Negative electrode lead paste of lead-acid storage battery

A lead-acid battery and negative electrode paste technology, applied in the field of electrochemistry, can solve the problems of short cycle life of lead-acid batteries, influence on development and use, early capacity loss, etc., achieve good hydrogen evolution suppression effect, long cycle life, reduce The effect of precipitation

Inactive Publication Date: 2018-03-30
HENAN CHAOWEI POWER SUPPLY
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, lead-acid batteries have shortcomings such as short cycle life, poor low tem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A negative lead paste for lead-acid battery, the raw materials are composed of 83% of lead powder, 0.3% of humic acid, 0.08% of short fiber, 0.3% of acetylene black, 6.82% of sulfuric acid and 9.5% of water in terms of mass percentage. Wherein, the density of the sulfuric acid is 1.4±0.001g / cm 3 (25° C.); the short fibers are chemical short fibers with a length of 5 mm.

Embodiment 2

[0025] A negative lead paste for a lead-acid storage battery. The raw materials are composed of 81% lead powder, 0.5% humic acid, 0.08% short fiber, 0.4% acetylene black, 8.6% sulfuric acid and 9.42% water in terms of mass percentage. Wherein, the density of the sulfuric acid is 1.4±0.001g / cm 3 (25°C); the short fibers are chemical short fibers with a length of 8 mm.

Embodiment 3

[0027] A negative lead paste for a lead-acid storage battery. The raw materials are: 82% of lead powder, 0.4% of humic acid, 0.06% of short fiber, 0.24% of acetylene black, 6.7% of sulfuric acid and 10.6% of water in terms of mass percentage. Wherein, the density of the sulfuric acid is 1.4±0.001g / cm 3 (25° C.); the short fibers are chemical short fibers with a length of 5 mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Lengthaaaaaaaaaa
Lengthaaaaaaaaaa
Lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses negative electrode lead paste of a lead-acid storage battery. The negative electrode lead paste is prepared from the raw materials based on mass percentages: 81-85% of lead powder, 0.1-0.5% of humic acid, 0.06-0.1% of short fibers, 0.1-0.5% of acetylene black, 6.7-8.6% of sulfuric acid and 7.9-10.6% of water. A preparation method of the lead paste of the lead-acid storage battery comprises the steps of adding the lead powder, humic acid, short fibers and acetylene black into a paste mixer to be stirred for 8-12min, and then adding water to the paste mixture to be subjected to wet stirring for 10-14min; and adding sulfuric acid to the paste mixture while stirring, wherein the sulfuric acid adding time is 13-16min, and performing continuous stirring for 10-15min aftersulfuric acid is added completely to obtain the lead paste. The lead-acid storage battery prepared from the lead paste is stable in charging-discharging performance, relatively high in low-temperature charging-discharging performance, long in cycle life and relatively high in negative electrode hydrogen evolution suppression effect.

Description

technical field [0001] The invention belongs to the technical field of electrochemistry, and in particular relates to a negative electrode paste of a lead-acid storage battery. Background technique [0002] Due to a series of advantages such as low price, easy availability of raw materials, high use safety, suitability for high current and wide temperature range, lead-acid batteries have advantages in chemical power sources. Moreover, with the development of the electric bicycle industry, Lead-acid batteries are widely used as a power source for electric bicycles and electric motorcycles. However, lead-acid batteries have shortcomings such as short cycle life, poor low-temperature performance, and early capacity loss, which affect their development and use. Technical indicators such as low-temperature performance and charge acceptance are related to the negative plate of lead-acid batteries, and it is urgent to improve the performance level of the negative plate to meet the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): H01M4/36H01M4/56H01M4/62H01M10/06
CPCH01M4/362H01M4/56H01M4/62H01M4/628H01M10/06H01M2220/20Y02E60/10
Inventor 胡庆涛李松林王淼葛冰
Owner HENAN CHAOWEI POWER SUPPLY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap