Processing technique of 6008 aluminum alloy crash box

A processing technology and energy-absorbing box technology, applied in the field of alloys, to achieve the effects of improving deformation capacity, good crushing effect, and improving performance

Inactive Publication Date: 2018-03-09
SHANGHAI UNISON ALUMINUM PRODS
View PDF3 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a processing technology for the 6008 aluminum alloy energy-absorbing box used in automobile bumpers, to solve the problem that the 6008 aluminum alloy meets the crushing deformation effect, product performance and section bearing capacity requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processing technique of 6008 aluminum alloy crash box
  • Processing technique of 6008 aluminum alloy crash box
  • Processing technique of 6008 aluminum alloy crash box

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Test equipment: aluminum smelting furnace and its casting system, 40T homogenizing furnace, aluminum rod sawing machine, aluminum extrusion machine -2000T, aging electric furnace, 20T universal testing machine.

[0027] experiment procedure:

[0028] 1) During the smelting process of 6008 aluminum rods, magnesium is added with 99.9% magnesium ingots, and silicon is added with 21% aluminum-silicon alloys; the temperature of the molten aluminum is 752°C when adding (requires the alloy content in the final aluminum rods: magnesium mass percentage Controlled at 0.55-0.60%, silicon mass percentage is controlled at 0.5-0.55%);

[0029] As in the original process of Comparative Example 1, in the final aluminum rod, the alloy content: silicon mass percentage: 0.6-0.7% magnesium mass percentage: 0.4-0.45%;

[0030] 2) The aluminum liquid adopts two-stage filtration, and the meshes of the filter plates are 40 mesh and 50 mesh respectively;

[0031] 3) Continuous casting is carr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of alloys and particularly relates to a processing technique of a 6008 aluminum alloy crash box, comprising the steps of A, during smelting of 6008 aluminum rods, using 99.9% magnesium ingots to add magnesium and 21% aluminum-silicon alloy to add silicon, wherein molten aluminum is at 752 DEG C during adding; B, subjecting the molten aluminum to double-level filtering, wherein filter plates are 40 and 50 in mesh respectively; C, using a hydraulic casting machine and a casting tray as well as a water-curtain cooling system including crystallizer and cooled byfed water to perform continuous casting so as to obtain aluminum rods; D, subjecting the aluminum rods to homogenous annealing at 560 DEG C for 7 H; E, extruding the aluminum rods to obtain a finishedcrack box; f, aging at 215 DEG C for 5 H. The magnesium and silicon alloy content in the 6008 aluminum alloy is adjusted, and the aging process is modified; after modification, the finished crash meets the requirements for both crushing and sectional bearing capacity and yielding strength.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to a composition of an Al-Mg-Si-V alloy and a heat treatment process for a 6008 brand aluminum alloy. Background technique [0002] The lightweight of automobiles is developing rapidly. Aluminum alloy has the characteristics of moderate strength, light weight, and easy forming, which is suitable for lightweight design of automobiles. [0003] The current energy-absorbing box products produced by 6008 alloy have a relatively high proportion of pressure collapse cracking when the yield strength is met; after adjusting the aging process, the problem of pressure collapse cracking is solved, but the yield strength cannot meet the requirements. Contents of the invention [0004] The purpose of the present invention is to provide a processing technology for a 6008 aluminum alloy crash box used in automobile bumpers, which solves the problem of 6008 grade aluminum alloy and simultaneously ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/02C22C21/08C22F1/043C22F1/047C22F1/05
CPCC22C21/02C22C21/08C22F1/043C22F1/047C22F1/05
Inventor 罗世兵李文通
Owner SHANGHAI UNISON ALUMINUM PRODS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap