Latex foaming thermal insulation material and application thereof in field of latex gloves

A technology of thermal insulation materials and latex gloves, applied in protective clothing and other directions, can solve the problems that gloves do not have the function of keeping warm and thermal insulation, and users freeze, and achieve the effect of cumbersome processing procedures, increased cost, and reduced pain.

Inactive Publication Date: 2018-03-27
BEIJING REAGENT LATEX PRODS
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] A large number of natural latex gloves have been used in family life in our country. Most of the existing household gloves are light-lined. Light-lined gloves do not have the function of keeping warm and heat preservation. It is easy to freeze the user's hands during long-term family work.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] S1: Preparation of sulfur, zinc dibutyldithiocarbamate (BZ), zinc oxide, antioxidant dispersion

[0047] A, preparation of sulfur dispersion

[0048] Add 5.34kg of soft water, 0.06kg of potassium hydroxide, 0.6kg of dispersant NNO, and 6Kg of sulfur into the ball mill and grind for 30 hours;

[0049] B, the preparation of zinc dibutyldithiocarbamate (BZ) dispersion

[0050]Add 2.546kg of soft water, 0.06kg of potassium hydroxide, 0.394kg of dispersant NNO, and 3kg of zinc dibutyldithiocarbamate (BZ) into a ball mill and grind for 30 hours;

[0051] C, preparation of zinc oxide dispersion

[0052] Add 6.6kg of soft water, 0.4kg of dispersant NNO, and 5kg of zinc oxide into the ball mill in order to grind for 17 hours;

[0053] D. Preparation of Antiaging Agent WL Dispersion

[0054] Add 7.85kg of soft water, 0.15kg of potassium hydroxide, 1kg of dispersant NNO, and 6kg of antiaging agent WL into the ball mill and grind for 30 hours;

[0055] The rotating speed of th...

Embodiment 2

[0074] S1: Preparation of sulfur, zinc dibutyldithiocarbamate (BZ), zinc oxide, antioxidant dispersion

[0075] A, preparation of sulfur dispersion

[0076] Add 5.34kg of soft water, 0.06kg of potassium hydroxide, 0.6kg of dispersant NNO, and 18Kg of sulfur into the ball mill and grind for 30 hours;

[0077] B, the preparation of zinc dibutyldithiocarbamate (BZ) dispersion

[0078] Add 2.546kg of soft water, 0.06kg of potassium hydroxide, 0.394kg of dispersant NNO, and 12kg of zinc dibutyldithiocarbamate (BZ) into a ball mill and grind for 30 hours;

[0079] C, preparation of zinc oxide dispersion

[0080] Add 6.6kg of soft water, 0.4kg of dispersant NNO, and 18kg of zinc oxide into the ball mill and grind for 17 hours;

[0081] D. Preparation of Antiaging Agent WL Dispersion

[0082] Add 7.85kg of soft water, 0.15kg of potassium hydroxide, 1kg of dispersant NNO, and 6kg of antiaging agent WL into the ball mill and grind for 30 hours;

[0083] The rotating speed of above-...

Embodiment 3

[0102] S1: Preparation of sulfur, zinc dibutyldithiocarbamate (BZ), zinc oxide, antioxidant dispersion

[0103] A, preparation of sulfur dispersion

[0104] Add 5.34kg of soft water, 0.06kg of potassium hydroxide, 0.6kg of dispersant NNO, and 12Kg of sulfur into the ball mill and grind for 30 hours;

[0105] B, the preparation of zinc dibutyldithiocarbamate (BZ) dispersion

[0106] Add 2.546kg of soft water, 0.06kg of potassium hydroxide, 0.394kg of dispersant NNO, and 7.5kg of zinc dibutyldithiocarbamate (BZ) into a ball mill and grind for 30 hours;

[0107] C, preparation of zinc oxide dispersion

[0108] Add 6.6kg of soft water, 0.4kg of dispersant NNO, and 17.5kg of zinc oxide into the ball mill and grind for 17 hours;

[0109] D. Preparation of Antiaging Agent WL Dispersion

[0110] Add 7.85kg of soft water, 0.15kg of potassium hydroxide, 1kg of dispersant NNO, and 6kg of antiaging agent WL into the ball mill and grind for 30 hours;

[0111] The rotating speed of abo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a latex foaming thermal insulation material, which comprises a basic component and a foaming component, wherein the basis component comprises low protein natural latex, sulphur, zinc dibutyl dithiocarbamate (BZ), and zinc oxide, and the foaming component comprises low protein natural latex, a foaming agent, sulphur, zinc dibutyl dithiocarbamate (BZ), and zinc oxide. The foaming component is subjected to a foaming process and then mixed with the basic component to obtain the thermal insulation material, thus ensuring that the foamed latex has a good thermal insulation effect and a better decompression effect. The thermal insulation material has a good decompression effect during thermal insulation, and can be suitable for using in environments in which thermal insulation is needed and hard objects needed to be contacted.

Description

technical field [0001] The invention relates to the technical field of processing latex thermal insulation materials, in particular to a latex foam thermal insulation material and its application in the field of latex gloves. Background technique [0002] Latex generally refers to a colloidal emulsion formed by dispersing polymer particles in water. Also known as latex. It is customary to refer to the aqueous dispersion of rubber particles as latex, and the aqueous dispersion of resin particles as emulsion. Products made from latex are called latex products, such as gloves, toys, rubber hoses, etc. [0003] Gloves have been widely used in people's production and life because of their barrier protection and can well protect the safety of users. According to its use, it can be divided into medical gloves, industrial gloves and household gloves, and gloves are generally divided into two categories: natural rubber gloves and nitrile gloves according to the materials used in p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L7/02C08K13/02C08K3/06C08K5/39C08K3/22C08J9/04A41D19/015
CPCC08J9/04A41D19/0055C08J9/0033C08J9/0066C08J9/0095C08J2307/02
Inventor 支玉园星宇王会侯福新孙喜民刘士新刘强高健
Owner BEIJING REAGENT LATEX PRODS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More