Epoxy non-cured rubber asphalt waterproof coating and preparation method thereof

A kind of asphalt waterproof coating and non-curing rubber technology, applied in the coating field, can solve the problems of heating construction, harmful gas pollution, etc., and achieve the effects of simplified construction operation, good anti-water channeling performance and good bonding performance

Inactive Publication Date: 2018-02-27
SICHUAN SHUYANG WATERPROOF MATERIAL
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the problem that non-curing rubber asphalt waterproof coating needs to be heated for construction and harmful gas pollution, the invention provides a kind of epoxy non-curing rubber asphalt waterproof coating. The coating includes component A and component B, component A and component B is mixed according to the mass ratio of A:B=1~90:1;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Epoxy non-cured rubber asphalt waterproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] An epoxy non-curing rubber asphalt waterproof coating, comprising component A and component B, component A and component B are mixed by the mass ratio of A:B=1~90:1;

[0044] The composition of component A is calculated in parts by mass:

[0045] 25 parts of 90# asphalt

[0046] base oil 5 parts

[0047] 1 part rubber SBS

[0048] Epoxy resin E-51 2 parts

[0049] The composition of component B is calculated in parts by mass as follows:

[0050] Polyamide curing agent 2 parts

[0051] An epoxy non-curing rubber asphalt waterproof coating. The preparation method is: add 25 parts of 90# asphalt and 5 parts of base oil into the stirring tank, heat to 180 ° C, stir at high speed, add 1 part of rubber SBS, continue stirring, and react for 0.5 hour, lower the temperature to 140°C, add 2 parts of epoxy resin E-51, continue to stir evenly, cool down to 80°C, and discharge to obtain Component A; Component B is 2 parts of polyamide curing agent; Component A and component B ...

Embodiment 2

[0053] An epoxy non-curing rubber asphalt waterproof coating, comprising component A and component B, component A and component B are mixed by the mass ratio of A:B=1~90:1;

[0054] The composition of component A is calculated in parts by mass:

[0055] 90# asphalt 35 parts

[0056] Minus 20 parts of third-line oil

[0057] Rubber SIS 8 parts

[0058] Epoxy resin NC-513 16 parts

[0059] Dodecyl-tetradecyl glycidyl ether 3.5 parts

[0060] 10 parts of waste car tire rubber powder

[0061] Talcum powder 15 parts

[0062] 2.5 parts of defoamer

[0063] The composition of component B is calculated in parts by mass as follows:

[0064] Polyetheramine curing agent 16 parts

[0065] 1.5 parts of curing accelerator

[0066] An epoxy non-curing rubber asphalt waterproof coating. The preparation method is: add 35 parts of 90# asphalt and 20 parts of third-line oil into the stirring tank, heat to 190 ° C, stir at high speed, add 8 parts of rubber SIS, continue stirring, and rea...

Embodiment 3

[0068]An epoxy non-curing rubber asphalt waterproof coating, comprising component A and component B, component A and component B are mixed by the mass ratio of A:B=1~90:1;

[0069] The composition of component A is calculated in parts by mass:

[0070] 50 parts of 100# asphalt

[0071] Aromatic oil 30 parts

[0072] Rubber SBR 15 parts

[0073] Epoxy resin NC-514 30 parts

[0074] Propyl glycidyl ether 7 parts

[0075] Waste car tire rubber powder 20 parts

[0076] Heavy calcium 30 parts

[0077] 5 parts of coupling agent

[0078] The composition of component B is calculated in parts by mass as follows:

[0079] Cardanol curing agent 30 parts

[0080] 3 parts curing accelerator

[0081] An epoxy non-curing rubber asphalt waterproof coating, its preparation method is: add 50 parts of 100# asphalt and 30 parts of aromatic oil into the stirring tank, heat it to 200 ° C, stir at high speed, add 15 parts of rubber SBR, continue stirring, and react 2 hour, add 20 parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thermal resistanceaaaaaaaaaa
Login to view more

Abstract

The invention discloses an epoxy non-cured rubber asphalt waterproof coating and a preparation method thereof and belongs to the field of coatings. The coating comprises a component A and a componentB, wherein the component A is prepared from asphalt, plasticizers, polymer modifiers and epoxy resin; the component B is prepared from epoxy curing agents. The problem that the non-cured rubber asphalt waterproof coating can be constructed after the coating is heated can be solved; the coating is energy-saving and environmentally friendly; the safety of constructors is ensured; the construction operation is simplified; the application range of the product is expanded; the coating is excellent in construction performance, does not need to be heated in the whole construction process, is excellent in high-temperature performance, can achieve obstacle-free construction under high temperature and low temperature, and is high in flexibility, high in elongation rate, excellent in creep property,high in self-healing capability, high in water channeling resistance and high in adhesion performance.

Description

technical field [0001] The invention relates to the field of coatings, in particular to an epoxy non-curing rubber asphalt waterproof coating and a preparation method thereof. Background technique [0002] Non-curing rubber asphalt waterproof coating is a new type of waterproof material with creep properties that maintains a viscous paste for a long time under the application state. bending fatigue damage or premature aging of the waterproof layer due to high stress; at the same time, due to the viscosity of the coating, it can well seal the capillary pores and cracks of the base layer, adapt to complex construction surfaces, and It can automatically find leaking parts, repair the damaged waterproof layer, solve the problem of water channeling in the waterproof layer, and greatly improve the reliability of waterproofing. However, the non-curing rubber asphalt waterproof coating has the following disadvantages. 1) It needs to be heated to 120-150°C before construction, which...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D195/00C09D163/00C09D119/00C09D191/00C09D153/02C09D109/06C09D7/61C09D7/65
CPCC08K2003/265C08L2201/08C08L2205/035C09D5/18C09D195/00C08L63/00C08L91/00C08L53/02C08L19/003C08K3/34C08L9/06C08K3/26
Inventor 杜勇
Owner SICHUAN SHUYANG WATERPROOF MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap