABLISH A BUSINESS SERVICES CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products