Environmentally-friendly antiflaming foaming material of bumper and preparation method

A foam material and bumper technology, which is applied in the field of environmental protection flame retardant foam materials for bumpers and their preparation, can solve the problem of short escape time for personnel, difficulty in protecting the body and people, and the inability of bumper strength to achieve ideal effects, etc. question

Inactive Publication Date: 2017-11-24
YANGZHONG TIANZHENG SYNTHETIC MATERIAL RES CENT
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The strength of traditional bumpers usually cannot achieve ideal results. In the event of an accident, it is difficult to provide ideal protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A method for preparing an environmentally friendly flame-retardant foaming material for a bumper, comprising the following preparation steps:

[0016] (1) raw material processing: carry out drying treatment with polyether 403, polyether 635 and isocyanate, drying temperature is 40 ℃, drying time 6H;

[0017] (2) Weighing proportion: according to the mass proportion, weigh silicone oil: 2.5 parts, catalyst HP300: 1.2 parts, catalyst HP224: 1 part, flame retardant TCEP: 38 parts and water: 3.5 parts, and after drying Polyether 403: 40 parts, polyether 635: 20 parts;

[0018] (3) Preparation of combined materials: Add the weighed polyether 403, polyether 635, silicone oil, catalyst HP300, catalyst HP224, water, and flame retardant TCEP into the reaction kettle in order to fully stir. The stirring time is 0.5h. The temperature is 50°C, the stirring speed is 250r / min, and the composite material can be obtained;

[0019] (4) Synthetic foaming material: add isocyanate in the...

Embodiment 2

[0021] A method for preparing an environmentally friendly flame-retardant foaming material for a bumper, comprising the following preparation steps:

[0022] (1) raw material processing: carry out drying treatment with polyether 403, polyether 635 and isocyanate, drying temperature is 40 ℃, drying time 7H;

[0023] (2) Weighing proportion: according to the mass proportion, weigh silicone oil: 2.75 parts, catalyst HP300: 1.3 parts, catalyst HP224: 1.25 parts, flame retardant TCEP: 40 parts and water: 4.05 parts, and after drying Polyether 403: 45 parts, polyether 635: 25 parts;

[0024] (3) Preparation of combined materials: Add the weighed polyether 403, polyether 635, silicone oil, catalyst HP300, catalyst HP224, water, and flame retardant TCEP into the reaction kettle in order to fully stir. The stirring time is 1h, and the stirring temperature The temperature is 65°C, and the stirring speed is 265r / min, and the composite material can be obtained;

[0025] (4) Synthetic fo...

Embodiment 3

[0027] A method for preparing an environmentally friendly flame-retardant foaming material for a bumper, comprising the following preparation steps:

[0028] (1) raw material processing: carry out drying treatment with polyether 403, polyether 635 and isocyanate, drying temperature is 40 ℃, drying time 8H;

[0029] (2) Weighing proportion: according to the mass proportion, weigh silicone oil: 3 parts, catalyst HP300: 1.4 parts, catalyst HP224: 1.5 parts, flame retardant TCEP: 42 parts and water: 4.6 parts, and after drying Polyether 403: 50 parts, polyether 635: 30 parts;

[0030] (3) Preparation of composite materials: Add the weighed polyether 403, polyether 635, silicone oil, catalyst HP300, catalyst HP224, water, and flame retardant TCEP into the reaction kettle in order to fully stir, the stirring time is 1.5h, and stir The temperature is 80°C, the stirring speed is 280r / min, and the composite material can be obtained;

[0031] (4) Synthetic foaming material: add isocya...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environmentally-friendly antiflaming foaming material of a bumper and a preparation method. The environmentally-friendly antiflaming foaming material of the bumper is prepared from the following ingredients in parts by weight: 1 part of acetonitrile polyester and 1.8 parts of composite material, wherein the composite material is prepared from the following ingredients in parts by weight: 40-50 parts of polyether 403, 20-30 parts of polyether 635, 2.5-3 parts of silicone oil, 1.2-1.4 parts of catalyst HP300, 1-1.5 parts of catalyst HP224, 3.5-4.6 parts of water and 38-42 parts of fire retardant TCEP (Tris(2-carboxyethyl)phosphine). According to the environmentally-friendly antiflaming foaming material, a reasonable proportion is adopted for raw materials, and the prepared foaming material has good fire resistance and stability; in addition, the bumper prepared from the foaming material has high fire-proof safety and strength and long service life; the foaming material prepared from an environmentally-friendly raw material which adopts the reasonable proportion does not release harmful substances so as to prevent from harming environment and human bodies.

Description

technical field [0001] The invention relates to an environment-friendly flame-retardant foaming material for a bumper and a preparation method thereof, belonging to the field of automobiles. Background technique [0002] At present, with the development of the automobile industry and the enhancement of people's awareness of safety and environmental protection, people's requirements for auto parts have also increased significantly. As a part of safety precautions, people have stricter requirements for bumpers. High temperature resistance, high flame retardancy, high strength, light weight, and high environmental protection characteristics. The strength of traditional bumpers usually cannot achieve ideal results. In the event of an accident, it is difficult to provide ideal protection for the body and people. Also, due to poor flame retardancy, the escape time of personnel is short, and there is a great potential safety hazard. . Therefore, it is the goal that this field has...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08G18/48C08G18/61C08L75/08C08K5/50
CPCC08G18/4804C08G18/48C08G18/61C08K5/50C08L2201/02C08L2201/08C08L2203/14C08L75/08
Inventor 朱章娣朱凌宇纪朝根
Owner YANGZHONG TIANZHENG SYNTHETIC MATERIAL RES CENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap