High-temperature-resistant belt material composition, and high-temperature-resistant belt and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A composition and high temperature resistant technology, which is applied in the field of belt production and preparation, can solve the problems of reducing the service life of the belt and belt aging
Inactive Publication Date: 2018-01-19
WUHU KANGDAOER TEXTILE SCI
View PDF0 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0004] In view of the above-mentioned prior art, the purpose of the present invention is to overcome the problem that in the prior art, in the actual use process, the friction frequency of the belt is often relatively high, which easily causes the belt to heat up due to friction and causes the aging of the belt, greatly reducing the service life of the belt. problems, thereby providing a high-temperature-resistant belt material composition, a high-temperature-resistant belt and a preparation method thereof that can effectively prolong the service life, greatly reduce the cost of use, and improve production efficiency
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
preparation example Construction
[0019] The present invention also provides a method for preparing a high-temperature-resistant belt, wherein the preparation method includes: mixing and melting acrylate rubber, EPDM rubber, magnesium nitrate, zinc nitrate, potassium hydrogen tartrate, sulfur, and nanometer zinc oxide After extruding, a high temperature resistant belt is obtained; wherein,
[0020] Relative to 100 parts by weight of the acrylate rubber, the amount of EPDM rubber is 30-80 parts by weight, the amount of magnesium nitrate is 10-20 parts by weight, and the amount of zinc nitrate is 10-20 parts by weight. 20 parts by weight, the amount of potassium hydrogen tartrate is 0.1-5 parts by weight, the amount of sulfur is 1-5 parts by weight, and the amount of nano zinc oxide is 1-5 parts by weight.
[0021] In a preferred embodiment of the present invention, in order to further improve the high temperature resistance of the belt, relative to 100 parts by weight of the acrylate rubber, the amount of the E...
Embodiment 1
[0028] Mix 100g of acrylic rubber, 40g of EPDM rubber, 13g of magnesium nitrate, 13g of zinc nitrate, 2g of potassium hydrogen tartrate, 2g of sulfur and 2g of nano-zinc oxide, put it under the condition of 200°C for melting, and extrude. A high temperature resistant belt A1 was prepared.
Embodiment 2
[0030] Mix 100g of acrylic rubber, 60g of EPDM rubber, 18g of magnesium nitrate, 18g of zinc nitrate, 4g of potassium hydrogen tartrate, 4g of sulfur and 4g of nano-zinc oxide, put it under the condition of 300°C for melting, and extrude. A high temperature resistant belt A2 was prepared.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses a high-temperature-resistant belt material composition, and a high-temperature-resistant belt and a preparation method thereof. The composition comprises acrylate rubber, ethylene propylene diene monomer rubber, magnesium nitrate, zinc nitrate, potassium bitartrate, sulfur and nano zinc oxide. Relative to 100 parts by weight of the acrylate rubber, the content of the ethylene propylene diene monomer rubber is 30-80 parts by weight, the content of the magnesium nitrate is 10-20 parts by weight, the content of the zinc nitrate is 10-20 parts by weight, the content of thepotassium bitartrate is 0.1-5 parts by weight, the content of the sulfur is 1-5 parts by weight, and the content of the nano zinc oxide is 1-5 parts by weight. Through the design, the effects of effectively prolonging the service life, greatly lowering the use cost and enhancing the production efficiency are realized.
Description
technical field [0001] The invention relates to the field of production and preparation of belts, in particular to a high-temperature-resistant belt material composition, a high-temperature-resistant belt and a preparation method thereof. Background technique [0002] Belts are widely used in daily knitting machines, but in actual use, the friction frequency of the belt is often high, which easily makes the belt heat due to friction and causes the belt to age, greatly reducing the service life of the belt. [0003] Therefore, it is an urgent problem to be solved in the present invention to provide a high-temperature-resistant belt material composition, a high-temperature-resistant belt and a preparation method thereof that can effectively prolong the service life, greatly reduce the cost of use, and improve production efficiency. Contents of the invention [0004] In view of the above-mentioned prior art, the purpose of the present invention is to overcome the problem that...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.