A technology of plastic mold steel and production process, which is applied in the field of iron and steel smelting, can solve the problems of not being able to meet the performance requirements of plastic mold steel 718, and can not be applied to plastic mold steel 718, and achieve the effect of improved production technology and excellent comprehensive performance

Active Publication Date: 2018-03-13
NANYANG HANYE SPECIAL STEEL CO LTD
View PDF4 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Practice shows that this production method is only suitable for low-alloy high-strength steel, and cannot be applie

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0044] Example 7

[0045] A production process of plastic mold steel 718 is carried out according to the following steps:

[0046] a. KR molten iron S is removed: the molten iron at the station is subjected to slag removal treatment. It is required that the front and rear slag be completely removed, and the molten iron after S removal contains S0.002%;

[0047] b. Converter smelting: the temperature of molten iron into the furnace is 1300 ℃, high Cr, high Mo and high Ni alloy scrap are added during the smelting process, and the tapping is C0.10%, P0.015%, S0.005% according to the mass percentage, and the number of spot blowing is not More than 2 times to avoid slag in the tapping process;

[0048] c. LF refining: use high iron oxide mixed slag, the mass percentage of the high iron oxide mixed slag is composed of: 70% iron oxide and 30% fluorite, add 800kg lime, control the temperature at 1620 ℃, make the steel The liquid and the slag surface fully react, and the P content of...

Example Embodiment

[0058] Example 8

[0059] A production process of plastic mold steel 718 is carried out according to the following steps:

[0060] a. KR molten iron S is removed: the molten iron at the station is subjected to slag removal treatment. It is required that the front and rear slag be completely removed, and the molten iron after S removal contains S0.002%;

[0061] b. Converter smelting: the temperature of molten iron into the furnace is 1330℃, high Cr, high Mo and high Ni alloy scraps are added during the smelting process, and the tapping is C0.15%, P0.012%, S0.003% according to the mass percentage, and the number of spot blowing is not more than 2 times;

[0062] c. LF refining: use high iron oxide mixed slag, the mass percentage of the high iron oxide mixed slag is composed of: 60% iron oxide and 40% fluorite, add 600kg lime, control the temperature at 1590 ℃, make the steel The liquid and the slag surface fully react, and the P content of the finished product is controlled b...

Example Embodiment

[0071] Example 9

[0072] A production process of plastic mold steel 718 is carried out according to the following steps:

[0073] a. KR molten iron S is removed: the molten iron at the station is subjected to slag removal treatment. It is required that the front and rear slag be completely removed, and the molten iron after S removal contains S0.003%;

[0074] b. Converter smelting: the temperature of molten iron into the furnace is 1315℃, high Cr, high Mo and high Ni alloy scrap is added during the smelting process, and the tapping is C0.12%, P0.012%, S0.004% by mass percentage, and the number of spot blowing is not more than 2 times;

[0075] c. LF refining: use high iron oxide mixed slag, the mass percentage of the high iron oxide mixed slag is composed of: 80% iron oxide and 20% fluorite, add 400kg lime, control the temperature at 1600 ℃, make the steel The liquid and the slag surface fully react, and the P content of the finished product is controlled below 0.003%;

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides plastic mold steel 718 and a production process thereof, and relates to the technical field of steel and iron smelting. The plastic mold steel 718 comprises the following chemical components in percentage by mass: 0.37-0.40% of C, 0.4-0.5 of Si, 1.4-1.5 of Mn, 1.8-2.0 of Cr, 0.4-0.5 of Mo, 1.0-1.1 of Ni, P not more than 0.008, S not more than 0.003, 0.018-0.030 of Als, and the balance of Fe and residual elements; and the thickness is 150 mm. The plastic mold steel 718 is excellent in mechanical performance, high in strength and excellent in impact resistance.

Description

technical field [0001] The invention relates to the technical field of iron and steel smelting, in particular to a plastic mold steel 718 and a production process thereof. Background technique [0002] 718 die steel is a brand of pre-hardened hot work die steel. This steel has excellent mechanical properties and machinability, and is widely used in the mold industry, especially in the field of plastic mold processing and production. In addition, its special production process makes 718 mold steel already have a hardness of 330~370HBW when it leaves the factory, so it can reduce the heat treatment link in the normal mold processing and production and improve economic benefits. Except that it cannot be used for plastic mold parts with corrosion resistance requirements, it is currently the most widely used typical steel grade for general-purpose plastic mold steel. Often referred to as "advanced" plastic mold steel, it is often used as a comparison model for newly developed ne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/02C22C38/04C22C38/06C22C38/44C21D8/02C21D1/28C21C7/10C21C5/28
CPCC21C5/28C21C7/10C21D1/28C21D8/0205C21D8/0226C22C38/02C22C38/04C22C38/06C22C38/44Y02P10/20
Inventor 朱书成李亮许少普李忠波张涛杨阳杨东唐郑磊刘庆波张占杰符可义朱先兴薛艳生庞百鸣于飒董真真袁少威袁永旗石教兴蒋鹏袁继恒康文举
Owner NANYANG HANYE SPECIAL STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap