Black aluminum alloy and preparation method thereof

An aluminum alloy, black technology, applied in the field of black aluminum alloy and its preparation, can solve problems such as affecting people's physical and mental health, environmental pollution, and can not meet the needs of modern people's lives, and achieves easy popularization, simple production process and low production cost. Effect

Inactive Publication Date: 2017-12-08
苏州飞伦利斯金属科技有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Non-ferrous metals in the traditional sense are determined by the color of the metal itself. Generally, paint and other materials need to be coated on its surface after processing for rust prevention and decoration. The production and use of paint will cause serious pollution to the environment. And after use, it will continue to release harmful substances, which will affect people's physical and mental health, and cannot meet the needs of modern people's lives. Therefore, an improved technology is urgently needed to solve the above technical defects

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A black aluminum alloy and a preparation method thereof, comprising the following components in parts by weight: aluminum: 50-80 parts; zinc: 20-40 parts; copper: 5-8 parts; titanium: 4-7 parts, black pigment: 5-10 servings.

[0019] The black pigment is copper chrome black.

[0020] Include the following steps:

[0021] a. Make aluminum, zinc, copper, titanium and black pigment into powder, the fineness of powder is 300-500 mesh;

[0022] b. Mix aluminum, zinc and copper powder and heat to 1000°C;

[0023] c. Heating the titanium powder until it melts;

[0024] d. Add the molten titanium obtained in step c to the molten mixture obtained in step b and stir, keep the temperature at 1000-1200°C, and stir for 3-5 minutes;

[0025] e. Add the black pigment powder to the alloy mixed melt obtained in step d, keep stirring for 10-15min, and keep the temperature at 900-1000°C during stirring;

[0026] f. Inject into the mold according to the molding requirements and cool n...

Embodiment 2

[0028] A black aluminum alloy and a preparation method thereof, comprising the following components in parts by weight: aluminum: 50-80 parts; zinc: 20-40 parts; copper: 5-8 parts; titanium: 4-7 parts, black pigment: 5-10 servings.

[0029] The black pigment is copper chrome black.

[0030] Include the following steps:

[0031] a. Make aluminum, zinc, copper, titanium and black pigment into powder, the fineness of powder is 300-500 mesh;

[0032] b. Mix aluminum, zinc and copper powder and heat to 1000°C;

[0033] c. Heating the titanium powder until it melts;

[0034] d. Add the molten titanium obtained in step c to the molten mixture obtained in step b and stir, keep the temperature at 1000-1200°C, and stir for 3-5 minutes;

[0035] e. Add the black pigment powder to the alloy mixed melt obtained in step d, keep stirring for 10-15min, and keep the temperature at 900-1000°C during stirring;

[0036] f. Inject into the mold according to the molding requirements and cool n...

Embodiment 3

[0038] A black aluminum alloy and a preparation method thereof, comprising the following components in parts by weight: aluminum: 50-80 parts; zinc: 20-40 parts; copper: 5-8 parts; titanium: 4-7 parts, black pigment: 5-10 servings.

[0039] The black pigment is copper chrome black.

[0040] Include the following steps:

[0041] a. Make aluminum, zinc, copper, titanium and black pigment into powder, the fineness of powder is 300-500 mesh;

[0042] b. Mix aluminum, zinc and copper powder and heat to 1000°C;

[0043] c. Heating the titanium powder until it melts;

[0044] d. Add the molten titanium obtained in step c to the molten mixture obtained in step b and stir, keep the temperature at 1000-1200°C, and stir for 3-5 minutes;

[0045] e. Add the black pigment powder to the alloy mixed melt obtained in step d, keep stirring for 10-15min, and keep the temperature at 900-1000°C during stirring;

[0046] f. Inject into the mold according to the molding requirements and cool n...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Login to View More

Abstract

The invention discloses black aluminum alloy and a preparation method thereof. The black aluminum alloy comprises the following components of, by weight, 50-80 parts of aluminum, 20-40 parts of zinc, 5-8 parts of copper, 4-7 parts of titanium and 5-10 parts of black pigment. The method comprises the following steps that a, aluminum, zinc, copper, titanium and the black pigment are powdered, and the powder fineness is 300-500 meshes; b, aluminum powder, zine powder and copper powder are mixed and heated to 1000 DEG C; c, titanium powder is heated to be melted; and d, the melted titanium obtained in the step c is added into a melted mixture obtained in the step b and stirred, the temperature is maintained at 1000-1200 DEG C, and the stirring time is 3-5 min. The black aluminum alloy and the preparation method thereof have the beneficial effects that the manufacturing process is simple, the manufacturing cost is low, the surfaces of finished products do not need to be coated with antirust paint or decoration paint, no hazardous substance is released, the health demands of people are met, and popularization is easy.

Description

technical field [0001] The invention relates to a method for preparing an alloy metal, in particular to a black aluminum alloy and a method for preparing the same. Background technique [0002] Non-ferrous metal alloys are widely used, mainly used in automobiles, building materials, home appliances, electric power, 3C, machinery manufacturing and other industries. In recent years, industries such as automobiles, building materials, home appliances, electric power, 3C, and machinery manufacturing have shown a trend of rapid development, while the development of the non-ferrous metal alloy manufacturing industry relies on the pull of downstream industries. With the development of downstream industries, the non-ferrous metal alloy manufacturing industry has also gained Rapid development. Non-ferrous metal alloys are widely used, mainly used in automobiles, building materials, home appliances, electric power, 3C, machinery manufacturing and other industries. In recent years, i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C21/10C22C1/02
CPCC22C1/026C22C21/10
Inventor 王晶
Owner 苏州飞伦利斯金属科技有限公司