Water-permeable high-imitation stone brick

A technology of stone bricks and stones, which is applied in the field of water-permeable high-imitation stone bricks, can solve the problems of affecting appearance, poor aesthetics, and easy efflorescence, etc., and achieve the effects of excellent water permeability, toughness, excellent strength and appearance

Pending Publication Date: 2018-02-09
重庆亲禾生态环境科技有限公司
View PDF6 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the pattern is less, the color is single, the aesthetics is poor, and it is prone to efflorescence, which seriously affects the appearance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-permeable high-imitation stone brick
  • Water-permeable high-imitation stone brick

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0042] Below in conjunction with accompanying drawing, the present invention is described in detail.

[0043] In order to make the purpose, technical solutions and advantages of the embodiments of the present invention clearer, the technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the drawings in the embodiments of the present invention. Obviously, the described embodiments It is a part of embodiments of the present invention, but not all embodiments. The components of the embodiments of the invention generally described and illustrated in the figures herein may be arranged and designed in a variety of different configurations.

[0044] Accordingly, the following detailed description of the embodiments of the invention provided in the accompanying drawings is not intended to limit the scope of the claimed invention, but merely represents selected embodiments of the invention. Based on the embodim...

Embodiment 1

[0049] As a preferred embodiment of the present invention, this embodiment discloses a water-permeable high-imitation stone brick, which includes:

[0050] A water-permeable high-imitation stone brick, including a water-permeable bottom layer and a water-permeable surface layer, the water-permeable bottom layer includes gravel, machine-made sand, cement, water and high-performance water reducer; the water-permeable surface layer includes adhesives and aggregates, The adhesive includes epoxy resin and curing agent, and the aggregate includes colored sand, stones and rock flakes; the components are matched according to the following parts by weight:

[0051] 78 pieces of colored sand;

[0052] Rock chips 5 parts;

[0053] 3 pieces of stones;

[0054] 6.13 parts of epoxy resin;

[0055] 1.71 parts of curing agent;

[0056] 6.16 parts of hydrophilic curing agent;

[0057] Crushed stone 49.3 parts;

[0058] 9.6 parts of machine-made sand;

[0059] 31.6 parts of cement;

[0...

Embodiment 2

[0065] As a preferred embodiment of the present invention, this embodiment discloses a water-permeable high-imitation stone brick, which includes:

[0066] A water-permeable high-imitation stone brick, including a water-permeable bottom layer and a water-permeable surface layer, the water-permeable bottom layer includes gravel, machine-made sand, cement, water and a high-performance water reducer; the water-permeable surface layer includes adhesives and aggregates, The adhesive includes epoxy resin and curing agent, and the aggregate includes colored sand, stones and rock flakes; the components are matched according to the following parts by weight:

[0067] 84 parts of colored sand;

[0068] Rock chips 4 parts;

[0069] 2 pieces of stones;

[0070] 5.25 parts of epoxy resin;

[0071] 1.37 parts of curing agent;

[0072] 3.38 parts of hydrophilic curing agent;

[0073] Crushed stone 49.3 parts;

[0074] 9.6 parts of machine-made sand;

[0075] 31.6 parts of cement;

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of compound type building materials and in particular relates to a water-permeable high-imitation stone brick. The water-permeable high-imitation stone brick comprises a water-permeable bottom layer and a water-permeable surface layer, wherein the water-permeable bottom layer comprises crushed stones, machine-made sand, cement, water and a high-performance water reducer; the water-permeable surface layer comprises an adhesive and aggregate; the adhesive comprises epoxy resin and a curing agent; the aggregate comprises colored sand, stones and rock sheets. According to the water-permeable high-imitation stone brick provided by the invention, the epoxy resin and the curing agent are used as the adhesive and the colored sand is used as the aggregate and good strength and appearance are obtained. The hydrophilic curing agent is utilized so that good water-permeable performance and toughness are obtained. The rock sheets with abundant color and luster and large-particle colored tones are used for adjusting the appearance and patterns of products.

Description

technical field [0001] The invention relates to the technical field of composite building materials, in particular to a water-permeable high imitation stone brick. Background technique [0002] In existing floor coverings, natural stone is popular for its aesthetic appeal. However, the surface of natural stone is dense and impermeable, and its strength is low after processing and use, so its use is limited. Although the general cement permeable brick products have high strength and excellent water permeability. However, the pattern is few, the color is single, the aesthetics is poor, and it is prone to efflorescence, which seriously affects the appearance. [0003] The Chinese invention patent with the publication number CN101234888B and the publication date of 20121219 discloses a natural stone imitation tile and its manufacturing method. The main raw materials of the tile are: low-temperature porcelain stone powder 10-15%, medium-temperature porcelain sand 10% ~20%, hig...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B26/14E01C5/06E01C11/22B28B1/04B28B1/093B28B3/02
CPCE01C5/065E01C11/225C04B26/14C04B28/00B28B1/045B28B1/093B28B3/022C04B14/02C04B14/06C04B2103/302
Inventor 余朝洪王田堂杜涛文钢甘小炎熊浩
Owner 重庆亲禾生态环境科技有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com