Honeycomb denitration catalyst with increased specific surface area and preparation method
A denitration catalyst, specific surface area technology, applied in chemical instruments and methods, heterogeneous catalyst chemical elements, physical/chemical process catalysts, etc., can solve the problem of unbalanced active centers, etc. Crush strength, the effect of improving efficiency
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0044] Example 1:
[0045] Add 20g of activated alumina to water, make a slurry to form a slurry, and add TiO 2 500g of titanyl sulfate is dissolved in sulfuric acid solution to form TiO 2 It is a 35g / L solution with WO 3 A total of 10g of ammonium paratungstate solution, after ultrasonic vibration for 2h, gradually add ammonia water to adjust the pH to 9.5, after the precipitation is complete, filter and wash; then use deionized water to make the washed material into a slurry with a water content of 50%, and add V 2 O 5 5g of ammonium metavanadate solution, ultrasonic vibration for 1.5h while stirring, after direct drying, roasting at 620℃ for 6h; after roasting, the powder is mixed with MoO 3 A total of 10g of ammonium molybdate was made into a slurry with 30% water. After stirring, 4g of sesame powder was added, stirred for 40min, sealed and allowed to stand for 24h, extruded into a honeycomb shape, dried and then coated with 15g of nano-scale tungsten oxide. After calcination a...
Example Embodiment
[0048] Example 2
[0049] Add 40g of activated alumina to water, make a slurry to form a slurry, and add TiO 2 500g of titanyl sulfate is dissolved in sulfuric acid solution to form TiO 2 40g / L solution, add WO 3 15g of ammonium paratungstate solution, after ultrasonic vibration for 1h, gradually add ammonia water to adjust the pH to 9.0. After precipitation is complete, filter and wash; then use deionized water to make a slurry with 50% water content and add V 2 O 5 20g of ammonium metavanadate solution, ultrasonic vibration for 1.5h while stirring, after direct drying, roasting at 400℃ for 6h; after roasting, the powder is mixed with MoO 3 A total of 3g of ammonium molybdate was made into a slurry with 30% water. After stirring, 4g of sesame powder was added, stirred for 40min, sealed and allowed to stand for 10h, extruded into a honeycomb shape, dried, and then coated with 25g of nano-grade tungsten oxide. After calcination at ℃ for 8h, a denitration catalyst is obtained. The f...
Example Embodiment
[0052] Example 3
[0053] Add 20g of activated alumina into water, make a slurry to form a slurry, and add TiO 2 500g of titanyl sulfate is dissolved in sulfuric acid solution to form TiO 2 40g / L solution, add WO 3 A total of 12.5g of ammonium paratungstate solution, after ultrasonic vibration for 3h, gradually add ammonia water to adjust the pH to 10.5, after the precipitation is complete, filter and wash; then use deionized water to make the washed material into a slurry with a water content of 35%. V 2 O 5 30g of ammonium metavanadate solution, ultrasonic vibration for 1.5h while stirring, after direct drying, calcination at 400℃ for 6h; after calcination, the powder is mixed with MoO 3 A total of 3g of ammonium molybdate was made into a slurry with 30% water, 4g of sesame powder was added after stirring, stirred for 40min, sealed and allowed to stand for 10h, extruded into a honeycomb shape, dried and coated with 25g of nanoscale tungsten oxide, After calcination at ℃ for 8h, ...
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Specific surface area | aaaaa | aaaaa |
Pore volume | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap