Marble glaze ceramic product and preparation method thereof

A technology for ceramic products and marble, which is applied in the field of marble glaze ceramic products and its preparation, can solve problems such as ripples, orange glaze, cracking, etc., achieve the effects of simple preparation methods, reduce production costs, and solve environmental pollution

Active Publication Date: 2020-01-07
福建省德化新奇丽工艺有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the preparation of marble glazed ceramic products is not so simple. The expansion coefficient of the body and the glaze must be close, otherwise defects such as cracking, peeling, orange glaze, and ripples will occur.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Marble glaze ceramic products, the raw material of the glaze is waste marble slurry produced in the marble production process, and the ceramic body includes the following raw materials in terms of parts by mass: 15 parts of kaolin, 18 parts of calcite, 12 parts of limestone, 8 parts of quartz, waste porcelain 6 parts of powder, 3 parts of calcium oxide, 2 parts of titanium dioxide, and 2 parts of pigment.

[0029] The preparation method of this marble glaze ceramic product comprises the steps:

[0030] 1) Weigh and mix the raw material components of the ceramic green body according to the formula, add them to a ball mill, add water accounting for 50% of the mass of the material, and ball mill for 12 hours. The fineness of the mud is screened on the basis that it can pass through a 300-mesh sieve;

[0031] 2) Carry out magnetic separation to remove iron impurities contained in the mud;

[0032] 3) carry out press filtration to last step gained mud, the moisture content ...

Embodiment 2

[0038] Marble glaze ceramic products, the raw material of the glaze is waste marble slurry produced in the marble production process, and the ceramic body includes the following raw materials in terms of parts by mass: 18 parts of kaolin, 21 parts of calcite, 15 parts of limestone, 10 parts of quartz, waste porcelain 8 parts of powder, 5 parts of calcium oxide, 3 parts of titanium dioxide, and 4 parts of pigment.

[0039] The preparation method of this marble glaze ceramic product comprises the steps:

[0040] 1) First select the calcite to remove impurities, and crush it until the particle size is less than 4mm, then weigh the raw material components of the ceramic green body according to the formula, mix them, add them to the ball mill, and then add water accounting for 60% of the mass of the material, ball mill for 12 hours, and the slurry The fineness is screened on the basis of passing through a 400-mesh sieve;

[0041] 2) Carry out magnetic separation to remove iron imp...

Embodiment 3

[0048] Marble glaze ceramic products, the raw material of the glaze is waste marble slurry produced in the marble production process, and the ceramic body includes the following raw materials in terms of parts by mass: 21 parts of kaolin, 25 parts of calcite, 16 parts of limestone, 12 parts of quartz, waste porcelain 10 parts of powder, 7 parts of calcium oxide, 4 parts of titanium dioxide, and 5 parts of pigment.

[0049] The preparation method of this marble glaze ceramic product comprises the steps:

[0050] 1) First select the calcite to remove impurities, and crush it until the particle size is less than 4mm, then weigh the raw material components of the ceramic green body according to the formula, mix them, add them to the ball mill, and then add water accounting for 60% of the mass of the material, ball mill for 12 hours, and the slurry The fineness is screened on the basis of passing through a 400-mesh sieve;

[0051] 2) Carry out magnetic separation to remove iron im...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a marble glaze ceramic product and a preparation method thereof, and belongs to the technical field of ceramics. A glaze raw material of the marble glaze ceramic product is waste marble pulp produced in the process of marble production. A ceramic body includes the following raw materials by mass: 15 to 21 parts of kaolin, 18 to 25 parts of calcite, 12 to 16 parts of limestone, 8 to 12 parts of quartz, 6 to 10 parts of waste porcelain powder, 3 to 7 parts of calcium oxide, 2-4 parts of titanium dioxide and 2 to 5 parts of a color material. The marble glaze ceramic product prepared by the invention has beautiful glaze surface, high glaze layer strength, good thermal stability, energy saving and emission reduction, and environmental friendliness.

Description

technical field [0001] The invention belongs to the technical field of ceramics, and in particular relates to a marble glaze ceramic product and a preparation method thereof. Background technique [0002] Marble originally refers to the white limestone with black patterns produced in Dali, Yunnan Province. Later, the name gradually developed into a name for all limestones with various color patterns. Marble is very beautiful after being polished. It is mainly used for processing into various shapes and plates for the walls, floors, platforms, and columns of buildings. It is also often used as materials for monumental buildings such as monuments, towers, and statues. Marble can also be carved into practical arts such as arts and crafts, stationery, lamps, and utensils. The beauty, elegance, and strength of marble make it more and more widely used. For example, it can be used as a glaze for ceramic vessels, which has both artistic value and practical storage. [0003] But pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/00C03C1/00C04B35/057C04B35/622C04B41/86
CPCC03C1/002C03C8/00C04B35/057C04B35/62204C04B41/5022C04B41/86C04B2235/3232C04B2235/3418C04B2235/349C04B2235/656C04B41/4539C04B41/0072
Inventor 马策新
Owner 福建省德化新奇丽工艺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More