Material for piston rod in ultra-low temperature reciprocating compressor and surface reinforcing method of material

A compressor medium and surface strengthening technology, which is applied in metal material coating process, coating, melt spraying, etc., can solve the problems of material and surface strengthening method selection, and achieve market expansion, small friction coefficient and stable size Effect

Active Publication Date: 2018-03-23
沈阳鼓风机集团往复机有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a material and surface strengthening method for the piston rod in the ultra-low temperature reciprocating compressor. The quality of the piston rod material and coating quality of the invention meets the performance requirements of the parts at ultra-low temperature, and solves the problem of the ultra-low temperature reciprocating compressor equipment. Difficulties in selecting materials and surface strengthening methods for main parts such as piston rods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Material for piston rod in ultra-low temperature reciprocating compressor and surface reinforcing method of material
  • Material for piston rod in ultra-low temperature reciprocating compressor and surface reinforcing method of material
  • Material for piston rod in ultra-low temperature reciprocating compressor and surface reinforcing method of material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] 1. Heat treatment process and substrate properties:

[0033] 1. Heat treatment process:

[0034] After 1Ni9 steel is forged, it is normalized (900±10°C, 3 hours, air cooling)——rough processing——primary quenching (820±10°C, 2 hours, oil quenching) + secondary quenching (670±10°C, 2 hours , water quenching) + tempering (580±10°C, 3 hours, air cooling)—semi-finishing—stabilization treatment (550±10°C, 3.5 hours, air cooling) to obtain materials for piston rods.

[0035] 2. Matrix performance

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a material for a piston rod in an ultra-low temperature reciprocating compressor and a surface reinforcing method of the material and belongs to the technical filed of materials of ultra-low temperature moving parts and surface reinforcing in equipment manufacturing industries. The material of the piston is obtained by means of the method that 1Ni9 steel forge pieces serveas a raw material and are sequentially subjected to performance heat treatment, finishing and stable treatment, wherein as for the performance heat treatment process, normalizing treatment is conducted at the temperature of 890-910 DEG C, primary quenching is conducted at the temperature of 810-830 DEG C, secondary quenching is conducted at the temperature of 660-680 DEG C, and tempering treatmentis conducted at the temperature of 570-590 DEG C. The surface of the material of the piston is sprayed with a WC-Co coating through a supersonic flame spraying technology. The material of the pistonrod and the coating quality meet the performance requirements of the parts under the ultra-low temperature, the difficult problem of selecting of the materials of the main parts such as the piston rodof the ultra-low temperature reciprocating compressor equipment and the surface reinforcing method is solved, and the foundation is laid for future better and quicker development of natural gas and hydrocarbon liquefaction, storage and conveying device equipment in China.

Description

technical field [0001] The invention relates to the technical field of material and surface strengthening of ultra-low temperature moving parts in the equipment manufacturing industry, in particular to a material and surface strengthening method for a piston rod in an ultra-low temperature reciprocating compressor. The piston rod is used as an ultra-low temperature reciprocating compressor The key parts in the compressor are used, and the operating temperature of the ultra-low temperature reciprocating compressor is -160~-180°C. Background technique [0002] In the LNG (liquefied natural gas liquefied natural gas) receiving station, the cryogenic compressor is used to extract the boil-off gas (referred to as BOG) in the LNG storage tank and transport it to other processing equipment, so as to avoid excessive pressure in the storage tank. The ultra-low temperature reciprocating compressor can directly suck BOG from the LNG storage tank, and the suction temperature is usually ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C21D1/19C21D1/28C23C4/129C23C4/06
CPCC21D1/19C21D1/28C23C4/06
Inventor 朱丽红邓德伟
Owner 沈阳鼓风机集团往复机有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products